Oxide and Sulfide Dispersive Precipitation and Effects on Microstructure and Properties of Low Carbon Steels

Electron microscopic investigation on low carbon steel strips produced by the CSP process has been carried out. Large number of oxide dispersive precipitates have been observed in the ferrite matrix of the steel strips. Dimension of them is about 10~20 nm. Electron diffraction study showed that the structure of these precipitates consists with cubic system spinel structure. Their lattice parameter is about 0.83 nm. The results implied that they should be complex oxides of Fe, Al et al. Small sulfide particles with 100-300 nm in size have also been observed. Remarkable strengthening and grain refinement effects can be obtained by the precipitations. The oxygen and sulfur in steels could play beneficial role under certain conditions.

Bainite Transformation Under Continuous Cooling of Nb-Microalloyed Low Carbon Steel

Utilizing Gleeble-1500 thermomechanical simulator, the influences of hot deformation parameters on continuous cooling bainite transformation in Nb-microalloyed low carbon steel were investigated. The results indicate that bainite starting temperature decreases with raising cooling rate and increases with increasing deformation temperature. Deformation has an accelerative effect on the bainite transformation when the specimens are deformed at 950 ℃. When the deformation temperature increases, the effect of deformation on bainite starting temperature is weakened. The amount of bainite is influenced by strain, cooling rate, and deformation temperature. When the specimens are deformed below 900 ℃, equiaxed ferrites are promoted and the bainite transformation is suppressed.

Effect of electromagnetic stirring in mold on the macroscopic quality of high carbon steel billet

An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.

Bonding characteristics of the Al_2O_3-metal composite coating fabricated onto carbon steel by combustion synthesis

The fabrication of an alumina-metal composite coating onto a carbon steel substrate by using a self-propagating high-temperature synthesis technique was demonstrated. The effects of the type and thickness of the pre-coated layer on the binding structure and surface qual- ity of the coating were systematically investigated. The macrostructure, phase composition, and bonding interface between the coating and the substrate were investigated by scanning electronic microscopy （SEM）, X-ray diffraction （XRD）, and energy-dispersive X-ray spectrometry （EDS）. The diffraction patterns indicated that the coating essentially consisted of α-Al2O3, Fe（Cr）, and FeO-Al2O3. With an increase in the thickness of the pre-coated working layer, the coating became more smooth and compact. The transition layer played an important role in enhancing the binding between the coating and the substmte. When the pre-coated working layer was 10 mm and the pre-coated transition layer was 1 ram, a compact structure and metallurgical bonding with the substrate were obtained. Thermal shock test results indicated that the ceramic coating exhibited good thermal shock resistance when the sample was rapidly quenched from 800℃ to room temperature by plunging into water.

Decarburization rate of RH refining for ultra low carbon steel

The decarburization behaviors of ultra low carbon steel in a 210-t RH vacuum degasser were investigated under practical operat- ing conditions. According to the apparent decarburization rate constant （Kc） calculated by the carbon content in the samples taken from the hot melt in a ladle at an interval of 1-2 min, it is observed that the total decarburization reaction period in RH can be divided into the quick decarburization period and the stagnant decarburization period, which is quite different from the traditional one with three stages. In this study, the average apparent decarburization rate constant during the quick decarburization period is 0.306 min^-1, and that of the stagnant period is 0.072 min^-1. Increasing the initial carbon content and enhancing the exhausting capacity can increase the apparent decarburization rate constant in the quick decarburization period. The decarburization reaction comes into the stagnant decarburization period when the carbon content in molten steel is less than 14× 10^-6 after 10 min of decarburization.

Effects of Deformation on Bainite Transformation During Continuous Cooling of Low Carbon Steels

Hot deformation experiments were carried out on Gleeble 1500 thermo-mechanical simulator. The bainite transformation after deformation was investigated by optical microstructure analysis. The results indicated that the deformation accelerated the bainite transformation when the deformation was carried out at high temperature and no or little ferrite was precipitated before bainite transformation; when the deformation was carried out at low temperature, the deformation hindered the bainite transformation because a lot of ferrite precipitated before bainite transformation.

New Spheroidizing Technique of Ultra-High Carbon Steel With Aluminum Addition

A new spheroidizing process of ultra-high carbon steel （UHCS） containing C 1.55%, Cr 1.45%, and Al 1.5% in mass percent has been proposed. The effect of processing parameters on the microstructure was analyzed. The UHCS produced by this new process has a microstructure with recrystallized ferrite matrix and fine and uniform carbide particles. After this spheroidizing, the UHCS exhibits good mechanical properties at ambient temperature, for example σb= 1 100 MPa, σs =915 MPa, δ=8% and high ratio of σs/σb.

