To investigate value in use of liquefied wood-based resin applications in molding material, Chinese fir （Cunninghamia lanceolata） and poplar （Populus tomentosa） wood meal were liquefied in phenol. The reactant was...To investigate value in use of liquefied wood-based resin applications in molding material, Chinese fir （Cunninghamia lanceolata） and poplar （Populus tomentosa） wood meal were liquefied in phenol. The reactant was co-condensed with formaldehyde to obtain liquefied wood-based resin. For this paper, we investigated the characterization of the resin and its application in molding material. The result shows that the basic properties of liquefied wood-based resin were satisfactory; the bonding strength of plywood prepared with liquefied Chinese fir and liquefied poplar resin can reach 1.54 and 1.00 MPa, respectively. The compression strengths of the molding material prepared with two kinds of liquefied wood resin were 73.01 and 73.58 MPa, almost the same as that of PF resin molding material. The limiting volume swelling of molding material made with liquefied Chinese resin and liquefied poplar resin were 8.5% and 8.3%, thickness swelling rates of water absorption were 3.3% and 4.2%, and the maximum weight ratios of water absorption were 25.9% and 26.2%, respectively. The soil burial test result shows that the weight loss rate of the molding materials made with liquefied Chinese resin and liquefied poplar resin were 8.3% and 9.1% and that of the PF resin molding material was 7.9%. After the soil internment test, the reduction ratio of compression strength of the two kinds of molding material achieved 16.9% and 17.7%, while that of the PF resin molding material was 15.4%. The test results of wood fungi inoculation on the three surfaces of the molding material indicate the breeding rate of molding material prepared with liquefied Chinese resin and liquefied poplar resin were at level 4 and that of PF resin molding material was at level 1 of the ISO standard.展开更多
On the basis of the comprehensive analysis about the automatic generation of the injection mold parting surface, the parting surface design method which introduces knowledge and case-based reasoning （CBR） into the c...On the basis of the comprehensive analysis about the automatic generation of the injection mold parting surface, the parting surface design method which introduces knowledge and case-based reasoning （CBR） into the computer-aided design is described by combining with the actual characteristic in injection mold design, and the design process of case-based reasoning method is also given. A case library including the information of parting surface is built with the index of main shape features, The automatic design of the mold parting surface is realized combined with the forward-reasoning method and the similarity solution procedure. The rule knowledge library is also founded including the knowledge, principles and experiences for parting surface design. An example is used to show the validity of the method, and the quality and the efficiency of the mold design are improved.展开更多
Effect of two-stage sintering parameters such as heating rate, top sintering temperature and holding time, sintering temperature and holding time at the second stage on relative density, transverse rupture strength(TR...Effect of two-stage sintering parameters such as heating rate, top sintering temperature and holding time, sintering temperature and holding time at the second stage on relative density, transverse rupture strength(TRS) and microstructures of powder injection molded Ti(C, N)-based cermets were investigated, by means of Archimedes’s method, three-point bending test and micrographic analysis. The results show that the optimum sintering cycle for powder injection molded Ti(C, N)-based cermets comprises rapid heating (10℃/min) at low temperatures, slow heating (5℃/min) at intermediate temperatures, holding at the highest sintering temperature (1420℃) for a short time (10min), and holding at the second stage (1360℃) for a longer time (6h) to avoid grain coarsening, and that its TRS reaches 624MPa, and there are little pores in their microstructures.展开更多
基金This study was financially supported by the National Natural Science Foundation of China （Grant No. 30471351）.
文摘To investigate value in use of liquefied wood-based resin applications in molding material, Chinese fir （Cunninghamia lanceolata） and poplar （Populus tomentosa） wood meal were liquefied in phenol. The reactant was co-condensed with formaldehyde to obtain liquefied wood-based resin. For this paper, we investigated the characterization of the resin and its application in molding material. The result shows that the basic properties of liquefied wood-based resin were satisfactory; the bonding strength of plywood prepared with liquefied Chinese fir and liquefied poplar resin can reach 1.54 and 1.00 MPa, respectively. The compression strengths of the molding material prepared with two kinds of liquefied wood resin were 73.01 and 73.58 MPa, almost the same as that of PF resin molding material. The limiting volume swelling of molding material made with liquefied Chinese resin and liquefied poplar resin were 8.5% and 8.3%, thickness swelling rates of water absorption were 3.3% and 4.2%, and the maximum weight ratios of water absorption were 25.9% and 26.2%, respectively. The soil burial test result shows that the weight loss rate of the molding materials made with liquefied Chinese resin and liquefied poplar resin were 8.3% and 9.1% and that of the PF resin molding material was 7.9%. After the soil internment test, the reduction ratio of compression strength of the two kinds of molding material achieved 16.9% and 17.7%, while that of the PF resin molding material was 15.4%. The test results of wood fungi inoculation on the three surfaces of the molding material indicate the breeding rate of molding material prepared with liquefied Chinese resin and liquefied poplar resin were at level 4 and that of PF resin molding material was at level 1 of the ISO standard.
文摘On the basis of the comprehensive analysis about the automatic generation of the injection mold parting surface, the parting surface design method which introduces knowledge and case-based reasoning （CBR） into the computer-aided design is described by combining with the actual characteristic in injection mold design, and the design process of case-based reasoning method is also given. A case library including the information of parting surface is built with the index of main shape features, The automatic design of the mold parting surface is realized combined with the forward-reasoning method and the similarity solution procedure. The rule knowledge library is also founded including the knowledge, principles and experiences for parting surface design. An example is used to show the validity of the method, and the quality and the efficiency of the mold design are improved.
文摘Effect of two-stage sintering parameters such as heating rate, top sintering temperature and holding time, sintering temperature and holding time at the second stage on relative density, transverse rupture strength(TRS) and microstructures of powder injection molded Ti(C, N)-based cermets were investigated, by means of Archimedes’s method, three-point bending test and micrographic analysis. The results show that the optimum sintering cycle for powder injection molded Ti(C, N)-based cermets comprises rapid heating (10℃/min) at low temperatures, slow heating (5℃/min) at intermediate temperatures, holding at the highest sintering temperature (1420℃) for a short time (10min), and holding at the second stage (1360℃) for a longer time (6h) to avoid grain coarsening, and that its TRS reaches 624MPa, and there are little pores in their microstructures.