Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat trea...Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat treated in order to obtain a homogenized microstructure.In this study,for the ASR process the rolling speed ratio between upper roller and lower was selected as 1.25.Both SR and ASR processes were utilized with 40%reduction per passes using 2 pass schedule for a total reduction ratio of 0.67.Symmetric and asymmetric rolled sheets were characterized using optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)techniques.Texture measurements were performed by using X-ray diffraction(XRD)technique and mechanical properties were investigated by tensile tests and also hardness measurements.展开更多
In ferritic stainless steels, a significant non-uniform recrystallization orientation and a substantial texture gradient usually occur, which can degrade the ridging resistance of the final sheets. To improve the homo...In ferritic stainless steels, a significant non-uniform recrystallization orientation and a substantial texture gradient usually occur, which can degrade the ridging resistance of the final sheets. To improve the homogeneity of the recrystallization orientation and reduce the texture gradient in ultra-purified 17%Cr ferritic stainless steel, in this work, we performed conventional and asymmetric rolling processes and conducted macro and micro-texture analyses to investigate texture evolution under different cold-rolling conditions. In the conventional rolling specimens, we observed that the deformation was not uniform in the thickness direction, whereas there was homogeneous shear deformation in the asymmetric rolling specimens as well as the formation of uniform recrystallized grains and random orientation grains in the final annealing sheets. As such, the ridging resistance of the final sheets was significantly improved by employing the asymmetric rolling process. This result indicates with certainty that the texture gradient and orientation inhomogeneity can be attributed to non-uniform deformation, whereas the uniform orientation gradient in the thickness direction is explained by the increased number of shear bands obtained in the asymmetric rolling process.展开更多
For refining grain and obtaining excellent properties, the experiments of asymmetric and symmetric monotonic hot rolling were carried out to investigate the role of shear strain on the microstructures and mechanical p...For refining grain and obtaining excellent properties, the experiments of asymmetric and symmetric monotonic hot rolling were carried out to investigate the role of shear strain on the microstructures and mechanical properties of V-microalloyed steel. The study demonstrates that the gradient ferrite distribution and dispersive pearlite through the sheet thickness are observed in asymmetric rolled specimen, and the homogeneous microstructure with ferrite and large pearlite is found in symmetric rolled specimen. The average grain size in asymmetric rolled specimen is smaller than the one in symmetric rolled specimen. The styles of precipitate morphology in asymmetric rolled specimen are random precipitate and obvious interphase precipitate, while the ones in symmetric rolled specimen are random precipitate and unobvious interphase precipitate. The additional shear strain results in the microstructure difference between asymmetric rolled specimen and symmetric rolled specimen. The impact energy of asymmetric rolled specimen, 58 J, is more than the one of symmetric rolled specimen, 48 J. Both deflection-energy curve and fracture morphology show that the fracture style of asymmetric rolled specimen is ductile, and the ones of symmetric rolled specimen are brittle and ductile.展开更多
The analysis of bending in finishing rolling was performed. An asymmetrical rolling force model was established, and the upper and lower neutral points were determined. Thc bending which resulted from the asymmetrical...The analysis of bending in finishing rolling was performed. An asymmetrical rolling force model was established, and the upper and lower neutral points were determined. Thc bending which resulted from the asymmetrical rolling force at the roll gap was studied and related flexibility equations were proposed according to elastic mechanics. Moreover, material mechanics was used to analyze the effects of temperature difference and self-weight on the bending out of the roll gap, and the flexibility equations were constructed. The main factors on bending were summed up, and the bending rule in the rolling could be obtained. In addition practical calculation was made with the production data of ribbon steel from Laiwu Iron & Steel Group Co. Ltd.展开更多
The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divide...The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divided into three zones according to the direction of the friction. Then, the three zones were studied, respectively. A rolling force model and a rolling torque model were developed based on the analysis, and they were used to analyze the influ- ence of asymmetrical rolling factors on deformation area and unit pressure if they had good precision which was determined by comparing the calculated results with the measured ones.展开更多
