Boric acid and kieserite were prepared from low-grade ascharite by sulfuric acid method.This method results in the recovery of 71.06%and 45.03%for boric acid and kieserite,respectively.Meanwhile,the boric acid was pre...Boric acid and kieserite were prepared from low-grade ascharite by sulfuric acid method.This method results in the recovery of 71.06%and 45.03%for boric acid and kieserite,respectively.Meanwhile,the boric acid was precipitated from the filtrate at low temperature and the solution was recycled without discharging waste liquid in the whole process.The influence of amount of sulfuric acid,mass fraction of sulfuric acid,reaction temperature and reaction time on the leaching rate of boric acid were studied. The results show that the leaching rate of boric acid reaches 93.80%under the following conditions:the amount of sulfuric acid is 85%of theoretical dosage;the mass fraction of sulfuric acid is 25%;reaction temperature is 95℃;and the reaction time is 100 min. Meanwhile,the effects of mass fraction of magnesium sulfate,crystallization temperature and crystallization time on the crystallization of kieserite were investigated and the optimal crystallization conditions are obtained:the mass fraction of magnesium sulfate is 28%;the crystallization temperature is 180℃and the crystallization time is 4h.展开更多
The activation effect of boric acid as an activator is good,and we investigate the best activation conditions for the boric acid impregnation method.To represent the structural characteristics and adsorption performan...The activation effect of boric acid as an activator is good,and we investigate the best activation conditions for the boric acid impregnation method.To represent the structural characteristics and adsorption performance of the Stellera Chamaejasme based carbon molecular sieves,we use Brunner-Emmet-Teller(BET)measurements,scan-ning electron microscope(SEM),Raman spectra(Raman),X-ray diffraction(XRD),and adsorption property measurement.When the loading ratio was 0.68:1,the specific surface area was 532.21 m^(2)/g,the total pore volume was 0.24 cm 3/g,the average pore size was 1.81 nm,the adsorption value of methylene blue was 145.28 mg/g,and the adsorption value of iodine was 713.33 mg/g,the results showed that boric acid had better activation effect.The carbon molecular sieves made from Stellera Chamaejasme and activated with boric acid produce two peaks on the aperture distribution graph that are densely distributed in the micropore range.This indicates that boric acid’s pore-forming tendency is primarily micropore.展开更多
基金Project(2006AA06Z368) supported by the National High-tech Research and Development Program of China
文摘Boric acid and kieserite were prepared from low-grade ascharite by sulfuric acid method.This method results in the recovery of 71.06%and 45.03%for boric acid and kieserite,respectively.Meanwhile,the boric acid was precipitated from the filtrate at low temperature and the solution was recycled without discharging waste liquid in the whole process.The influence of amount of sulfuric acid,mass fraction of sulfuric acid,reaction temperature and reaction time on the leaching rate of boric acid were studied. The results show that the leaching rate of boric acid reaches 93.80%under the following conditions:the amount of sulfuric acid is 85%of theoretical dosage;the mass fraction of sulfuric acid is 25%;reaction temperature is 95℃;and the reaction time is 100 min. Meanwhile,the effects of mass fraction of magnesium sulfate,crystallization temperature and crystallization time on the crystallization of kieserite were investigated and the optimal crystallization conditions are obtained:the mass fraction of magnesium sulfate is 28%;the crystallization temperature is 180℃and the crystallization time is 4h.
基金Graduate Innovation Project of Qinghai University for Nationalities(2021XJXS12)Graduate Innovation Project of Qinghai University for Nationalities(12M2021018).
文摘The activation effect of boric acid as an activator is good,and we investigate the best activation conditions for the boric acid impregnation method.To represent the structural characteristics and adsorption performance of the Stellera Chamaejasme based carbon molecular sieves,we use Brunner-Emmet-Teller(BET)measurements,scan-ning electron microscope(SEM),Raman spectra(Raman),X-ray diffraction(XRD),and adsorption property measurement.When the loading ratio was 0.68:1,the specific surface area was 532.21 m^(2)/g,the total pore volume was 0.24 cm 3/g,the average pore size was 1.81 nm,the adsorption value of methylene blue was 145.28 mg/g,and the adsorption value of iodine was 713.33 mg/g,the results showed that boric acid had better activation effect.The carbon molecular sieves made from Stellera Chamaejasme and activated with boric acid produce two peaks on the aperture distribution graph that are densely distributed in the micropore range.This indicates that boric acid’s pore-forming tendency is primarily micropore.