The matching performance among the visible and near infrared coating.the low infrared emitting coating and the microwave absorbing coating was investigated.Experimental results show that the resulting malerial is char...The matching performance among the visible and near infrared coating.the low infrared emitting coating and the microwave absorbing coating was investigated.Experimental results show that the resulting malerial is characteristic of wideband effect ranging from the visible,near infrared and 3-5μm,8-14μm infrared protion of the spectrum,as well as the radar region from 8 to 18GHz when these three materials form αlayerstructure material system.The microwave absorbing ability of material is hardly changed.The resonance peak moves towards lower frequency as the thickness of the visible,near infrared coating and the low infrared emitting coating increases.This problem can be resolved by controlling the thickness of the matrial.On the other hand, the infrared emissivity εof the material system increases as the thickness of the visible,near infrared coating increases.This can be resolved by increasing infrared transparency of the visible and near infrared topcoating or controlling its thickness.The experimental resulting material system has spectral reflection characteristics in visible and near infrared regions that are similar to those of the natural background.展开更多
文摘The matching performance among the visible and near infrared coating.the low infrared emitting coating and the microwave absorbing coating was investigated.Experimental results show that the resulting malerial is characteristic of wideband effect ranging from the visible,near infrared and 3-5μm,8-14μm infrared protion of the spectrum,as well as the radar region from 8 to 18GHz when these three materials form αlayerstructure material system.The microwave absorbing ability of material is hardly changed.The resonance peak moves towards lower frequency as the thickness of the visible,near infrared coating and the low infrared emitting coating increases.This problem can be resolved by controlling the thickness of the matrial.On the other hand, the infrared emissivity εof the material system increases as the thickness of the visible,near infrared coating increases.This can be resolved by increasing infrared transparency of the visible and near infrared topcoating or controlling its thickness.The experimental resulting material system has spectral reflection characteristics in visible and near infrared regions that are similar to those of the natural background.