Influences of lanthanum stearate （LaSt3） and calcium stearate/zinc stearate （Ca/Zn） stabilizers on stabilization efficiency of dibutyltin dilaurate （DBTDL） to polyvinyl chloride （PVC） in air were investigated....Influences of lanthanum stearate （LaSt3） and calcium stearate/zinc stearate （Ca/Zn） stabilizers on stabilization efficiency of dibutyltin dilaurate （DBTDL） to polyvinyl chloride （PVC） in air were investigated. The results revealed that the stabilization effect of DBTDL could be achieved by the La/Sn stabilizers with a ratio of 8/2. Addition of DBTDL could enhance thermal property and reduce dynamic storage modulus （G＇） at 180℃ for PVC containing LaSt3 or Ca/Zn stabilizers. On the other hand, incorporation of LaSh did not influence the stabilization efficiency of DBTDL markedly; while addition of Ca/Zn stabilizers could significantly decrease thermal property for the DBTDL stabilized PVC. Furthermore, the effects of LaSt3 and Ca/Zn stabilizers on the stabilization efficiency of DBTDL were explained in the framework of ionization potential.展开更多
The synergistic stabilization effect of different metal lanolin fatty acids as natural-based thermal stabilizers for poly（vinyl chloride） （PVC） including calcium lanolin fatty acid （Calan2）,zinc lanolin fatty ac...The synergistic stabilization effect of different metal lanolin fatty acids as natural-based thermal stabilizers for poly（vinyl chloride） （PVC） including calcium lanolin fatty acid （Calan2）,zinc lanolin fatty acid （Znlan2） and lanthanum lanolin fatty acid （Lalan3） were studied through Congo red testing,color measurements,FTIR analyses and thermal behavior in this paper. The results showed that Lalan3/Calan2/Znlan2 stabilizers exhibited more excellent thermal stabilization efficiency to PVC than Calan2/Znlan2 thermal stabilizers,and the optimal mass ratio of Lalan3/Calan2/Znlan2 was 8：9：3. At last,the effect of degradation mechanism on PVC and synergistic stabilization was also investigated by FTIR analyses and thermal behavior.展开更多
基金supported by Key Projects in the National Science & Technology Pillar Program(No. 2007BAE10B04)
文摘Influences of lanthanum stearate （LaSt3） and calcium stearate/zinc stearate （Ca/Zn） stabilizers on stabilization efficiency of dibutyltin dilaurate （DBTDL） to polyvinyl chloride （PVC） in air were investigated. The results revealed that the stabilization effect of DBTDL could be achieved by the La/Sn stabilizers with a ratio of 8/2. Addition of DBTDL could enhance thermal property and reduce dynamic storage modulus （G＇） at 180℃ for PVC containing LaSt3 or Ca/Zn stabilizers. On the other hand, incorporation of LaSh did not influence the stabilization efficiency of DBTDL markedly; while addition of Ca/Zn stabilizers could significantly decrease thermal property for the DBTDL stabilized PVC. Furthermore, the effects of LaSt3 and Ca/Zn stabilizers on the stabilization efficiency of DBTDL were explained in the framework of ionization potential.
基金Project supported by the Natural Science Foundation of Fujian Province (2007HZ0001-2)
文摘The synergistic stabilization effect of different metal lanolin fatty acids as natural-based thermal stabilizers for poly（vinyl chloride） （PVC） including calcium lanolin fatty acid （Calan2）,zinc lanolin fatty acid （Znlan2） and lanthanum lanolin fatty acid （Lalan3） were studied through Congo red testing,color measurements,FTIR analyses and thermal behavior in this paper. The results showed that Lalan3/Calan2/Znlan2 stabilizers exhibited more excellent thermal stabilization efficiency to PVC than Calan2/Znlan2 thermal stabilizers,and the optimal mass ratio of Lalan3/Calan2/Znlan2 was 8：9：3. At last,the effect of degradation mechanism on PVC and synergistic stabilization was also investigated by FTIR analyses and thermal behavior.