Cu(NO3)(2) and (NH4)(6)H(2)W(12)O(40)center dot 4H(2)O were used to prepare W/Cu nanosized composite powder by sol-gel technique. The influences of heat treatment process, pH value of the solution and the amount of an...Cu(NO3)(2) and (NH4)(6)H(2)W(12)O(40)center dot 4H(2)O were used to prepare W/Cu nanosized composite powder by sol-gel technique. The influences of heat treatment process, pH value of the solution and the amount of an addition agent on particle size were investigated by DSC, XRD and TEM. The results show that, at a certain heat treatment temperature, the W/Cu nanoparticle size increases with the pH value or the amount of the addition agent increasing.展开更多
Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental res...Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental results showed that: (1) the ball milled Mo/Cu powder has lamellar structure, (2) the microstructures of the sintered Mo-Cu alloy were homogenous compound structures of adhesive phase Cu linking Mo grains, (3) Mo grains frequently strung or gathered in Cu phase, and (4) the full densities of Mo-Cu alloy was achieved through sintering and special densification process. As a result, the properties of the alloy are good enough to satisfy various requirements.展开更多
Mechanically activated W-Cu powders were sintered by a spark plasma sinteringsystem (SPS) in order to develop a new process and improve the properties of the alloy. Propertiessuch as density and hardness were measured...Mechanically activated W-Cu powders were sintered by a spark plasma sinteringsystem (SPS) in order to develop a new process and improve the properties of the alloy. Propertiessuch as density and hardness were measured. The microstructures of the sintered W-Cu alloy sampleswere observed by SEM (scanning electron microscope). The results show that spark plasma sinteringcan obviously lower the sintering temperature and increase the density of the alloy. This processcan also improve the hardness of the alloy. SPS is an effective method to obtain W-Cu powders withhigh density and superior physical properties.展开更多
Highly supersaturated nanocrystalline fcc Fe60Cu40 alloy has been prepared by mechanical alloying of elemental powders. The phase transformation is monitored by X-ray diffraction (XRD),Mossbauer spectroscopy and exten...Highly supersaturated nanocrystalline fcc Fe60Cu40 alloy has been prepared by mechanical alloying of elemental powders. The phase transformation is monitored by X-ray diffraction (XRD),Mossbauer spectroscopy and extended X-ray absorption fine structure (EXAFS). The powder obtained after milling is of single fcc structure with grain size of nanometer order. The Mossbauer spectra of the milled powder can be fitted by two subspectra whose hyperfine magnetic fields are 16 MA/m and 20 MA/m while that of pure Fe disappeared. EXAFS results show that the radial structure function (RSF) of Fe K-edge changed drastically and finally became similar to that of reference Cu K-edge, while that of Cu K-edge nearly keeps unchanged in the process of milling. These imply that bcc Fe really transforms to fcc structure and alloying between Fe and Cu occurs truly on an atomic scale. EXAFS results indicate that iron atoms tend to segregate at the boundaries and Cu atoms are rich in the fcc lattice. Annealing experiments show that the Fe atoms at the interfaces are easy to cluster to α-Fe at a lower temperature, whereas the iron atoms in the lattice will form γ-Fe first at temperature above 350℃, and then transform to bcc Fe展开更多
W-15% Cu (mass fraction) alloys were sintered with mechanically activated powder in order to develop new preparing processes and improve properties of alloys. The microstructures of the activated powder and the sinter...W-15% Cu (mass fraction) alloys were sintered with mechanically activated powder in order to develop new preparing processes and improve properties of alloys. The microstructures of the activated powder and the sintered alloy were observed. Properties such as density were measured. The results show that through mechanical activation, the particle size of the powder becomes finer to sub-micron or nanometer level, some copper was soluble in tungsten, and high density W-Cu alloys can be obtained by mechanically activated powder for its action to the activation sintering.展开更多
Al-20Sn-1Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa. The characteristics of the powders are determined by means of dry sieving, scanning electron mic...Al-20Sn-1Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa. The characteristics of the powders are determined by means of dry sieving, scanning electron microscopy （SEM）, optical microscopy （OM）, and X-ray diffractometry （XRD）. The results show that the powders exhibit a bimodal size distribution and a higher gas pressure results in a broad size distribution. All particles in both cases are spherical or nearly spherical and satellites form on the surface of coarse particles. Dendritic and cellular structures coexist in the particle. With decreasing particle diameter, the secondary dendrite arm spacing （SDAS） decreases and the cooling rate increases. The particles processed under high gas atomization pressure （1.6 MPa） exhibit a lower SDAS value and a higher cooling rate than those of the same size under low gas atomization pressure （1.1 MPa）. The XRD results show that the Sn content increases with decreasing particle size.展开更多
