Synthesis of Caged Bicyclic Phosphate Derivatives

Seven caged bicyclic phosphate compounds were synthesized by using 1-oxo-4-hydroxymethyl-2, 6, 7-trioxa-l-pho-sphabicyclo [ 2.2.2 ] octane （PEPA） as starting material. Within them were three PEPA derivatives containing single caged bicyclic phosphate structure（ 1a, 2a, 3a）, another three PEPA deviratives containing two caged bicyclic phosphate structures（1b, 2b, 3b） and one devirative（1c） containing three caged bicyclic phosphate structures. Structures of the products were characterized by FTIR, ^1H NMR, elemental analysis and TG analysis. The reaction conditions were also discussed. Thermal analysis showed they had high thermal stability and excellent char-forming ability. Besides, these compounds had pentaerythritol bone and flame retardant dements of phosphorus, bromine or nitrogen simultaneously in their molecules, endowed them with good fire retardancy, and made them can be used as intumescent flame retardant.

Synthesis and Structure of A Novel Caged Bicyclic Phosphate Flame Retardant

PI novel caged bicyclic phosphate flame retardant tri(1-oxo-2,6,7-trioxa-1-phosphabicyclo [2.2.2] octane-methyl) phosphate (Trimer) was synthesized from 1-oxo-4-hydroxymethyl-2,6,7-trioxa-1-phosphabicyclo [2.2.2] octane (PEPA) and phosphorus oxychloride in this paper. Its structure was characterized by elemental analysis. FTIR, H-1 NMR. P-31 NMR and X-ray diffraction analysis.

PROMOTION EFFECT OF MELAMINE ON FLAME RETARDANCY OF EPOXY RESINS CONTAINING CAGED BICYCLIC PHOSPHATE

Caged bicyclic phosphate （CBP） and its dimelamine salt （PDS） were synthesized and added to epoxy resins to obtain the flame retarded epoxy resin composites. The flammability of the composites was characterized by the limiting oxygen index （LOI） and cone calorimeter tests. The LOI values of flame retarded composites increase consistently with the increase of flame retardant amounts, and they are almost the same when the loading of CBP is the same as that of PDS, although the phosphorus content of PDS is much lower than that of CBP. The total heat release increases in the order of CBP30/ER 〈 PDS30/ER 〈 PDS15/ER 〈 CBPI5/ER, whereas that of specific extinction area is CBP15/ER 〉 CBP30/ER 〉 PDS30/ER ≌ PDS15/ER. PDS exhibits more effective inhibition of oxidation of combustible gases. In the tests of thermogravimetric analyses （TG） and Fourier transform infrared spectroscopy （FT-IR）, it is found that the degradation of the composites is influenced greatly by the addition of flame retardants. By scanning electron microscopy （SEM）, a thick and tight char-layer is observed for PDS30/ER, resulting from the interaction of nitrogen species with phosphorus species. Therefore, the combination of CBP with melamine in the flame retarded system can improve the flame retardancy greatly.

Study of Flame Retardation of Polycarbonate Modified by Polyhedral Oligomeric Silsesquioxane and Caged Bicyclic Phosphate

The flame-retarded polycarbonate（PC） has been made with octaphenyl polyhedral silsesquioxane（OPS） and/or caged bicyclic phosphate（Trimer）.Thermal gravimetric analysis（TGA）,Fourier-transform infrared（FTIR）,TGA-FTIR,limiting oxygen index（LOI）,and mechanical tests have been employed to characterize the modified PC.The additives of OPS and Trimer in PC have been proved to be effective flame-retardants because of the synergistic interaction between the elements of P and Si.The role of OPS and Trimer in PC degradation are different：OPS participates in the charring of PC,while Trimer makes PC degrade in advance.In addition,OPS and Trimer induced obvious differences in the mechanical properties of PC.