Behaviors of Lanthanum and Cerium on Grain Boundaries in Carbon Manganese Clean Steel

The behaviors of La and Ce on gram boundaries in carbon manganese clean steel were investigated by high-reso- lution transmission elecetron microscope （HRTEM）, scanning elecetron microscopy（SEM ）, energy dispersive spectrometer （EDS） and X-ray diffraction（XRD） analysis. The existing forms of rare earths （RE） in clean steel were as follows： dissolved in sohd solution, forming inclusion or second phase containing RE （RE-Fe-P, La-P, Fe-La eutectic and Fe-Ce phase）. The dissolved La or Ce segregated at grain boundaries. The segregation of both S and P at gram boundaries was reduced with suitable RE content. The impact toughness of the steel was improved obviously. La and Ce had effecets on purifying molten steel and modifying inclusions in clean steel, whereas with excessive La or Ce, La-Fe-P, La-P and Fe-La eutecetic phase or Ce-Fe-P and Fe-Ce intermetallic compound would form along grain boundaries, causing the impact energy to decrease significantly.

Effects of cooling rate and Al on MnS formation in medium-carbon non-quenched and tempered steels

The effect of Al on the morphology of MnS in medium-carbon non-quenched and tempered steel was investigated at three different cooling rates of 0.24, 0.43, and 200°C·s^-1. The formation mechanisms of three types of MnS were elucidated based on phase diagram information combined with crystal growth models. The morphology of MnS is governed by the precipitation mode and the growth conditions. A monotectic reaction and subsequent fast solidification lead to globular Type I MnS. Type II MnS inclusions with different morphological characteristics form as a result of a eutectic reaction followed by the growth in the Fe matrix. Type III MnS presents a divorced eutectic morphology. At the cooling rate of 0.24°C·s^-1, the precipitation of dispersed Type III MnS is significantly enhanced by the addition of 0.044wt% acid-soluble Al（Als）, while Type II MnS clusters prefer to form in steels with either 0.034wt% or 0.052wt% Als. At the relatively higher cooling rates of 200°C·s^-1 and 0.43°C·s^-1, the formation of Type I and Type II MnS inclusions is promoted, and the influence of Al is negligible. The results of this work are expected to be employed in practice to improve the mechanical properties of non-quenched and tempered steels.

Evolution of Al2O3 inclusions by cerium treatment in low carbon high manganese steel

The influence of cerium（Ce）treatment on the morphologies,size and distributions of Al_2O_3 inclusions in low carbon high manganese steel was investigated by OM,SEM-EDS and theoretical calculation.The results showed that Ce can modify the morphologies and types of Al_2O_3 inclusions.After Ce treatment,the irregular Al_2O_3 inclusions were replaced by smaller and dispersive spherical cerium oxysulfides.The effects of treatment time and Ce content on the evolution of Al_2O_3 inclusions were examined.It indicated that Al_2O_3 inclusions were wrapped by rare earth inclusions to form a ring like shape Ce-enriched band around the inclusions.Model was established to elucidate the evolution mechanism of Al_2O_3 inclusions.Evolution kinetics of inclusions was discussed qualitatively to analyze the velocity controlled step.It was found that diffusion of Ce^（3＋）and Al^（3＋）in solid inclusion core and the formed intermediate layer would be the limited step during the evolution process.