In asymmetric cold rolling, the workpiece is often bent downwards or upwards. A two-dimensional explicit dynamic finite element model with Arbitrary Lagrangian Eulerian (ALE) adaptive meshing technique has been empl...In asymmetric cold rolling, the workpiece is often bent downwards or upwards. A two-dimensional explicit dynamic finite element model with Arbitrary Lagrangian Eulerian (ALE) adaptive meshing technique has been employed to simulate asymmetrical sheet rolling, in which asymmetrical conditions are here due to different roll radii. To validate the simulation, the results of simulation and experiment are compared. Effects of asymmetry due to roll radii mismatch on the normal and shear distributions and on sheet curvature variations are discussed. An optimum roll radii ratio could be found to produce flat sheet. Trials were conducted to investigate the effectiveness of roll radii mismatch as an approach of sheet curvature control.展开更多
Based on the rigid-plastic finite element method(FEM), the shear stress field of deformation region for high manganese austenite steel during hot asymmetrical rolling process was analyzed. The influences of rolling ...Based on the rigid-plastic finite element method(FEM), the shear stress field of deformation region for high manganese austenite steel during hot asymmetrical rolling process was analyzed. The influences of rolling parameters, such as the velocity ratio of upper to lower rolls, the initial temperature of workpiece and the reduction rate, on the shear deformation of three nodes in the upper, center and lower layers were discussed. As the rolling parameters change, distinct shear deformation appears in the upper and lower layers, but the shear deformation in the center layer appears only when the velocity ratio is more than 1.00, and the absolute value of the shear stress in this layer is changed with rolling parameters. A mathematical model which reflected the change of the maximal absolute shear stress for the center layer was established, by which the maximal absolute shear stress for the center layer can be easily calculated and the appropriate rolling technology can be designed.展开更多
The influence of asymmetric reduction rolling (ARR) on the microstructure, texture and mechanical properties of AZ91 was investigated. The microstructural characteristics of the AZ91 sheet processed by symmetric ro...The influence of asymmetric reduction rolling (ARR) on the microstructure, texture and mechanical properties of AZ91 was investigated. The microstructural characteristics of the AZ91 sheet processed by symmetric roiling (SR) were the twins, intersection of twins and dynamic recrystalization (DRX) grains around the coarse grains and within the twins. However, the amount of twins and DRX grains in ARRed AZ91 was much smaller than that in SRed AZ91. The SRed AZ91 after annealing exhibited fine DRX grains and some coarse grains with a size of ~ 100 pro. The grains in ARRed AZ91 after annealing were much finer and more homogeneous than those in SRed AZ91 after annealing. The intensity of basal texture of ARRed AZ91 after annealing was lower than that of SRed AZ91 rolling after annealing. The average Schmid factor of ARRed AZ91 is 0.34, which is higher than that of SRed AZ91. The yield strength and ultimate tensile strength of the ARRed AZ91 sheet were inCreased to 16.1% and 31.8% compared to SRed AZ91 sheet, from 155 to 180 MPa, and from 220 to 290 MPa, respectively. The improvement of mechanical properties in ARRed AZ91 after annealing was attributed to much finer, more homogeneous DRX grains and weaker basal texture.展开更多
Asymmetrical hot rolling(ASHR) was proposed to acquire productive grain refinement for Fe-20Mn-4Al-0.3C and Fe-18Cr-18Mn-0.5N non-magnetic austenitic steels. The intensive additional shear deformation caused by ASHR...Asymmetrical hot rolling(ASHR) was proposed to acquire productive grain refinement for Fe-20Mn-4Al-0.3C and Fe-18Cr-18Mn-0.5N non-magnetic austenitic steels. The intensive additional shear deformation caused by ASHR promotes the nucleation of recrystallization and grain refining of steel plates. With the speed ratio of 1.2, the austenitic grains were refined to ~5 m on the surface, the recrystallization fraction was enhanced to ~34.7%, and the thickness of fine-grained surface layer increases to ~450m for Fe-20Mn-4Al-0.3 C steel. The Fe-18Cr-18Mn-0.5N steel also exhibited an effective surface grain refinement with an average size of ~3μm, and the recrystallization fraction reached ~76.9% at the speed ratio of 1.15.展开更多
