The novel carbon dioxide (CO2) adsorbents with a high capture efficiency were prepared through impregnating the as-synthesized MCM-41 with three kinds of amines, namely diethylenetriamine (DETA), triethylenetetram...The novel carbon dioxide (CO2) adsorbents with a high capture efficiency were prepared through impregnating the as-synthesized MCM-41 with three kinds of amines, namely diethylenetriamine (DETA), triethylenetetramine (TETA) and 2-amino-2-methyl-1- propanol (AMP). The resultant samples were characterized by small angle X-ray diff action and low temperature N2 adsorption. The synthesis way not only saves the energy or extractor to remove the template but also is environmentally friendly due to the absence of the potential pollutants such as toluene. CO2 capture was investigated in a dynamic packed column. The sample impregnated by TETA showed the highest adsorption capacity, approximately 2.22 mmol/g at 60℃ due to its highest amino-groups content among the three amines. The CO2 adsorption behavior was also investigated with the deactivation model, which showed an excellent prediction for the breakthrough curves.展开更多
制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射(XPD)分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NM...制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射(XPD)分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NMR研究了试样中Al的化学环境,结果表明,即使在高铝含量的情况下,样品中的铝原子仍以四配位结合在MCM-41的硅骨架上,未能检测出骨架外六配位铝的存在.文中还就Al含量对孔结构的影响以及Al-MCM-41形成机理作了讨论.展开更多
基金supported by the Program to Sponsor Teams for Innovation in the Construction of Talent Highlands in Guangxi Institutions of Higher Learning (No.GuiJiaoRen[2007]71)the National Natural Sciences Foundation of China(No.20976159,50968005)
文摘The novel carbon dioxide (CO2) adsorbents with a high capture efficiency were prepared through impregnating the as-synthesized MCM-41 with three kinds of amines, namely diethylenetriamine (DETA), triethylenetetramine (TETA) and 2-amino-2-methyl-1- propanol (AMP). The resultant samples were characterized by small angle X-ray diff action and low temperature N2 adsorption. The synthesis way not only saves the energy or extractor to remove the template but also is environmentally friendly due to the absence of the potential pollutants such as toluene. CO2 capture was investigated in a dynamic packed column. The sample impregnated by TETA showed the highest adsorption capacity, approximately 2.22 mmol/g at 60℃ due to its highest amino-groups content among the three amines. The CO2 adsorption behavior was also investigated with the deactivation model, which showed an excellent prediction for the breakthrough curves.
文摘制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射(XPD)分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NMR研究了试样中Al的化学环境,结果表明,即使在高铝含量的情况下,样品中的铝原子仍以四配位结合在MCM-41的硅骨架上,未能检测出骨架外六配位铝的存在.文中还就Al含量对孔结构的影响以及Al-MCM-41形成机理作了讨论.