Aspects of microstructure in low carbon steels produced by the CSP process

The solidification structure, microstructure evolution during rolling andprecipitates with nanometers in dimension of the low carbon steels produced by CSP process with thinslabs have been studied in recent years. Important differences in microstructure and mechanicalproperties between the CSP products and the conventional one were observed. These differences mayarise from the much rapider solidification rate and cooling rate after casting of the thin slabs.Some aspects of the microstructure for the low carbon steels of the CSP thin slabs are summarizedand compared with the conventional one.

Amine-based solvent for CO_2 absorption and its impact on carbon steel corrosion: A perspective review

Carbon dioxide(CO2)is one of the commonly emitted gaseous by-products in industrial processes.While CO2 gas is the main cause to greenhouse effect,various CO2 capture technologies have been proposed and implemented to sequester the CO2 before the waste gases being released into the atmosphere.One of the mature technologies for CO2 absorption is by using amine-based solvents.In this regard,different single amine solvents or blended amine solvents have been proven for their capability to remove CO2.However,the dissolution and reaction of CO2 gas with the amine solvents turn the solution corrosive.Such phenomenon is undesired as it posts corrosion problem to the absorption column,which normally built of carbon steel material.Henceforth,understanding the behaviour of different amine-based solvents in absorbing CO2 and its subsequent impact on carbon steel corrosion is very significant.In this review article,we will outline some of the more commonly used solvents and their respective advantages and disadvantages,motivating further investigation into the corrosion tendency.Meanwhile,existing gaps in this research area are discussed for future investigation.

DEFORMATION ENHANCED FERRITE TRANSFORMATION IN PLAIN LOW CARBON STEEL

The microstructure evolution during deformation enhanced transformation of undercooled austenite of a plain low carbon steel has been investigated by means of hot compression simulation experiment under various conditions of strain rate, deformation temperature and strain. The effect of austenite grain size on the strain enhanced ferrite transformation has been studied. The ferrite dynamic recrystallization involved in successive hot deformation has been explored.

INFLUENCE OF HOT DEFORMATION ON CONTINUOUSCOOLING BAINITIC TRANSFORMATION IN A LOWCARBON STEEL

The influence of hot deformation conditions on continuous cooling bainitic transformation has been investigated for a low carbon microalloyed steel. The CCT diagrams show that deformation in unrecrpstallized austcnite ation can accelerate transformation process. Bainitic transformation in intermediate transformation temperature region is prominent, and the proeutectoid polygonal ferrite transformation at evelated high temperature is suppressed. According to optical and TEM analyses, low carbon bainitic ferrite is characterized by granular and lathlike ferrite, based on the cooling rate and deformation conditions. For nondeformation, groaps of coarse parallel ferrite lath form from the prior austenite grain boundaries with the same crystallographic orientation. For heavy deformaton, cell structure within the austenite grains due to the high dislocation density formed, which provides more nucleation sites for bainite ferrite. So deformation can discontinue the growth of ferrite laths and decrease the length of ferrite laths.

Austenite Recrystallization and Controlled Rolling of Low Carbon Steels

The dynamic recrystallization and static recrystallization in a low carbon steel were investigated through single-pass and double-pass experiments. The results indicate that as the deformation temperature increases and the strain rate decreases, the shape of the stress-strain curve is changed from dynamic recovery shape to dynamic recrystallization shape. The austenite could not recrystallize within a few seconds after deformation at temperature below 900 ℃. According to the change in microstructure during deformation, the controlled rolling of low carbon steel can be divided into four stages： dynamic recrystallization, dynamic recovery, strain-induced ferrite transformation, and rolling in two-phase region. According to the microstructure after deformation, the controlled rolling of low carbon steel can be divided into five regions： non-recrystallized austenite, partly-recrystallized austenite, fully-recrystallized austenite, austenite to ferrite transformation, and dual phase.

Prediction of the Charpy V-notch impact energy of low carbon steel using a shallow neural network and deep learning

The impact energy prediction model of low carbon steel was investigated based on industrial data. A three-layer neural network, extreme learning machine, and deep neural network were compared with different activation functions, structure parameters, and training functions. Bayesian optimization was used to determine the optimal hyper-parameters of the deep neural network. The model with the best performance was applied to investigate the importance of process parameter variables on the impact energy of low carbon steel. The results show that the deep neural network obtains better prediction results than those of a shallow neural network because of the multiple hidden layers improving the learning ability of the model. Among the models, the Bayesian optimization deep neural network achieves the highest correlation coefficient of 0.9536, the lowest mean absolute relative error of 0.0843, and the lowest root mean square error of 17.34 J for predicting the impact energy of low carbon steel. Among the variables, the main factors affecting the impact energy of low carbon steel with a final thickness of7.5 mm are the thickness of the original slab, the thickness of intermediate slab, and the rough rolling exit temperature from the specific hot rolling production line.