A bulk nanostructured twinning-induced plasticity (TWIP) steel with high ductility and high strength was fabricated by cryogenic asymmetry-rolling (cryo-ASR) and subsequent recovery treatment. It was found that th...A bulk nanostructured twinning-induced plasticity (TWIP) steel with high ductility and high strength was fabricated by cryogenic asymmetry-rolling (cryo-ASR) and subsequent recovery treatment. It was found that the cryo-ASRed TWIP steels exhibit simultaneous improvements in the ductility, strength and work hardening. Typical microstructures of the cryo-ASR TWIP steel were characterized by shear bands and intensive mechanical nano-sized twins induced by cryogenic deformation. These mechanical nano-scale twins remain thermally stable during the subsequent recovery treatment. It is believed that the ductility enhancement and high work-hardening ability for the cryo-ASR TWIP steels should be mainly attributed to the high-densitv pre-existing nano-scale twins.展开更多
Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this mode...Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this model, the non- uniform normal and shear stresses and the upper and lower surface temperatures of the workpiece were taken into ac- count. Moreover, the flow stress model, considering the dynamic recovery and dynamic recrystallization behaviors of the material, was established. The rolling pressure distribution, the rolling force, the rolling torque and the neutral points could be calculated quickly and easily by the roiling force model. The predicted results were shown to be in good agreement with the measured values, which indicated that the model can satisfy the requirement of industrial application.展开更多
Experiments show that special processing techniques such as asymmetrical rolling (ASR), equal channel angular pressing (ECAP) and equal channel angular rolling (ECAR) can weaken the basal texture of the magnesiu...Experiments show that special processing techniques such as asymmetrical rolling (ASR), equal channel angular pressing (ECAP) and equal channel angular rolling (ECAR) can weaken the basal texture of the magnesium alloys and therefore improve their plasticity. However, the deformation mechanisms related are different. In this paper, we determine the deformation mechanisms activated during ASR, ECAP and ECAR by calculation of orientation factors. Analysis shows that during ASR the shear stress σ13 on the rolling plane of the samples obviously weakens the basal slip and tension twinning that all produce basal texture and improve plasticity due to the promotion of tilt basal texture. During ECAP the shear stress σs on the intersecting plane of two channels promotes tension twinning in the basal oriented grains, whereas under ECAR the shear stress σ13 induced by roller friction on the rolling plane produces the shear stress as on the intersection plane of the two channels that also promotes tension twinning. Although the shear strain is lower in ECAR than in ECAP, the channel clearance in ECAR facilitates tension twinning.展开更多
文摘Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat treated in order to obtain a homogenized microstructure.In this study,for the ASR process the rolling speed ratio between upper roller and lower was selected as 1.25.Both SR and ASR processes were utilized with 40%reduction per passes using 2 pass schedule for a total reduction ratio of 0.67.Symmetric and asymmetric rolled sheets were characterized using optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)techniques.Texture measurements were performed by using X-ray diffraction(XRD)technique and mechanical properties were investigated by tensile tests and also hardness measurements.
基金financially supported by the National Key R&D Program of China (2016YFB0300200)National Natural Science Foundation of China (Nos. U1660114 and 51174026)
文摘In ferritic stainless steels, a significant non-uniform recrystallization orientation and a substantial texture gradient usually occur, which can degrade the ridging resistance of the final sheets. To improve the homogeneity of the recrystallization orientation and reduce the texture gradient in ultra-purified 17%Cr ferritic stainless steel, in this work, we performed conventional and asymmetric rolling processes and conducted macro and micro-texture analyses to investigate texture evolution under different cold-rolling conditions. In the conventional rolling specimens, we observed that the deformation was not uniform in the thickness direction, whereas there was homogeneous shear deformation in the asymmetric rolling specimens as well as the formation of uniform recrystallized grains and random orientation grains in the final annealing sheets. As such, the ridging resistance of the final sheets was significantly improved by employing the asymmetric rolling process. This result indicates with certainty that the texture gradient and orientation inhomogeneity can be attributed to non-uniform deformation, whereas the uniform orientation gradient in the thickness direction is explained by the increased number of shear bands obtained in the asymmetric rolling process.
