The semi-continuous seeded emulsion eopolymerization of vinyl acetate and butyl acrylate was carried out with hydroxyethyl cellulose as a colloid stabilizer. The morphology of the latex particle and the relationship b...The semi-continuous seeded emulsion eopolymerization of vinyl acetate and butyl acrylate was carried out with hydroxyethyl cellulose as a colloid stabilizer. The morphology of the latex particle and the relationship between the reaction time and the average particle diameter and/or the conversion ratio during the polymerization were invstiguted. The experimental results shaw that the morphology of the latex particle possesses the stable sterie construction. In the seeded polymerizution, the average particle diameter of latex decreased while the conversion ratio increased. At the second term of the emulsion copolymerization （the growth stage of particle size）, the latex particle average diameter increased with copolymerization continuously, but the instantaneous conversation ratio was not large, so it was very necessaO to properly prolong the time during the holding temperature stage.展开更多
文摘The semi-continuous seeded emulsion eopolymerization of vinyl acetate and butyl acrylate was carried out with hydroxyethyl cellulose as a colloid stabilizer. The morphology of the latex particle and the relationship between the reaction time and the average particle diameter and/or the conversion ratio during the polymerization were invstiguted. The experimental results shaw that the morphology of the latex particle possesses the stable sterie construction. In the seeded polymerizution, the average particle diameter of latex decreased while the conversion ratio increased. At the second term of the emulsion copolymerization （the growth stage of particle size）, the latex particle average diameter increased with copolymerization continuously, but the instantaneous conversation ratio was not large, so it was very necessaO to properly prolong the time during the holding temperature stage.