The treatment of the Gacun complex Cu-Pb bulk concentrate with high Zn,Ag,etc.,by oxygen pressure acid leaching was studied.The pri-mary copper and leadminerals in the concentrate are tetrahedrite and galena.The treat...The treatment of the Gacun complex Cu-Pb bulk concentrate with high Zn,Ag,etc.,by oxygen pressure acid leaching was studied.The pri-mary copper and leadminerals in the concentrate are tetrahedrite and galena.The treatment of tetrahedrite was rarely studied,and most of silver occurred in themineral too.The optimum operating parameters of oxygen pressure acid leaching were established by conditional tests.Under these parameters,the result of pilot scale test showed that the leaching percentages of copper and zinc were separately as high as 98.9 wt.% and 94.9 wt.%,while lead and silver were transformed into sulfate and sulfide precipitations,respectively.The copper and zinc in lixivium were reclaimed by extraction-electrowinning and purification-electrowinning,respectively,and the lead and silver in the residue were reclaimed separately by carbonate transformation-silicofluoric acid leaching and thiourea leaching.展开更多
Lime(CaO)and sodium humate(NaHA)were used as the combined depressant for arsenopyrite pre-treated by CuSO_(4) and butyl xanthate.Micro-flotation tests show that the combined depressant CaO and NaHA achieved the select...Lime(CaO)and sodium humate(NaHA)were used as the combined depressant for arsenopyrite pre-treated by CuSO_(4) and butyl xanthate.Micro-flotation tests show that the combined depressant CaO and NaHA achieved the selective depression of arsenopyrite.Closed-circuit lab-scale test results indicate that the synergistic effect of CaO+NaHA achieved a satisfactory flotation separation of sphalerite and arsenopyrite,for which the Zn grade and recovery of Zn concentrate were 51.21%and 92.21%,respectively.Contact angle measurements,adsorption amount measurements and X-ray photoelectron spectroscopy analysis indicate that the dissolved calcium species(mainly as Ca(2+))were adsorbed on the mineral surfaces,thereby promoting NaHA adsorption.Moreover,the surface of the arsenopyrite absorbed more amount of calcium species and NaHA than that of the sphalerite,thereby accounting for the strong hydrophilic surface of arsenopyrite.The adsorption of NaHA on arsenopyrite was mainly chemical adsorption through its carboxyl groups and Ca atoms,whereas that on sphalerite surface was relatively weak.展开更多
基金the 11th Five-Year Plan of National Scientific and Technological Program of China (No.2007 BAB22B01)
文摘The treatment of the Gacun complex Cu-Pb bulk concentrate with high Zn,Ag,etc.,by oxygen pressure acid leaching was studied.The pri-mary copper and leadminerals in the concentrate are tetrahedrite and galena.The treatment of tetrahedrite was rarely studied,and most of silver occurred in themineral too.The optimum operating parameters of oxygen pressure acid leaching were established by conditional tests.Under these parameters,the result of pilot scale test showed that the leaching percentages of copper and zinc were separately as high as 98.9 wt.% and 94.9 wt.%,while lead and silver were transformed into sulfate and sulfide precipitations,respectively.The copper and zinc in lixivium were reclaimed by extraction-electrowinning and purification-electrowinning,respectively,and the lead and silver in the residue were reclaimed separately by carbonate transformation-silicofluoric acid leaching and thiourea leaching.
基金the National Natural Science Foundation of China(Nos.51974364,51904339,52074355)the 13th Five-Year National Key R&D Program of China(No.2020YFC1909203)。
文摘Lime(CaO)and sodium humate(NaHA)were used as the combined depressant for arsenopyrite pre-treated by CuSO_(4) and butyl xanthate.Micro-flotation tests show that the combined depressant CaO and NaHA achieved the selective depression of arsenopyrite.Closed-circuit lab-scale test results indicate that the synergistic effect of CaO+NaHA achieved a satisfactory flotation separation of sphalerite and arsenopyrite,for which the Zn grade and recovery of Zn concentrate were 51.21%and 92.21%,respectively.Contact angle measurements,adsorption amount measurements and X-ray photoelectron spectroscopy analysis indicate that the dissolved calcium species(mainly as Ca(2+))were adsorbed on the mineral surfaces,thereby promoting NaHA adsorption.Moreover,the surface of the arsenopyrite absorbed more amount of calcium species and NaHA than that of the sphalerite,thereby accounting for the strong hydrophilic surface of arsenopyrite.The adsorption of NaHA on arsenopyrite was mainly chemical adsorption through its carboxyl groups and Ca atoms,whereas that on sphalerite surface was relatively weak.