基金Funded by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China during the“12th Five-Year Plan”(No.2011BAE25B03)the National Natural Science Foundation of China(No.51274063)the National High Technology Research and Development Program of China(No.2015AA03A501)
文摘For refining grain and obtaining excellent properties, the experiments of asymmetric and symmetric monotonic hot rolling were carried out to investigate the role of shear strain on the microstructures and mechanical properties of V-microalloyed steel. The study demonstrates that the gradient ferrite distribution and dispersive pearlite through the sheet thickness are observed in asymmetric rolled specimen, and the homogeneous microstructure with ferrite and large pearlite is found in symmetric rolled specimen. The average grain size in asymmetric rolled specimen is smaller than the one in symmetric rolled specimen. The styles of precipitate morphology in asymmetric rolled specimen are random precipitate and obvious interphase precipitate, while the ones in symmetric rolled specimen are random precipitate and unobvious interphase precipitate. The additional shear strain results in the microstructure difference between asymmetric rolled specimen and symmetric rolled specimen. The impact energy of asymmetric rolled specimen, 58 J, is more than the one of symmetric rolled specimen, 48 J. Both deflection-energy curve and fracture morphology show that the fracture style of asymmetric rolled specimen is ductile, and the ones of symmetric rolled specimen are brittle and ductile.
文摘The analysis of bending in finishing rolling was performed. An asymmetrical rolling force model was established, and the upper and lower neutral points were determined. Thc bending which resulted from the asymmetrical rolling force at the roll gap was studied and related flexibility equations were proposed according to elastic mechanics. Moreover, material mechanics was used to analyze the effects of temperature difference and self-weight on the bending out of the roll gap, and the flexibility equations were constructed. The main factors on bending were summed up, and the bending rule in the rolling could be obtained. In addition practical calculation was made with the production data of ribbon steel from Laiwu Iron & Steel Group Co. Ltd.
基金Item Sponsored by National Natural Science Foundation of China (50104006)National Key Technology Research and Development Program of China(2006BAE03A08)
文摘The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divided into three zones according to the direction of the friction. Then, the three zones were studied, respectively. A rolling force model and a rolling torque model were developed based on the analysis, and they were used to analyze the influ- ence of asymmetrical rolling factors on deformation area and unit pressure if they had good precision which was determined by comparing the calculated results with the measured ones.
基金Sponsored by National Basic Research Program of China(2011CB606306-2)Scientific Research Fund for Young Teachers of China(N100307001)
文摘In asymmetric cold rolling, the workpiece is often bent downwards or upwards. A two-dimensional explicit dynamic finite element model with Arbitrary Lagrangian Eulerian (ALE) adaptive meshing technique has been employed to simulate asymmetrical sheet rolling, in which asymmetrical conditions are here due to different roll radii. To validate the simulation, the results of simulation and experiment are compared. Effects of asymmetry due to roll radii mismatch on the normal and shear distributions and on sheet curvature variations are discussed. An optimum roll radii ratio could be found to produce flat sheet. Trials were conducted to investigate the effectiveness of roll radii mismatch as an approach of sheet curvature control.
基金Item Sponsored by National Natural Science Foundation of China(51274062)
文摘Based on the rigid-plastic finite element method(FEM), the shear stress field of deformation region for high manganese austenite steel during hot asymmetrical rolling process was analyzed. The influences of rolling parameters, such as the velocity ratio of upper to lower rolls, the initial temperature of workpiece and the reduction rate, on the shear deformation of three nodes in the upper, center and lower layers were discussed. As the rolling parameters change, distinct shear deformation appears in the upper and lower layers, but the shear deformation in the center layer appears only when the velocity ratio is more than 1.00, and the absolute value of the shear stress in this layer is changed with rolling parameters. A mathematical model which reflected the change of the maximal absolute shear stress for the center layer was established, by which the maximal absolute shear stress for the center layer can be easily calculated and the appropriate rolling technology can be designed.
