Spray auto-ignition experiments were carried out in a constant volume combustion chamber for some pure alkanes(n-paraffins with different chain length, cyclohexane, n-butyl cyclohexane, and isooctane) and blends of n-...Spray auto-ignition experiments were carried out in a constant volume combustion chamber for some pure alkanes(n-paraffins with different chain length, cyclohexane, n-butyl cyclohexane, and isooctane) and blends of n-decane with Standard Blended Fuel(isooctane/n-heptane) and product gasoline. Test results showed that the reaction activity of n-paraffins was relatively high. Meanwhile, the auto-ignition characteristics differed significantly with the molecular structures of alkanes. Adding different volume fractions of n-decane to Standard Blended Fuel and product gasoline could improve the fuel reaction activity at varying degree. Finally, functional groups effects were used to simulate the relationship between the molecular topology and the auto-ignition quality.展开更多
Based on the structure of chute - feed and autoleveHer, an analysis of their working principle and the verification of their practical production results have been carried out. Finally, the future investigation direet...Based on the structure of chute - feed and autoleveHer, an analysis of their working principle and the verification of their practical production results have been carried out. Finally, the future investigation direetiom of chute - feed and card autuleveller are put forward.展开更多
WC?10Co?4Cr and Cr3C2?25NiCr coatings were deposited on H13 steel by high velocity oxy fuel (HVOF) spraying. To enhance the thermal stability of the WC?10Co?4Cr coating, NiCr powders were sprayed between the surface c...WC?10Co?4Cr and Cr3C2?25NiCr coatings were deposited on H13 steel by high velocity oxy fuel (HVOF) spraying. To enhance the thermal stability of the WC?10Co?4Cr coating, NiCr powders were sprayed between the surface coating and substrate. The microstructures of the surface and cross section, thermal shock and wear resistance of these two coatings were investigated in detail. The carbon diffusion in the two coatings was explained from the view of the thermodynamic. And the adhesive strength of Cr3C2?25NiCr coating (64.40 MPa) is almost the same as that of WC?10Co?4Cr coating (61.69 MPa). The friction tests show that the Cr3C2?25NiCr coating has higher friction coefficient than the WC?10Co?4Cr coating at both 500 and 600 °C. The wear resistance of the Cr3C2?25NiCr coating is better than that of the WC?10Co?4Cr coating.展开更多
An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coati...An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coatings was comprehensively evaluated based on both anti-corrosion and anti-biofouling properties.The results reveal that the sealing treatment is remarkably useful to decrease the porosity of the coating,and the porosity of the coating sealed with the hybrid agent is only 0.035%.Immersion corrosion test and Tafel polarization test reveal that the sealed coating with the hybrid agent exhibits a better corrosion resistance by compared with the coating sealed with silicone agent.The corrosion current density i_(corr) of the hybrid agent sealed coating is only 0.7×10^(-6)A·cm^(-2).Moreover,anti-biofouling tests both in the outdoor analogue hydraulic environment and in the natural marine environment prove that the mentioned novel coating presents a better combination of corrosion resistance and anti-biofouling property by compared with the other coatings,and it could be used as a protection of metal components in the marine environment.展开更多
Proteus 170O - TEQ insecticide was subjected through rigorous testing over years （2005 to 2008） at four concentrations 0.15% （9 mls/10L.H20）, 0.31% （18 mls/10L.H2O）, 0.46% （27 mls/10L.H2O） and 0.61% （36 mls/1...Proteus 170O - TEQ insecticide was subjected through rigorous testing over years （2005 to 2008） at four concentrations 0.15% （9 mls/10L.H20）, 0.31% （18 mls/10L.H2O）, 0.46% （27 mls/10L.H2O） and 0.61% （36 mls/10L.H2O）. Each concentration was replicated three times in the field. The mortality rates of mirids on exposure to the various concentrations of Proteus and Standard miricide in the laboratory were similar at 0.46% concentration as both gave a 100% kill ofmirids at the 40th minute. The first year field mortalities of mirids recorded 24 hours after the initial and residual applications at the Ibadan, Owena and Ikom at 0.46% active ingredient concentration gave 100% kill of mirids. The mortalities of mirids recorded 24 hours after the second year field initial and residual treatments at the lowest concentration of 0.15% active ingredient ranged between 70.2% and 100%. In the third year, the insecticide at 0.31% concentration compared favourably with the Standard. The residues of thiacloprid in the analyzed cocoa bean samples were below the Limit of Quantitation （LOQ） of 0.01 mg/kg. Spraying of mature and fruiting cocoa farms at application rate of 0.46% was found adequate and recommended.展开更多
The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing...The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.展开更多
基金funded by the National Key Research and Development Program (2017YFB0306505)
文摘Spray auto-ignition experiments were carried out in a constant volume combustion chamber for some pure alkanes(n-paraffins with different chain length, cyclohexane, n-butyl cyclohexane, and isooctane) and blends of n-decane with Standard Blended Fuel(isooctane/n-heptane) and product gasoline. Test results showed that the reaction activity of n-paraffins was relatively high. Meanwhile, the auto-ignition characteristics differed significantly with the molecular structures of alkanes. Adding different volume fractions of n-decane to Standard Blended Fuel and product gasoline could improve the fuel reaction activity at varying degree. Finally, functional groups effects were used to simulate the relationship between the molecular topology and the auto-ignition quality.