Simple Predicting Method for Fatigue Crack Growth Rate Based on Tensile Strength of Carbon Steel

Three types of fatigue tests for an annealed carbon steel containing carbon of 0.42%were carried out on smooth specimens and specimens with a small blind hole in order to investigate the fatigue crack growth law.A simple predicting method for crack growth rates has been proposed involving strengthσband the relation between cyclic stress and strain.The validity of proposed method has been confirmed by experiments on several carbon steels with different loadings.

Surface Ferrite Grain Refinement and Mechanical Properties of Low Carbon Steel Plates

Considering the specialities of the steel plate production, the TMCP study has been carried out with Gleeble 2000 tester to explore the possibility of fine grained ferrite in the low carbon steel plates with the chemical composition of C 0.13--0.18, Si 0.12-0.18, Mn 0.50-0. 65, P 0. 010-0. 025, and S 0. 005-0. 028. The plates with thickness of 8. 7 mm in which the ferrite grain size is smaller than 8μm have been produced by special de- formation process in the laboratory. Furthermore, the trial production of special plain carbon steel plates of 16-25 mm in thickness and 2 000- 2 800 mm in width with fine grained ferrite has been successfully carried out in the Shougang Steel Plate Rolling Plant. The ferrite grain size is 5.5-7μm in the surface layers and 9.5-15μm in the central layer respectively. The yield strength is 320- 360 MPa, tensile strength is 440-520 MPa and the elongation is 25%- 34 %. It is very important for the rolling plants to improve the low carbon steel plates＇ mechanical properties. The results show that the ferrite grains in the surface layer can be refined effectively by the appropriate rolling process, and the strength can be also increased.

A method to study interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel

A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the content of arsenic has great effect on grain growth and phase transformation at high temperature. When the arsenic content is no more than lwt%, there is no obvious grain growth and no obvious ferrite transitional region formed at the diffusion interface. However, when the arsenic content is no less than 5wt%, the grain grows very rapidly. In addition, the arsenic-enriched ferrite transitional layer forms at the diffusion interface in the hot-rolling process, which results from a slower diffusion rate of arsenic atoms than that of carbon in ferrite.

Effects of heat treatment on the corrosion resistance of carbon steel coated with LaMgAl_(11)O_(19) thermal barrier coatings

LaMgAl11O19thermal barrier coatings（TBCs） were applied to carbon steels with a NiCoCrAlY bond coat by plasma spraying. The effects of heat treatment on the corrosion resistance of carbon steel coated with LaMgAl11O19TBCs were investigated in 3.5wt% Na Cl solution using polarization curves, electrochemical impedance spectroscopy（EIS）, scanning electron microscopy（SEM）, and X-ray diffraction（XRD）. The results show that a large number of cracks are found in the LaMgAl11O19TBCs after the samples are heat-treated, including some through-thickness cracks. The corrosion forms of the as-sprayed and heat-treated TBCs are uniform corrosion and pitting corrosion, respectively. The as-sprayed TBCs exhibit three EIS time constants after being immersed for less than 7 d, and then a new time constant appears because of steel substrate corrosion. When the immersion time is increased to 56 d, a Warburg impedance（W） component appears in the EIS data. The EIS data for the heat-treated TBCs exhibit only two time constants after the samples are immersed for less than 14 d, and a new time constant appears when the immersion time is increased further. The heat treatment reduces the corrosion resistance of carbon steel coated with LaMgAl11O19TBCs. The corrosion products are primarily γ-Fe OOH and Fe3O4.

Preparation and Properties of Anti-oxidation Inorganic Nano-coating for Low Carbon Steel at an Elevated Temperature

A new kind of anti-oxidation inorganic nano-coating for the common low carbon steel was prepared. It included magnesite mineral, metallurgic dust and silicate adhesive as the main raw materials. The nano-coating could be sprayed directly onto the low carbon steel slab even though with hot surface as far as under 1000 ℃ . And at the same time, a compact thin nano-film was formed, and the film would inhibit the oxygen into the interface of the steel body and decrease the loss of weight because of oxidation. The loss was decreased by about 60% or more. The properties and mechanism of oxidation resistance of the coating were discussed through XRD, TG-DTA and SEM. The experimental results show that many reactions would happen among the companents of the coating and then many microspheres with the size of 80- 100nm generated in the system. By using the heat of the steel body, the silicate adhesive would interact with the microspheres, and the other components of the coating would be soft and sintered so that when the coating was sprayed onto the suface of the steel slab , the intact and compact film could be formed and adhesive with the steel body. Besides the special properties of anti- oxidation, the coating could prevent the volatilization of microelement in the steel such as silicate and carbon at a high temperature. So it can improve the quality and output of steel with this new kind of nano-coating.