Two novel copolymers based on benzothiadizole-thiophene-phenylenevinylene have been synthesized through palladium catalyzed triple-bond polycondensation method.The copolymers exhibit good solubility in common organic ...Two novel copolymers based on benzothiadizole-thiophene-phenylenevinylene have been synthesized through palladium catalyzed triple-bond polycondensation method.The copolymers exhibit good solubility in common organic solvents such as CHCl;,CH;Cl;and THF.The structures and properties of the two copolymers are characterized by FT-IR,;H-NMR,UV-Vis absorbance（Abs）,gel permeation chromatography（GPC）,thermal gravimetric analysis and cyclic voltammetry（CV）.The copolymers of P;and P;show absorption spectra with maximum peak at 532 nm and 573 nm in solution,respectively.Compare to their monomers M;and M;,the absorption peaks of P;and P;were red-shifted by 34 nm and 54 nm respectively.Thermal gravimetric analysis demonstrated that the polymers were stable and little weight loss was observed below 300℃.Cyclic voltammetry experiments showed that the band gaps of the copolymers were 1.81 eV and 1.62 eV,respectively,suggesting their potential for applications as organic solar cell materials.展开更多
基金supported by the Key Foundation of Education Ministry of China(No.20070610053)Sichuan Province Foundation for Youths(No.2008JY0050)
文摘Two novel copolymers based on benzothiadizole-thiophene-phenylenevinylene have been synthesized through palladium catalyzed triple-bond polycondensation method.The copolymers exhibit good solubility in common organic solvents such as CHCl;,CH;Cl;and THF.The structures and properties of the two copolymers are characterized by FT-IR,;H-NMR,UV-Vis absorbance（Abs）,gel permeation chromatography（GPC）,thermal gravimetric analysis and cyclic voltammetry（CV）.The copolymers of P;and P;show absorption spectra with maximum peak at 532 nm and 573 nm in solution,respectively.Compare to their monomers M;and M;,the absorption peaks of P;and P;were red-shifted by 34 nm and 54 nm respectively.Thermal gravimetric analysis demonstrated that the polymers were stable and little weight loss was observed below 300℃.Cyclic voltammetry experiments showed that the band gaps of the copolymers were 1.81 eV and 1.62 eV,respectively,suggesting their potential for applications as organic solar cell materials.