Two novel poly[(3-alkylthiophene-2,5-diyl)-(benzylidenequinomethane-2,5-diyl)s] derivatives, poly[ (3-butylthiophene-2,5-diyl)-( p-N,N-dimethylamino) benzylidenequinomethane-2,5-diyl) ] ( PBTDMABQ) and poly [( 3-octyl...Two novel poly[(3-alkylthiophene-2,5-diyl)-(benzylidenequinomethane-2,5-diyl)s] derivatives, poly[ (3-butylthiophene-2,5-diyl)-( p-N,N-dimethylamino) benzylidenequinomethane-2,5-diyl) ] ( PBTDMABQ) and poly [( 3-octylthiophene2,5-diyl) -(p-N, N-dimethylamino ) benzylidenequinomethane-2, 5-diyl)] (POTDMABQ), were synthesized.The band gaps of the two polymers are calculated as 1. 75 eV for PBTDMABQ and 1. 69 eV for POTDMABQ,respectively. The homogenous films of the two polymers were prepared and their third-ordernonlinear optical properties were studied by the backward degenerate four-wave mixing at 532 nm. Byusing the relative measurement technique, the third-order nonlinear optical susceptibilities ofPBTDMABQ and POTDMABQ are calculated as 5. 62 X 10^(-9) and 1. 22 X 10^(-8) ESU, respectively. It isfound that substituted alky groups have strong effects on the band gap and nonlinear opticalproperties of the two polymers. The relatively big third-order nonlinear optical susceptibilitiesand small band gap of POTDMABQ resulted mainly from the longer alkyl with strong electron-donatingability can enhance the delocation degree of conjugated π electronics.展开更多
In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of t...In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.展开更多
基金National Natural Science Foundation of China (60277002)
文摘Two novel poly[(3-alkylthiophene-2,5-diyl)-(benzylidenequinomethane-2,5-diyl)s] derivatives, poly[ (3-butylthiophene-2,5-diyl)-( p-N,N-dimethylamino) benzylidenequinomethane-2,5-diyl) ] ( PBTDMABQ) and poly [( 3-octylthiophene2,5-diyl) -(p-N, N-dimethylamino ) benzylidenequinomethane-2, 5-diyl)] (POTDMABQ), were synthesized.The band gaps of the two polymers are calculated as 1. 75 eV for PBTDMABQ and 1. 69 eV for POTDMABQ,respectively. The homogenous films of the two polymers were prepared and their third-ordernonlinear optical properties were studied by the backward degenerate four-wave mixing at 532 nm. Byusing the relative measurement technique, the third-order nonlinear optical susceptibilities ofPBTDMABQ and POTDMABQ are calculated as 5. 62 X 10^(-9) and 1. 22 X 10^(-8) ESU, respectively. It isfound that substituted alky groups have strong effects on the band gap and nonlinear opticalproperties of the two polymers. The relatively big third-order nonlinear optical susceptibilitiesand small band gap of POTDMABQ resulted mainly from the longer alkyl with strong electron-donatingability can enhance the delocation degree of conjugated π electronics.
基金This report is part of the fundamental research report with contract No.486 127/UN14.2/PNL.01.03.00/2016.
文摘In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.