文摘Based on the structure of chute - feed and autoleveHer, an analysis of their working principle and the verification of their practical production results have been carried out. Finally, the future investigation direetiom of chute - feed and card autuleveller are put forward.
基金Project(51371200)supported by the National Natural Science Foundation of ChinaProject(2014CB644000)supported by the National Basic Research Program of ChinaProject(502044009)supported by the Fundamental Research Funds for the Central Universities,China
文摘WC?10Co?4Cr and Cr3C2?25NiCr coatings were deposited on H13 steel by high velocity oxy fuel (HVOF) spraying. To enhance the thermal stability of the WC?10Co?4Cr coating, NiCr powders were sprayed between the surface coating and substrate. The microstructures of the surface and cross section, thermal shock and wear resistance of these two coatings were investigated in detail. The carbon diffusion in the two coatings was explained from the view of the thermodynamic. And the adhesive strength of Cr3C2?25NiCr coating (64.40 MPa) is almost the same as that of WC?10Co?4Cr coating (61.69 MPa). The friction tests show that the Cr3C2?25NiCr coating has higher friction coefficient than the WC?10Co?4Cr coating at both 500 and 600 °C. The wear resistance of the Cr3C2?25NiCr coating is better than that of the WC?10Co?4Cr coating.
基金the National Natural Science Foundation of China(No.51379070)the Graduate Research and Innovation Projects of Jiangsu Province(No.KYCX21_0463)。
文摘An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coatings was comprehensively evaluated based on both anti-corrosion and anti-biofouling properties.The results reveal that the sealing treatment is remarkably useful to decrease the porosity of the coating,and the porosity of the coating sealed with the hybrid agent is only 0.035%.Immersion corrosion test and Tafel polarization test reveal that the sealed coating with the hybrid agent exhibits a better corrosion resistance by compared with the coating sealed with silicone agent.The corrosion current density i_(corr) of the hybrid agent sealed coating is only 0.7×10^(-6)A·cm^(-2).Moreover,anti-biofouling tests both in the outdoor analogue hydraulic environment and in the natural marine environment prove that the mentioned novel coating presents a better combination of corrosion resistance and anti-biofouling property by compared with the other coatings,and it could be used as a protection of metal components in the marine environment.
文摘Proteus 170O - TEQ insecticide was subjected through rigorous testing over years （2005 to 2008） at four concentrations 0.15% （9 mls/10L.H20）, 0.31% （18 mls/10L.H2O）, 0.46% （27 mls/10L.H2O） and 0.61% （36 mls/10L.H2O）. Each concentration was replicated three times in the field. The mortality rates of mirids on exposure to the various concentrations of Proteus and Standard miricide in the laboratory were similar at 0.46% concentration as both gave a 100% kill ofmirids at the 40th minute. The first year field mortalities of mirids recorded 24 hours after the initial and residual applications at the Ibadan, Owena and Ikom at 0.46% active ingredient concentration gave 100% kill of mirids. The mortalities of mirids recorded 24 hours after the second year field initial and residual treatments at the lowest concentration of 0.15% active ingredient ranged between 70.2% and 100%. In the third year, the insecticide at 0.31% concentration compared favourably with the Standard. The residues of thiacloprid in the analyzed cocoa bean samples were below the Limit of Quantitation （LOQ） of 0.01 mg/kg. Spraying of mature and fruiting cocoa farms at application rate of 0.46% was found adequate and recommended.
文摘The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.