Analysis on the Bonding Failure Mechanism of High Modulus Carbon Fiber Composites

In order to explore the bonding failure mechanism of high modulus carbon fiber composite materials,the tensile experiment and finite element numerical simulation for single-lap and bevel-lap joints of unidirectional laminates are carried out,and the stress distributions,the failure modes,and the damage contours are analyzed. The analysis shows that the main reason for the failure of the single-lap joint is that the stress concentration of the ply adjacent to the adhesive layer is serious owing to the modulus difference,and the stress cannot be effectively transmitted along the thickness direction of the laminate. When the tensile stress of the ply exceeds its ultimate strength in the loading process,the surface fiber will fail. Compared with the single-lap joint,the bevel-lap joint optimizes the stress transfer path along the thickness direction,allows each layer of the laminate to share the load,avoids the stress concentration of the surface layer,and improves the bearing capacity of the bevel-lap joint. The improved bearing capacity of the bevellap joint is twice as much as that of the single-lap joint. The research in this paper provides a new idea for the subsequent study of mechanical properties of adhesively bonded composite materials.

The impact of the new composite material technology on the performance of the tennis rackets

With the continues improving of people＇s living standards, more and more people work out in all kinds of sports fields beyond the busy work. On the other hand, the development of the modem competitive sports also requires that the sports experts should not only strive for the scientific training, but should also pay much attention on the improvement and development of the sports equipment at the same time, which makes the sports equipment market have achieved unprecedented prosperity. This paper introduces the application of the fiber reinforced composite materials in the field of sports equipment, which is described mainly from the advantages of the fiber reinforced composite materials used in sports equipment areas, and from the aspects of the principles of material selection, the product varieties, the application examples and the status.

Research on the Crack Detection of Conductive Components Using Pulsed Eddy Current Thermography

Crack of conductive component is one of the biggest threats to daily production. In order to detect the crack on conductive component,the pulsed eddy current thermography models were built according to different materials with the cracks based on finite element method(FEM) simulation. The influence of the induction heating temperature distribution with the different defect depths were simulated for the carbon fiber reinforced plastic(CFRP) materials and general metal materials. The grey value of image sequence was extracted to analyze its relationship with the depth of crack. Simulative and experimental results show that in the carbon fiber reinforced composite materials,the bigger depth of the crack is,the larger temperature rise of the crack during the heating phase is; and the bigger depth of the crack is,the faster the cooling rate of the crack during the cooling phase is. In general metal materials,the smaller depth of the crack is,the lager temperature rise of the crack during the heating phase is; and the smaller depth of the crack is,the faster the cooling rate of crack during the cooling phase is.