Studies of benzyl hydroxamic acid/calcium lignosulphonate addition order in the flotation separation of smithsonite from calcite

Flotation separation of smithsonite from calcite is difficult due to their similar surface properties.In the present study,a reagent scheme of depressant calcium lignosulphonate(CLS) and collector benzyl hydroxamic acid(BHA) was introduced in the flotation of smithsonite from calcite.Microflotation tests revealed that the efficient flotation of smithsonite from calcite could only be obtained with the addition order of BHA before CLS,which was opposite to the widely-used order that adding depressant prior to the collector.The zeta potential measurements indicated that BHA selectively adsorbed onto smithsonite surface,then not allowed the CLS adsorption onto the smithsonite surface rather than calcite surface because of the steric hindrance,thereby the smithsonite surface remained hydrophobic while calcite surface became more hydrophilic after the addition of CLS.As a result,the calcite flotation was completely depressed while the smithsonite flotation recovery was still in high value,leading to the optimal flotation separation performance.

Stabilization Mechanism of Calcium Lignosulphonate Used in Expansion Sensitive Soil

A series of tests were performed to investigate the macroscopic properties and the stabilization mechanism of calcium lignosulphonate modified expansive soil.Compared with natural soil,soil modified by 4%calcium lignosulphonate showed 56.5%increased 28 days unconfined compressive strength and 23.8%decreased free expansion rate.The X-ray diffraction analysis results indicate the existence of cation exchange and the reduction of montmorillonite interplanar spacing.The X-computed tomography results demonstrate that calcium lignosulphonate decreased the porosity and optimized the pore distribution.The calcium lignosulphonate also increased the stability of the suspension system according to the Zeta potential results.Moreover,the results of rheological tests show that the moderate amount of calcium lignosulphonate enhanced the yield stress and the plastic viscosity,proving the formation of a strong connection between soil particles.

Research of Lignin Modified Phenol Formaldehyde Resin Bonded Magnesia Carbon Bricks

In order to reduce the cost and to improve the low temperature bonding strength of phenol formaldehyde resin（ PF）,the lignin modified phenol formaldehyde resin（ LPF） was synthesized using calcium lignosulfonate as a partial replacement of phenol,and sodium hydroxide as catalyzer. Then the magnesia carbon bricks were prepared using the LPF as binder. Different process conditions of LPFs such as calcium lignosulfonate additions（ 10%,20%,30%,40% and 50%,in mass,the same hereinafter）,catalyzer additions（ extra added,1%,2%,3%,4% and 5%） and reaction times（ 1,1. 5,2,2. 5 and 3 h） were investigated. Effects of prepared LPFs on properties of magnesia carbon bricks（ baked at 200 ℃ for 24 h） were researched in order to modify the synthesizing conditions of LPFs. Cold physical properties and hot modulus of rupture of magnesia carbon bricks bonded by LPF and by traditional PF after baked at 200 ℃ for 24 h and fired at 1 200 ℃ for 3 h were compared,respectively. The results show that the optimal synthesizing conditions of LPF for preparing magnesia carbon bricks are 30% calcium lignosulfonate,1% catalyzer,and 2 h reaction time. The magnesia carbon bricks bonded by the optimal LPF achieve：（ 1） the bulk densities 2. 84 g · cm- 3and 2. 82g·cm- 3,apparent porosities 9. 6% and 14. 6%,moduli of rupture 17. 8 MPa and 6. 4 MPa,crushing strengths72. 3 MPa and 48. 7 MPa,after baked at 200 ℃ and1 200 ℃,respectively;（ 2） the hot modulus of rupture7. 3 MPa after fired at 1 400 ℃. The above properties are better than those of the magnesia carbon brick bonded by PF.