A multi-component Cu-based metal powder was chosen for direct laser sintering. The powder consists of a mixture of high-purity Cu powder, pre-alloyed CuSn and CuP powder. Liquid phase sintering with complete melting o...A multi-component Cu-based metal powder was chosen for direct laser sintering. The powder consists of a mixture of high-purity Cu powder, pre-alloyed CuSn and CuP powder. Liquid phase sintering with complete melting of the binder (CuSn) but non-melting of the cores of structural metal (Cu) proves to be a feasible mechanism for laser sintering of this powder system. The microstructural evolution of the sintered powder with variation of laser processing parameters was presented. High sintering activities and sound densification response were obtained by optimizing the laser powers and scan speeds. Using a high laser power accompanied by a high scan speed gives rise to balling effect. At a high laser power with a slow scan speed the sintering mechanism may change into complete melting/solidification, which decreases the obtainable sintered density. The role of additive phosphorus in the laser sintering process is addressed. Phosphorus can act as a fluxing agent and has a preferential reaction with oxygen to form phosphatic slag, protecting the Cu particles from oxidation. The phosphatic slag shows a concentration along grain boundaries due to its light mass as well as the short thermal cycle of SLS.展开更多
Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characte...Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.展开更多
The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reductio...The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reduction technology were investigated. In comparison to the conventional HE sintering processing, microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time. Furthermore, higher performances in microwave sintered compacts were obtained, but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.展开更多
The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymeri...The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.展开更多
基金Natural Science Foundation of China(No.51871244)Hunan Provincial Innovation Foundation for Postgraduate,China(No.CX20200172)Fundamental Research Funds for the Central Universities of Central South University,China(No.1053320190103)。
基金supported by the Key Laboratory of Micro-systems and Micro-structures Manufacturing of Ministry of Education,Harbin Institute of Technology,China(No.2020KM005)the Natural Science Foundation of Heilongjiang Province,China(No.YQ2020E030)。
基金This Project was financially supported by the National Natural Science Foundation of China (No. 50471033).
文摘Cu(NO3)(2) and (NH4)(6)H(2)W(12)O(40)center dot 4H(2)O were used to prepare W/Cu nanosized composite powder by sol-gel technique. The influences of heat treatment process, pH value of the solution and the amount of an addition agent on particle size were investigated by DSC, XRD and TEM. The results show that, at a certain heat treatment temperature, the W/Cu nanoparticle size increases with the pH value or the amount of the addition agent increasing.
文摘Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental results showed that: (1) the ball milled Mo/Cu powder has lamellar structure, (2) the microstructures of the sintered Mo-Cu alloy were homogenous compound structures of adhesive phase Cu linking Mo grains, (3) Mo grains frequently strung or gathered in Cu phase, and (4) the full densities of Mo-Cu alloy was achieved through sintering and special densification process. As a result, the properties of the alloy are good enough to satisfy various requirements.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50174007)
文摘Mechanically activated W-Cu powders were sintered by a spark plasma sinteringsystem (SPS) in order to develop a new process and improve the properties of the alloy. Propertiessuch as density and hardness were measured. The microstructures of the sintered W-Cu alloy sampleswere observed by SEM (scanning electron microscope). The results show that spark plasma sinteringcan obviously lower the sintering temperature and increase the density of the alloy. This processcan also improve the hardness of the alloy. SPS is an effective method to obtain W-Cu powders withhigh density and superior physical properties.
