The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and o...The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and one lower, were used to partially replace Portland cement at 0%, 10%, and 30% by weight. The water to binder ratio（w/b） of 0.5 was used for all the blended cement paste mixes. Experimental results indicate that the blended cement of activated coal gangue mortar with higher kaolin mineral content has a higher compressive strength than that with lower kaolin mineral content. The porosity and pore size of blended cement mortar were significantly affected by the replacement of activated coal gangue.展开更多
An amended method for accurate measuring the quantity of calcium silicate hydrate(C-S-H) in pure cement paste and blended cement paste by water adsorption was made, which based on R.A.Olson’s method. Two improvements...An amended method for accurate measuring the quantity of calcium silicate hydrate(C-S-H) in pure cement paste and blended cement paste by water adsorption was made, which based on R.A.Olson’s method. Two improvements to this method, such as using C-S-H gel by hydro-thermal synthesis as standard sample and the stoichiometry of C-S-H gel is partitioned based on hydration time and the amount of mineral admixture. The result of C-S-H gel content in pure cement paste and blended cement paste is higher than by R.A.Olson’s method.展开更多
基金the National Basic Research Program of China(No.2001CB610703)the Basic Research of Preparation and Application of High Performance Cement
文摘The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and one lower, were used to partially replace Portland cement at 0%, 10%, and 30% by weight. The water to binder ratio（w/b） of 0.5 was used for all the blended cement paste mixes. Experimental results indicate that the blended cement of activated coal gangue mortar with higher kaolin mineral content has a higher compressive strength than that with lower kaolin mineral content. The porosity and pore size of blended cement mortar were significantly affected by the replacement of activated coal gangue.
基金Funded by the Ministry of Science and Technology of the People's Republic of China (No. 2001CD610704-2) Wuhan City Chenguan Plan (No. 20055003059231)
文摘An amended method for accurate measuring the quantity of calcium silicate hydrate(C-S-H) in pure cement paste and blended cement paste by water adsorption was made, which based on R.A.Olson’s method. Two improvements to this method, such as using C-S-H gel by hydro-thermal synthesis as standard sample and the stoichiometry of C-S-H gel is partitioned based on hydration time and the amount of mineral admixture. The result of C-S-H gel content in pure cement paste and blended cement paste is higher than by R.A.Olson’s method.