The local environment of Cu atoms in Fe73.5Cu1Nb3Si13.5B9 alloy was investigated by extended X-ray absorption fine structure(EXAFS).Cu clusters began to order when the annealing temperature was around 733 K from the r...The local environment of Cu atoms in Fe73.5Cu1Nb3Si13.5B9 alloy was investigated by extended X-ray absorption fine structure(EXAFS).Cu clusters began to order when the annealing temperature was around 733 K from the results of the Fourier transform curves.The fitting results showed that the first shell of the near fcc(face-centered cubic)Cu clusters only contained Cu atoms.The coordination number increased with the annealing temperature.Subsequently,the occupancy rate increased from 33.3%(annealed at 733 K)to 100% (annealed at 853 K).This local structural change of Cu atoms could probably affect the distribution of the bcc(body-centered cubic)α-Fe in Fe73.5Cu1Nb3Si13.5B9 alloy.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51071109)the Young Excellent Talents in Tongji University(Grant No.2009KJ003)
文摘The local environment of Cu atoms in Fe73.5Cu1Nb3Si13.5B9 alloy was investigated by extended X-ray absorption fine structure(EXAFS).Cu clusters began to order when the annealing temperature was around 733 K from the results of the Fourier transform curves.The fitting results showed that the first shell of the near fcc(face-centered cubic)Cu clusters only contained Cu atoms.The coordination number increased with the annealing temperature.Subsequently,the occupancy rate increased from 33.3%(annealed at 733 K)to 100% (annealed at 853 K).This local structural change of Cu atoms could probably affect the distribution of the bcc(body-centered cubic)α-Fe in Fe73.5Cu1Nb3Si13.5B9 alloy.