基金financially supported by the National Natural Science Foundation of China(No.51271046)
文摘The influence of asymmetric reduction rolling (ARR) on the microstructure, texture and mechanical properties of AZ91 was investigated. The microstructural characteristics of the AZ91 sheet processed by symmetric roiling (SR) were the twins, intersection of twins and dynamic recrystalization (DRX) grains around the coarse grains and within the twins. However, the amount of twins and DRX grains in ARRed AZ91 was much smaller than that in SRed AZ91. The SRed AZ91 after annealing exhibited fine DRX grains and some coarse grains with a size of ~ 100 pro. The grains in ARRed AZ91 after annealing were much finer and more homogeneous than those in SRed AZ91 after annealing. The intensity of basal texture of ARRed AZ91 after annealing was lower than that of SRed AZ91 rolling after annealing. The average Schmid factor of ARRed AZ91 is 0.34, which is higher than that of SRed AZ91. The yield strength and ultimate tensile strength of the ARRed AZ91 sheet were inCreased to 16.1% and 31.8% compared to SRed AZ91 sheet, from 155 to 180 MPa, and from 220 to 290 MPa, respectively. The improvement of mechanical properties in ARRed AZ91 after annealing was attributed to much finer, more homogeneous DRX grains and weaker basal texture.
基金financially supported by the National Natural Science Foundation of China(Grant No.51274062)the Research Fund for the Doctoral Program of Higher Education of China(Grant No.20130042110040)
文摘Asymmetrical hot rolling(ASHR) was proposed to acquire productive grain refinement for Fe-20Mn-4Al-0.3C and Fe-18Cr-18Mn-0.5N non-magnetic austenitic steels. The intensive additional shear deformation caused by ASHR promotes the nucleation of recrystallization and grain refining of steel plates. With the speed ratio of 1.2, the austenitic grains were refined to ~5 m on the surface, the recrystallization fraction was enhanced to ~34.7%, and the thickness of fine-grained surface layer increases to ~450m for Fe-20Mn-4Al-0.3 C steel. The Fe-18Cr-18Mn-0.5N steel also exhibited an effective surface grain refinement with an average size of ~3μm, and the recrystallization fraction reached ~76.9% at the speed ratio of 1.15.
基金financially supported by the Jiangxi Provincial Science and Technology Department(No.20151BDH80082)the China National Major Science and Technology Project(No.2014ZX07214-002)the financial support from China Postdoctoral Science Foundation(No.2015M581608)
文摘A bulk nanostructured twinning-induced plasticity (TWIP) steel with high ductility and high strength was fabricated by cryogenic asymmetry-rolling (cryo-ASR) and subsequent recovery treatment. It was found that the cryo-ASRed TWIP steels exhibit simultaneous improvements in the ductility, strength and work hardening. Typical microstructures of the cryo-ASR TWIP steel were characterized by shear bands and intensive mechanical nano-sized twins induced by cryogenic deformation. These mechanical nano-scale twins remain thermally stable during the subsequent recovery treatment. It is believed that the ductility enhancement and high work-hardening ability for the cryo-ASR TWIP steels should be mainly attributed to the high-densitv pre-existing nano-scale twins.
基金Item Sponsored by National Science and Technology Major Project of China(2011ZX04002-101)National Science and Technology Support Plan of China(2011BAF15B02)National Natural Science Foundation of China(51305388)
文摘Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this model, the non- uniform normal and shear stresses and the upper and lower surface temperatures of the workpiece were taken into ac- count. Moreover, the flow stress model, considering the dynamic recovery and dynamic recrystallization behaviors of the material, was established. The rolling pressure distribution, the rolling force, the rolling torque and the neutral points could be calculated quickly and easily by the roiling force model. The predicted results were shown to be in good agreement with the measured values, which indicated that the model can satisfy the requirement of industrial application.
基金support from the National Natural Science Foundation of China(Nos50571009 and 50771019)
文摘Experiments show that special processing techniques such as asymmetrical rolling (ASR), equal channel angular pressing (ECAP) and equal channel angular rolling (ECAR) can weaken the basal texture of the magnesium alloys and therefore improve their plasticity. However, the deformation mechanisms related are different. In this paper, we determine the deformation mechanisms activated during ASR, ECAP and ECAR by calculation of orientation factors. Analysis shows that during ASR the shear stress σ13 on the rolling plane of the samples obviously weakens the basal slip and tension twinning that all produce basal texture and improve plasticity due to the promotion of tilt basal texture. During ECAP the shear stress σs on the intersecting plane of two channels promotes tension twinning in the basal oriented grains, whereas under ECAR the shear stress σ13 induced by roller friction on the rolling plane produces the shear stress as on the intersection plane of the two channels that also promotes tension twinning. Although the shear strain is lower in ECAR than in ECAP, the channel clearance in ECAR facilitates tension twinning.