It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. T...It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li2O to CaO based fluxes was recommended.展开更多
It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing...It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li 2O to CaO based fluxes was recommended.展开更多
An effective process for recycling lead from hazardous waste cathode ray tubes(CRTs) funnel glass through traditional lead smelting has been presented previously. The viscous behavior of the molten high lead slag, w...An effective process for recycling lead from hazardous waste cathode ray tubes(CRTs) funnel glass through traditional lead smelting has been presented previously. The viscous behavior of the molten high lead slag, which is affected by the addition of funnel glass, plays a critical role in determining the production efficiency. Therefore, the viscosities of the CaO–SiO_2–"FeO"–12wt%ZnO–3wt%Al_2O_3 slags were measured in the current study using the rotating spindle method. The slag viscosity decreases as the CaO/SiO_2 mass ratio is increased from 0.8 to 1.2 and also as the FeO content is increased from 8wt% to 20wt%. The breaking temperature of the slag is lowered substantially by the addition of FeO, whereas the influence of the CaO/SiO_2 mass ratio on the breaking temperature is complex. The structural analysis of quenched slags using Fourier transform infrared(FTIR) spectroscopy and Raman spectroscopy reveals that the silicate network structure is depolymerized with increasing CaO/SiO_2 mass ratio or increasing FeO content. The [FeO_6]-octahedra in the slag melt increase as the CaO/SiO_2 mass ratio or the FeO content increases. This increase can further decrease the degree of polymerization(DOP) of the slag. Furthermore, the activation energy for viscous flow decreases both with increasing CaO/SiO_2 mass ratio and increasing FeO content.展开更多
基金Item Sponsored by National Natural Science Foundation of China(59774015)
文摘It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li2O to CaO based fluxes was recommended.
基金the support of Wong K C Education Foundation , Hong Kong
文摘It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li 2O to CaO based fluxes was recommended.
基金financially supported by the National Natural Science Foundation of China (Nos. 51374066 and 51304047)the National Key Technologies R&D Program (No. 2014BAC03B07)the Industrial Research Projects in Liaoning Province, China (Nos. 2012223002 and 2014020037)
文摘An effective process for recycling lead from hazardous waste cathode ray tubes(CRTs) funnel glass through traditional lead smelting has been presented previously. The viscous behavior of the molten high lead slag, which is affected by the addition of funnel glass, plays a critical role in determining the production efficiency. Therefore, the viscosities of the CaO–SiO_2–"FeO"–12wt%ZnO–3wt%Al_2O_3 slags were measured in the current study using the rotating spindle method. The slag viscosity decreases as the CaO/SiO_2 mass ratio is increased from 0.8 to 1.2 and also as the FeO content is increased from 8wt% to 20wt%. The breaking temperature of the slag is lowered substantially by the addition of FeO, whereas the influence of the CaO/SiO_2 mass ratio on the breaking temperature is complex. The structural analysis of quenched slags using Fourier transform infrared(FTIR) spectroscopy and Raman spectroscopy reveals that the silicate network structure is depolymerized with increasing CaO/SiO_2 mass ratio or increasing FeO content. The [FeO_6]-octahedra in the slag melt increase as the CaO/SiO_2 mass ratio or the FeO content increases. This increase can further decrease the degree of polymerization(DOP) of the slag. Furthermore, the activation energy for viscous flow decreases both with increasing CaO/SiO_2 mass ratio and increasing FeO content.