The feasibility of a new method for separating arsenic from arsenic-antimony-bearing dusts using Cu S was put forward,in which Sb was transformed into Sb2O4 and Sb2S3 that stayed in the roasted calcine while As was vo...The feasibility of a new method for separating arsenic from arsenic-antimony-bearing dusts using Cu S was put forward,in which Sb was transformed into Sb2O4 and Sb2S3 that stayed in the roasted calcine while As was volatilized in the form of As4O6.The factors such as roasting temperature and Cu S addition amount were studied using XRD,EPMA and SEM-EDS.Cu S has an active effect on the separation of arsenic due to the destruction of(Sb,As)2 O3 structures in the original dust and the simultaneous release of As in the form of As4O6.At a roasting temperature of 400°C and Cu S addition amount of 130%,the volatilization rates of arsenic and antimony reach 97.80 wt.%and 8.29 wt.%,respectively.Further,the high As volatile matter can be used to prepare ferric arsenate after it is oxidized,with this treatment rendering the vapor harmlessness.展开更多
This paper mainly investigated the antimony recovery from antimony-bearing dusts through reduction roasting process after the dust firstly oxidation roasted.CO–CO2 mixture gas was used as reducing agent,and the antim...This paper mainly investigated the antimony recovery from antimony-bearing dusts through reduction roasting process after the dust firstly oxidation roasted.CO–CO2 mixture gas was used as reducing agent,and the antimony-containing phase was reduced into Sb4O6,volatilized into smoke,and finally recovered through the cooling cylinder.The antimony recovery rate increased from 66.00 wt%to 73.81 wt%in temperature range of 650 to 800°C,and decreased with temperature increased further to 900°C due to the reduction of Sb4O6 to the nonvolatile Sb.Similarly,the CO partial pressure also played a double role in this test.Under optimized conditions of roasting temperature of 800°C,CO partial pressure of 7.5 vol%and roasting time of 120 min,98.40 wt%of arsenic removal rate and 80.40 wt%antimony recovery rate could be obtained.In addition,the“As2O3”product could be used for preparing ferric arsenate which realized the harmless treatment of it.展开更多
基金Project(51564034)supported by the National Natural Science Foundation for Distinguished Regional Scholars,ChinaProject(2015HA019)supported by the Scientific and Technological Leading Talent Program in Yunnan Province,China.
文摘The feasibility of a new method for separating arsenic from arsenic-antimony-bearing dusts using Cu S was put forward,in which Sb was transformed into Sb2O4 and Sb2S3 that stayed in the roasted calcine while As was volatilized in the form of As4O6.The factors such as roasting temperature and Cu S addition amount were studied using XRD,EPMA and SEM-EDS.Cu S has an active effect on the separation of arsenic due to the destruction of(Sb,As)2 O3 structures in the original dust and the simultaneous release of As in the form of As4O6.At a roasting temperature of 400°C and Cu S addition amount of 130%,the volatilization rates of arsenic and antimony reach 97.80 wt.%and 8.29 wt.%,respectively.Further,the high As volatile matter can be used to prepare ferric arsenate after it is oxidized,with this treatment rendering the vapor harmlessness.
基金Project(51564034)supported by the National Science Fund for Distinguished Regional Scholars,China
文摘This paper mainly investigated the antimony recovery from antimony-bearing dusts through reduction roasting process after the dust firstly oxidation roasted.CO–CO2 mixture gas was used as reducing agent,and the antimony-containing phase was reduced into Sb4O6,volatilized into smoke,and finally recovered through the cooling cylinder.The antimony recovery rate increased from 66.00 wt%to 73.81 wt%in temperature range of 650 to 800°C,and decreased with temperature increased further to 900°C due to the reduction of Sb4O6 to the nonvolatile Sb.Similarly,the CO partial pressure also played a double role in this test.Under optimized conditions of roasting temperature of 800°C,CO partial pressure of 7.5 vol%and roasting time of 120 min,98.40 wt%of arsenic removal rate and 80.40 wt%antimony recovery rate could be obtained.In addition,the“As2O3”product could be used for preparing ferric arsenate which realized the harmless treatment of it.