Limit loads are widely studied and several limit load solutions are proposed to some typical geometry of weldments.However,there are no limit load solutions exist for the single edge crack weldments in tension（SEC（...Limit loads are widely studied and several limit load solutions are proposed to some typical geometry of weldments.However,there are no limit load solutions exist for the single edge crack weldments in tension（SEC（T））,which is also a typical geometry in fracture analysis.The mis-matching limit load for thick plate with SEC（T） are investigated and the special limit load solutions are proposed based on the available mis-matching limit load solutions and systematic finite element analyses.The real weld configurations are simplified as a strip,and different weld strength mis-matching ratio M,crack depth/width ratio a/W and weld width 2H are in consideration.As a result,it is found that there exists excellent agreement between the limit load solutions and the FE results for almost all the mis-matching ration M,a/W and ligament-to-weld width ratio（W-a）/H.Moreover,useful recommendations are given for evaluating the limit loads of the EBW structure with SEC（T）.For the EBW joints with SEC（T）,the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal,when M changing from 1.6 to 0.6.When M decreasing to 0.4,the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal only for large value of（W-a）/H.The recommendations may be useful for evaluating the limit loads of the EBW structures with SEC（T）.The engineering simplifications are given for assessing the limit loads of electron beam welded structure with SEC（T）.展开更多
The creep crack growth(CCG)and the time to carck initiation and rupture of specimen (t_(rc)and t_r)were measured by means of electrical potential method on single edge notched specimens at 700℃.The field near the cra...The creep crack growth(CCG)and the time to carck initiation and rupture of specimen (t_(rc)and t_r)were measured by means of electrical potential method on single edge notched specimens at 700℃.The field near the crack tip under steady-state creep was represented by energy rate integral(C~*),and the CCG rate as a function of C~* has been obtained.The agreement between the predicted and observed t_(rc)values is quite good.It was found that the addition of small amount of Mg and Zr in the alloys causes t_(rc)and t_r of the specimens to in- crease significantly.展开更多
低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度...低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。展开更多
基金supported by National Natural Science Foundation of China (Grant No. 50935008)
文摘Limit loads are widely studied and several limit load solutions are proposed to some typical geometry of weldments.However,there are no limit load solutions exist for the single edge crack weldments in tension（SEC（T））,which is also a typical geometry in fracture analysis.The mis-matching limit load for thick plate with SEC（T） are investigated and the special limit load solutions are proposed based on the available mis-matching limit load solutions and systematic finite element analyses.The real weld configurations are simplified as a strip,and different weld strength mis-matching ratio M,crack depth/width ratio a/W and weld width 2H are in consideration.As a result,it is found that there exists excellent agreement between the limit load solutions and the FE results for almost all the mis-matching ration M,a/W and ligament-to-weld width ratio（W-a）/H.Moreover,useful recommendations are given for evaluating the limit loads of the EBW structure with SEC（T）.For the EBW joints with SEC（T）,the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal,when M changing from 1.6 to 0.6.When M decreasing to 0.4,the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal only for large value of（W-a）/H.The recommendations may be useful for evaluating the limit loads of the EBW structures with SEC（T）.The engineering simplifications are given for assessing the limit loads of electron beam welded structure with SEC（T）.
文摘The creep crack growth(CCG)and the time to carck initiation and rupture of specimen (t_(rc)and t_r)were measured by means of electrical potential method on single edge notched specimens at 700℃.The field near the crack tip under steady-state creep was represented by energy rate integral(C~*),and the CCG rate as a function of C~* has been obtained.The agreement between the predicted and observed t_(rc)values is quite good.It was found that the addition of small amount of Mg and Zr in the alloys causes t_(rc)and t_r of the specimens to in- crease significantly.
文摘低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。