The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), s...The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: there occurred three new formation phases, Cu(s.s), FeNi and Ag(s.s) in TiC cermet/iron joint. The interface structure was expressed as TiC cermet/Cu(s.s)+FeNi/Ag(s.s)+a little Cu(s.s)+a little FeNi/Cu(s.s)+FeNi/iron, With brazing time increasing, there appeared highest shear strength of the joints, the value of which was up to 252.2MPa when brazing time was 10min.展开更多
Gas pore is a common defect in brazed joint. It lowers the brazing rate and affects the properties of joint. Experimental results show that the application of unequal-gap brazing seam effectively decreases the amount ...Gas pore is a common defect in brazed joint. It lowers the brazing rate and affects the properties of joint. Experimental results show that the application of unequal-gap brazing seam effectively decreases the amount and volume of gas pores, and increases brazing rate.This paper establishes a force model of unequal-gap brazing seam, and proposes the constitutive relationship between expulsion force and curvature. The force condition of gas bubble in geometrically different brazing seams were calculated, and the results were verified with experiments. The results show that the expulsion force of gas bubble is positively correlated to the curvature of the seam geometry. The gas bubble tends to move towards the direction with large curvature and wider gap. The directional bubble movement is obtained through varying the configuration of gas-liquid interface to meet geometric conditions. Gas bubble accelerates to expulse with arc, hyperbola and cycloid brazing seams, in which the best drainage effects of gas bubble occur for cycloid seams.展开更多
In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melt...In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melting temperature was measured by differential scanning calorimetry(DSC),and the brazability of Ag-50Cu-5Ga alloy on copper and metallized copper/kovar were ascertained at 850℃under 1×10-4 Pa in this article.The microstructures of the filler metal and the joints have been analyzed by using scanning electron microscopy(SEM),equipped with an energy dispersive spectroscopy.The results show that vacuum brazing was success to join with copper or metallized copper/kovar using Ag-50Cu-5Ga filler and reliable joints were obtained.There were Ag-rich phase,Cu-rich phase and a fine eutectic structure of Ag-based solid solution and Cu-based solid solution in the copper joints and the width of brazing seam is about 60μm.The joints of kovar alloy to copper after surface nickel plating was composed of AgCu eutectic phase,Ag,Cu,Cu2Ga and CuNi2 phase.The tensile strength was 167 MPa and 150 MPa,respectively.The tensile results of joints show that the joint strengths were equivalent to the traditional brazing filler metals.展开更多
BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and we...BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were tested.During the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal alloy.The matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel matrix.The mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 MPa.The dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.展开更多
When a brazed plate heat exchanger is used as an evaporator,the working mass in the channel may undergo soli-dification,thereby hindering the refrigeration cycle.In this study the liquid solidification process and its o...When a brazed plate heat exchanger is used as an evaporator,the working mass in the channel may undergo soli-dification,thereby hindering the refrigeration cycle.In this study the liquid solidification process and its optimi-zation in a brazed plate heat exchanger are investigated numerically for different inlet velocities;moreover,different levels of corrugation are considered.The results indicate that solidificationfirst occurs around the con-tacts,followed by the area behind the contacts.It is also shown that deadflow zones exist in the sharp areas and such areas are prone to liquid solidification.After optimization,the solidification area attains its smallest value when a corrugation spacingλ=4.2 mm is considered.展开更多
Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The tem...Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The temperature variation of powder and paste coating is systematically studied,and the heat conduction mode and path in the brazecoating process are analyzed.The results show that rise of the coating temperature mainly depends on the heat absorption from the substrate.The liquid-solid interface conducts heat violently and advances step by step,which promotes the melting spread of metal filler metal.The powdery brazecoating material is in a free state,and there is a gas insulation film between the powder particles and the diamond,making it difficult for substrate to conduct heat to the coating.The binder not only assists forming,shell making and oxygen isolation,but also plays an important role during melting.展开更多
基金sponsored by National Natural Science Foundation (No.50175021)National Key Laboratory of Advanced Welding Production Technology of Harbin Institute of Technology,China.