文摘Highly supersaturated nanocrystalline fcc Fe60Cu40 alloy has been prepared by mechanical alloying of elemental powders. The phase transformation is monitored by X-ray diffraction (XRD),Mossbauer spectroscopy and extended X-ray absorption fine structure (EXAFS). The powder obtained after milling is of single fcc structure with grain size of nanometer order. The Mossbauer spectra of the milled powder can be fitted by two subspectra whose hyperfine magnetic fields are 16 MA/m and 20 MA/m while that of pure Fe disappeared. EXAFS results show that the radial structure function (RSF) of Fe K-edge changed drastically and finally became similar to that of reference Cu K-edge, while that of Cu K-edge nearly keeps unchanged in the process of milling. These imply that bcc Fe really transforms to fcc structure and alloying between Fe and Cu occurs truly on an atomic scale. EXAFS results indicate that iron atoms tend to segregate at the boundaries and Cu atoms are rich in the fcc lattice. Annealing experiments show that the Fe atoms at the interfaces are easy to cluster to α-Fe at a lower temperature, whereas the iron atoms in the lattice will form γ-Fe first at temperature above 350℃, and then transform to bcc Fe
文摘W-15% Cu (mass fraction) alloys were sintered with mechanically activated powder in order to develop new preparing processes and improve properties of alloys. The microstructures of the activated powder and the sintered alloy were observed. Properties such as density were measured. The results show that through mechanical activation, the particle size of the powder becomes finer to sub-micron or nanometer level, some copper was soluble in tungsten, and high density W-Cu alloys can be obtained by mechanically activated powder for its action to the activation sintering.
基金the Major State Ba-sic Research Development Program of China (Nos. 2006CB605203 and 2006CB605204)
文摘Al-20Sn-1Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa. The characteristics of the powders are determined by means of dry sieving, scanning electron microscopy （SEM）, optical microscopy （OM）, and X-ray diffractometry （XRD）. The results show that the powders exhibit a bimodal size distribution and a higher gas pressure results in a broad size distribution. All particles in both cases are spherical or nearly spherical and satellites form on the surface of coarse particles. Dendritic and cellular structures coexist in the particle. With decreasing particle diameter, the secondary dendrite arm spacing （SDAS） decreases and the cooling rate increases. The particles processed under high gas atomization pressure （1.6 MPa） exhibit a lower SDAS value and a higher cooling rate than those of the same size under low gas atomization pressure （1.1 MPa）. The XRD results show that the Sn content increases with decreasing particle size.
文摘A multi-component Cu-based metal powder was chosen for direct laser sintering. The powder consists of a mixture of high-purity Cu powder, pre-alloyed CuSn and CuP powder. Liquid phase sintering with complete melting of the binder (CuSn) but non-melting of the cores of structural metal (Cu) proves to be a feasible mechanism for laser sintering of this powder system. The microstructural evolution of the sintered powder with variation of laser processing parameters was presented. High sintering activities and sound densification response were obtained by optimizing the laser powers and scan speeds. Using a high laser power accompanied by a high scan speed gives rise to balling effect. At a high laser power with a slow scan speed the sintering mechanism may change into complete melting/solidification, which decreases the obtainable sintered density. The role of additive phosphorus in the laser sintering process is addressed. Phosphorus can act as a fluxing agent and has a preferential reaction with oxygen to form phosphatic slag, protecting the Cu particles from oxidation. The phosphatic slag shows a concentration along grain boundaries due to its light mass as well as the short thermal cycle of SLS.
基金supported by the National Natural Science Foundation of China (No.50574075)Program for New Century Excellent Talents in University(No.NCET-05-0873)Specialized Research Fund for the Doctoral Program of Higher Education (SRFDP 20060700011)
文摘Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.
基金Funded by the Project for Science and Technology Plan of Wuhan City(200910321092)the Youth Science Plan for Light of the Morning Sun of Wuhan City (200750731270)
文摘The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reduction technology were investigated. In comparison to the conventional HE sintering processing, microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time. Furthermore, higher performances in microwave sintered compacts were obtained, but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.
文摘The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.