A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2S...A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4（3：1） or Na2SO4/NaCl（3：1） salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.展开更多
In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating c...In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating coated with mixed salts of Na2SO4 ＋ K2SO4 and Na2SO4 ＋ NaC1 were carried out at 700 ℃. The results indicated that the composite coating performed better against the corrosion due to the gradient element distribution in Al-enriched outer layer and Cr-enriched inner layer. The corrosion mechanisms for the two coatings were also discussed.展开更多
基金financially supported by the National Natural Science Foundation of China (No.51001106)National Basic Research Program of China (No.2012CB625100)
文摘A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4（3：1） or Na2SO4/NaCl（3：1） salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.
基金supported by the National Natural Science Foundation of China(Grant No.51001106)
文摘In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating coated with mixed salts of Na2SO4 ＋ K2SO4 and Na2SO4 ＋ NaC1 were carried out at 700 ℃. The results indicated that the composite coating performed better against the corrosion due to the gradient element distribution in Al-enriched outer layer and Cr-enriched inner layer. The corrosion mechanisms for the two coatings were also discussed.