文摘The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: there occurred three new formation phases, Cu(s.s), FeNi and Ag(s.s) in TiC cermet/iron joint. The interface structure was expressed as TiC cermet/Cu(s.s)+FeNi/Ag(s.s)+a little Cu(s.s)+a little FeNi/Cu(s.s)+FeNi/iron, With brazing time increasing, there appeared highest shear strength of the joints, the value of which was up to 252.2MPa when brazing time was 10min.
基金supported by the 2020 Ningbo"3315 Talent Introduction Plan"Innovative Team (C-Class)Henan Province's Major Key Technology Demand Unveiling and Tackling Key Projects (Grant No. 191110111000)。
文摘Gas pore is a common defect in brazed joint. It lowers the brazing rate and affects the properties of joint. Experimental results show that the application of unequal-gap brazing seam effectively decreases the amount and volume of gas pores, and increases brazing rate.This paper establishes a force model of unequal-gap brazing seam, and proposes the constitutive relationship between expulsion force and curvature. The force condition of gas bubble in geometrically different brazing seams were calculated, and the results were verified with experiments. The results show that the expulsion force of gas bubble is positively correlated to the curvature of the seam geometry. The gas bubble tends to move towards the direction with large curvature and wider gap. The directional bubble movement is obtained through varying the configuration of gas-liquid interface to meet geometric conditions. Gas bubble accelerates to expulse with arc, hyperbola and cycloid brazing seams, in which the best drainage effects of gas bubble occur for cycloid seams.
基金the National Key R&D Program of China(Grant No.2017YFB0305702).
文摘In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melting temperature was measured by differential scanning calorimetry(DSC),and the brazability of Ag-50Cu-5Ga alloy on copper and metallized copper/kovar were ascertained at 850℃under 1×10-4 Pa in this article.The microstructures of the filler metal and the joints have been analyzed by using scanning electron microscopy(SEM),equipped with an energy dispersive spectroscopy.The results show that vacuum brazing was success to join with copper or metallized copper/kovar using Ag-50Cu-5Ga filler and reliable joints were obtained.There were Ag-rich phase,Cu-rich phase and a fine eutectic structure of Ag-based solid solution and Cu-based solid solution in the copper joints and the width of brazing seam is about 60μm.The joints of kovar alloy to copper after surface nickel plating was composed of AgCu eutectic phase,Ag,Cu,Cu2Ga and CuNi2 phase.The tensile strength was 167 MPa and 150 MPa,respectively.The tensile results of joints show that the joint strengths were equivalent to the traditional brazing filler metals.
基金supported by the National Natural Science Foundation of China(Grant No.U2004186).
文摘BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were tested.During the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal alloy.The matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel matrix.The mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 MPa.The dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.
基金This research is supported by the Scientific Problem Tackling Program of Science and Technology Commission of Shanghai Municipality(18DZ1202000)the Shanghai Local University Project“Research and Application of Key Technologies of New Efficient Micro Gas Turbine System”(No.19020500900).
文摘When a brazed plate heat exchanger is used as an evaporator,the working mass in the channel may undergo soli-dification,thereby hindering the refrigeration cycle.In this study the liquid solidification process and its optimi-zation in a brazed plate heat exchanger are investigated numerically for different inlet velocities;moreover,different levels of corrugation are considered.The results indicate that solidificationfirst occurs around the con-tacts,followed by the area behind the contacts.It is also shown that deadflow zones exist in the sharp areas and such areas are prone to liquid solidification.After optimization,the solidification area attains its smallest value when a corrugation spacingλ=4.2 mm is considered.
基金supported by the 2020 Ningbo “3315 Talent Introduction Plan” Innovative Team (C-Class)the major project of Ningbo “Scientific and Technological Innovation 2025”(Grant No.2020Z111)Science and Technology Major Project of Zhejiang Province (No.203ZP20220161)
文摘Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The temperature variation of powder and paste coating is systematically studied,and the heat conduction mode and path in the brazecoating process are analyzed.The results show that rise of the coating temperature mainly depends on the heat absorption from the substrate.The liquid-solid interface conducts heat violently and advances step by step,which promotes the melting spread of metal filler metal.The powdery brazecoating material is in a free state,and there is a gas insulation film between the powder particles and the diamond,making it difficult for substrate to conduct heat to the coating.The binder not only assists forming,shell making and oxygen isolation,but also plays an important role during melting.