The effect of solution annealing on the microstructure and mechanical properties of a Ni-Cr-W-Fe alloy developed for advanced 700？C ultra-supercritical power plants was investigated. Test samples in this study were s...The effect of solution annealing on the microstructure and mechanical properties of a Ni-Cr-W-Fe alloy developed for advanced 700？C ultra-supercritical power plants was investigated. Test samples in this study were subjected to different solution treatments and the same aging treatment（at 760？C for 1 h）.When solution annealing temperature was elevated from 1020？C to 1150？C, the stress-rupture life at750？C/320 MPa was increased from 60 h to 300 h, the stress-rupture elongation was enhanced from12% to 17%, and the elongation of the tensile at 750？C was improved from 11% to 24%. All tensile and stress-rupture samples displayed an intergranular dimple mixed fracture. Intergranular micro-cracks had a great relationship with the morphology of grain boundary carbides. Most carbides retained the morphology of globular shape and continuous thin plate. After tensile and stress-rupture tests, a few carbides were converted into lamellar. The results showed that intergranular micro-cracks were easier to form at continuous thin plate carbides than at globular shape carbides. Lamellar carbides hardly caused the nucleation of micro-cracks. Besides, grain boundaries sliding and elements diffusion during stressrupture tests led to the formation of precipitate free zones, which accelerated the extension of microcracks and influenced the stress-rupture life.展开更多
文摘The effect of solution annealing on the microstructure and mechanical properties of a Ni-Cr-W-Fe alloy developed for advanced 700？C ultra-supercritical power plants was investigated. Test samples in this study were subjected to different solution treatments and the same aging treatment（at 760？C for 1 h）.When solution annealing temperature was elevated from 1020？C to 1150？C, the stress-rupture life at750？C/320 MPa was increased from 60 h to 300 h, the stress-rupture elongation was enhanced from12% to 17%, and the elongation of the tensile at 750？C was improved from 11% to 24%. All tensile and stress-rupture samples displayed an intergranular dimple mixed fracture. Intergranular micro-cracks had a great relationship with the morphology of grain boundary carbides. Most carbides retained the morphology of globular shape and continuous thin plate. After tensile and stress-rupture tests, a few carbides were converted into lamellar. The results showed that intergranular micro-cracks were easier to form at continuous thin plate carbides than at globular shape carbides. Lamellar carbides hardly caused the nucleation of micro-cracks. Besides, grain boundaries sliding and elements diffusion during stressrupture tests led to the formation of precipitate free zones, which accelerated the extension of microcracks and influenced the stress-rupture life.