The texture evolution of ferritic hot rolled Ti-IF steel during cold rolling was investigated in which the reduction was from 15% to 85 %. It was found that α fibre texture was monotonously intensified with the incre...The texture evolution of ferritic hot rolled Ti-IF steel during cold rolling was investigated in which the reduction was from 15% to 85 %. It was found that α fibre texture was monotonously intensified with the increase in the cold rolling reduction, while y fibre texture changed in a different way. When the cold rolling reduction was in the range of 15 % -- 35 % or 45 % -- 75 %, γ fibre texture was strengthened ; however, when the cold rolling reduction was 35 %- 45 % or 75 %- 85%, the intensity of 7 fibre was reduced. The 7 fibre displayed a maximum intensity for the reduction of 75%, and the highest average plastic strain ratio was simultaneously obtained owing to the favorable recrystallization texture.展开更多
基金Item Sponsored by National Natural Science Foundation of China (50104004)
文摘The texture evolution of ferritic hot rolled Ti-IF steel during cold rolling was investigated in which the reduction was from 15% to 85 %. It was found that α fibre texture was monotonously intensified with the increase in the cold rolling reduction, while y fibre texture changed in a different way. When the cold rolling reduction was in the range of 15 % -- 35 % or 45 % -- 75 %, γ fibre texture was strengthened ; however, when the cold rolling reduction was 35 %- 45 % or 75 %- 85%, the intensity of 7 fibre was reduced. The 7 fibre displayed a maximum intensity for the reduction of 75%, and the highest average plastic strain ratio was simultaneously obtained owing to the favorable recrystallization texture.