The Mg-Al-Ti-B alloy prepared by mechanical alloying is poor in microstructural uniformity and compactness. In order to improve the microstructural uniformity and compactness of Mg-Al-Ti-B alloy and thus to improve th...The Mg-Al-Ti-B alloy prepared by mechanical alloying is poor in microstructural uniformity and compactness. In order to improve the microstructural uniformity and compactness of Mg-Al-Ti-B alloy and thus to improve the mechanical properties, effect of B2O3 on microstructure and mechanical properties of cast Mg-9Al-6Ti alloy was studied by optical microscopy, scanning electron microscopy, X-ray diffraction and mechanical property testing. The results show that due to the addition of B2O3, the average grain size of Mg-Al-Ti-B alloys is refined to 12μm, dispersed Ti phases completely disappear, the amount of precipitation phase Mgl7All2 is reduced and TiA13 is increased, and new phases MgB6 and TiaB4 are precipitated. The average hardness, average tensile strength, yield strength and elongation of the alloy are HV 77.1, 171.2 MPa, 113.5 MPa and 5.2%, respectively.展开更多
基金Project (2009MS0802) supported by the Inner Mongolian Natural Science Foundation of ChinaProject supported by Inner Mongolia Autonomous Region Talent Development fund of China
文摘The Mg-Al-Ti-B alloy prepared by mechanical alloying is poor in microstructural uniformity and compactness. In order to improve the microstructural uniformity and compactness of Mg-Al-Ti-B alloy and thus to improve the mechanical properties, effect of B2O3 on microstructure and mechanical properties of cast Mg-9Al-6Ti alloy was studied by optical microscopy, scanning electron microscopy, X-ray diffraction and mechanical property testing. The results show that due to the addition of B2O3, the average grain size of Mg-Al-Ti-B alloys is refined to 12μm, dispersed Ti phases completely disappear, the amount of precipitation phase Mgl7All2 is reduced and TiA13 is increased, and new phases MgB6 and TiaB4 are precipitated. The average hardness, average tensile strength, yield strength and elongation of the alloy are HV 77.1, 171.2 MPa, 113.5 MPa and 5.2%, respectively.