Trivalent samarium ion (Sm^(3+)) activated calcium molybdate (CaMoO_4) phosphor was prepared by solid-state reaction in air. The XRD pattern of the powder CaMoO_4∶Sm shows that the CaMoO_4∶Sm single phase is develop...Trivalent samarium ion (Sm^(3+)) activated calcium molybdate (CaMoO_4) phosphor was prepared by solid-state reaction in air. The XRD pattern of the powder CaMoO_4∶Sm shows that the CaMoO_4∶Sm single phase is developed fully through our preparation procedure. The excitation spectrum of CaMoO_4∶Sm is composed of a broad absorption of host and some sharp lines of the f-f transition absorption of Sm^(3+). Illustrated in photoluminescence spectrum, CaMoO_4 doped with Sm^(3+) displays orange red emission that is ascribed to the inner 4f^5 electron transitions ~6H_(7/2)(orange)and ~6H_(9/2)(red)of Sm^(3+). Different from the sites of Sm^(3+) in CdWO_4, the Sm^(3+) ions substitute for the Ca^(2+) and form only one type emission center in the CaMoO_4 crystal lattice.展开更多
This article investigated molybdenum recovery from oxygen pressure water leaching residue of Ni-Mo ore using alkaline leaching, followed by chemical treatment of leach liquor. Parameters affecting Mo leaching rate, su...This article investigated molybdenum recovery from oxygen pressure water leaching residue of Ni-Mo ore using alkaline leaching, followed by chemical treatment of leach liquor. Parameters affecting Mo leaching rate, such as sodium hydroxide concentration, reaction time, a liquid- to-solid ratio, and temperature for the preliminary alkaline leaching were experimentally determined. The results showed that more than 88 % of molybdenum was leached under the optimum conditions （2.5 ml.g-1 NaOH, 80 ℃, a liquid to solid ratio 3 ml.g-1, and reaction time 3 h）. After the purification of leach liquor, a CaMoO4 product of 99.2 % purity could be obtained by CaCla precipitation method. The whole Mo recovery reached about 82.7 %.展开更多
文摘Trivalent samarium ion (Sm^(3+)) activated calcium molybdate (CaMoO_4) phosphor was prepared by solid-state reaction in air. The XRD pattern of the powder CaMoO_4∶Sm shows that the CaMoO_4∶Sm single phase is developed fully through our preparation procedure. The excitation spectrum of CaMoO_4∶Sm is composed of a broad absorption of host and some sharp lines of the f-f transition absorption of Sm^(3+). Illustrated in photoluminescence spectrum, CaMoO_4 doped with Sm^(3+) displays orange red emission that is ascribed to the inner 4f^5 electron transitions ~6H_(7/2)(orange)and ~6H_(9/2)(red)of Sm^(3+). Different from the sites of Sm^(3+) in CdWO_4, the Sm^(3+) ions substitute for the Ca^(2+) and form only one type emission center in the CaMoO_4 crystal lattice.
基金supported by the National High Technology Research and Development Program of China(No.2009AA06Z106)Yunnan Provincial Science and Technology Department of China(No.2011GA004)
文摘This article investigated molybdenum recovery from oxygen pressure water leaching residue of Ni-Mo ore using alkaline leaching, followed by chemical treatment of leach liquor. Parameters affecting Mo leaching rate, such as sodium hydroxide concentration, reaction time, a liquid- to-solid ratio, and temperature for the preliminary alkaline leaching were experimentally determined. The results showed that more than 88 % of molybdenum was leached under the optimum conditions （2.5 ml.g-1 NaOH, 80 ℃, a liquid to solid ratio 3 ml.g-1, and reaction time 3 h）. After the purification of leach liquor, a CaMoO4 product of 99.2 % purity could be obtained by CaCla precipitation method. The whole Mo recovery reached about 82.7 %.