The process characteristics of heat treatment of aluminum alloy auto body sheet and the working principle of air cushion furnace were introduced.The process position and irreplaceable role of air cushion furnace in th...The process characteristics of heat treatment of aluminum alloy auto body sheet and the working principle of air cushion furnace were introduced.The process position and irreplaceable role of air cushion furnace in the aluminum alloy auto body sheet production was pointed out after the difficulty and key points in the whole production process of auto body sheet were studied.Then the development process of air cushion furnace line of aluminum alloy sheet was reviewed,summarized and divided to two stages.Based on the research of air cushion furnace,the key technology of it was analyzed,then the key points on process,equipment and control models of air cushion furnace for aluminum alloy auto body sheet in future were put forward.With the rapid development of automotive industry,there will be certainly a new upsurge of research and application of air cushion furnace for heat treatment of aluminum alloy auto body sheet.展开更多
Three different types of tensile strength （TS） 980 MPa grade advanced high-strength steels used in automotive applications, namely, 980MS （ martensite steel ）, 980DP （ dual phase ） and 980QP （ quenching and par...Three different types of tensile strength （TS） 980 MPa grade advanced high-strength steels used in automotive applications, namely, 980MS （ martensite steel ）, 980DP （ dual phase ） and 980QP （ quenching and partitioning） steels were examined. The delayed fracture resistance of the steels was evaluated using a U-bend test, slow strain rate test（SSRT） and a constant load tensile test. The results indicated that all the steels could pass the 300 h HC1 solution immersion test and none of the U-bend specimens was fractured in the test. However,the steels exhibited different susceptibilities to delayed fracture under SSRT and the constant load tensile tests. 980DP exhibited the highest resistance to delayed fracture among all the samples, while 980MS was found to be the most susceptible to delayed fracture.展开更多
文摘The process characteristics of heat treatment of aluminum alloy auto body sheet and the working principle of air cushion furnace were introduced.The process position and irreplaceable role of air cushion furnace in the aluminum alloy auto body sheet production was pointed out after the difficulty and key points in the whole production process of auto body sheet were studied.Then the development process of air cushion furnace line of aluminum alloy sheet was reviewed,summarized and divided to two stages.Based on the research of air cushion furnace,the key technology of it was analyzed,then the key points on process,equipment and control models of air cushion furnace for aluminum alloy auto body sheet in future were put forward.With the rapid development of automotive industry,there will be certainly a new upsurge of research and application of air cushion furnace for heat treatment of aluminum alloy auto body sheet.
文摘Three different types of tensile strength （TS） 980 MPa grade advanced high-strength steels used in automotive applications, namely, 980MS （ martensite steel ）, 980DP （ dual phase ） and 980QP （ quenching and partitioning） steels were examined. The delayed fracture resistance of the steels was evaluated using a U-bend test, slow strain rate test（SSRT） and a constant load tensile test. The results indicated that all the steels could pass the 300 h HC1 solution immersion test and none of the U-bend specimens was fractured in the test. However,the steels exhibited different susceptibilities to delayed fracture under SSRT and the constant load tensile tests. 980DP exhibited the highest resistance to delayed fracture among all the samples, while 980MS was found to be the most susceptible to delayed fracture.