In this study,the effects of WC nano-particles amount and surface roughness on corrosion behavior of magnesium metal matrix nanocomposites in 3.5%NaCl solution are examined with the help of electrochemical test.Varyin...In this study,the effects of WC nano-particles amount and surface roughness on corrosion behavior of magnesium metal matrix nanocomposites in 3.5%NaCl solution are examined with the help of electrochemical test.Varying wt%of WC nano-particles(0.5,1,1.5 and 2)are used to fabricate metal matrix nano-composites through ultrasonic vibration assisted stir casting method.Basic characterizations of fabricated composites are performed by using scanning electron microscopy(SEM)and energy dispersive x-ray analysis(EDAX).SEM images show that nano-particles are well distributed throughout the magnesium matrix while EDAX results confirm the presence of WC particles in nano-composites.Micro-hardness result shows increasing trend with increasing weight percentage of WC.Mg nano-composite containing 0.5 wt%WC nano-particles is found to be the most corrosion resistive one followed by base alloy,Mg-2 wt%WC,Mg-1.5 wt%WC and Mg-1 wt%WC.Additionally,corrosion behavior of Mg-2WC with different surface quality is examined and it is observed that sample with lowest surface roughness shows better corrosion resistance.In the end,corrosion mechanisms are assessed with the help of SEM and EDAX study of corroded surfaces.展开更多
As an ionic conductive functional layer of intermediate temperature solid oxide fuel cells(ITSOFC), samarium-doped ceria(SDC)–Li Na SO4nano-composites were synthesized by a sol–gel method and their properties were i...As an ionic conductive functional layer of intermediate temperature solid oxide fuel cells(ITSOFC), samarium-doped ceria(SDC)–Li Na SO4nano-composites were synthesized by a sol–gel method and their properties were investigated. It was found that the content of Li Na SO4 strongly affected the crystal phase, defect concentration, and conductivity of the composites. When the content of Li Na SO4 was 20 wt%, the highest conductivity of the composite was found to be, respectively, 0.22, 0.26, and 0.35 S cm-1at temperatures of 550, 600, and 700 °C, which are much higher than those of SDC. The peak power density of the single cell using this composite as an interlayer was improved to, respectively, 0.23, 0.39, and 0.88 W cm-2at 500, 600, and 700 °C comparing with that of the SDC-based cell. Further, the SDC–Li Na SO4(20 wt%)-based cell also displayed better thermal stability according to the performance measurements at 560 °C for 50 h. These results reveal that SDC–Li Na SO4 composite may be a potential good candidate as interlayer for ITSOFC due to its high ionic conductivity and thermal stability.展开更多
This study investigates the removal of Congo Red dye from aqueous solution using functionalized generation 3.0 and 5.0 polyamidoamine dendrimer-silica gel composite (G-3PS, G-5PS). Fourier Transform-Infra Red spectros...This study investigates the removal of Congo Red dye from aqueous solution using functionalized generation 3.0 and 5.0 polyamidoamine dendrimer-silica gel composite (G-3PS, G-5PS). Fourier Transform-Infra Red spectroscopy, Brunauer Emmett and Teller, Thermo Gravimetric Analysis, pH at point of zero charge, and scanning electron microscopy measurements have been applied to characterize the synthetic nanohybrid composite, these techniques revealed the successful functionalization of both dendrimer molecules and subsequent immobilization onto silica gel. The implications of varying adsorption parameters such as contact time, initial concentration of adsorbate, temperature and pH on both composites were studied. Experimental data obtained from batch adsorption processes were fitted into two equilibrium isotherms (Langmuir and Freundlich) and 3 kinetic models (Pseudo-First-Order, Pseudo-Second-Order, Intra Particle Diffusion). Adsorption mechanism was mainly governed by film diffusion due to electrostatic interactions between the functionalized dendrimer surface and Congo Red molecules. Thermodynamic parameters illustrate that the adsorption is endothermic and spontaneous. Findings suggest the Nanocomposites (G-3PS and G-5PS) are good adsorbents for the removal of Congo Red dye from aqueous solutions.展开更多
Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on common carbon steel surface by pulse electrodeposition of nickel, tungsten, phosphorus, rare earth (nano-CeO2) and silicon carbide (nano-SiO2) particles. T...Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on common carbon steel surface by pulse electrodeposition of nickel, tungsten, phosphorus, rare earth (nano-CeO2) and silicon carbide (nano-SiO2) particles. The effects of nano-CeO2 concentrations in electrolyte on microstructures and properties of nano-composite coatings were studied. The samples were characterized with chemical compositions, elements distributions, microhardness and microstructures. The results indicated that when nano-CeO2 concentration was controlled at 10 g/L, the nano-composite coatings possessed higher microhardness and compact microstmctures with clear outline of spherical matrix metal crystallites, fine crystallite sizes and uniform distribution of elements W, P, Ce and Si within the Ni-W-P matrix metal. Increasing the nano-CeO2 particles concentrations from 4 to 10 g/L led to refinement in grain structure and improvement of microstructures, while when increased to 14 g/L, the crystallite sizes began to increase again and there were a lot of small boss with nodulation shape appearing on the nano-composite coatings surface.展开更多
The radical polymerization of maleic anhydride(MA),styrene(ST)with the vinyl groups introduced onto the surface of the nano-sized silica via solution polymerization method was developed.The methacryloxypropyl nano...The radical polymerization of maleic anhydride(MA),styrene(ST)with the vinyl groups introduced onto the surface of the nano-sized silica via solution polymerization method was developed.The methacryloxypropyl nano-sized silica(MPNS)was used as macromonomer and polymerized with maleic anhydride and styrene by initiating with BPO in toluene.The structure and properties of MPNS/SMA nano-composite were characterized by FT-IR spectra and TEM.Meanwhile,it was applied as tanning agent compared with the traditional styrene-maleic anhydride copolymer in leather.It was found that the applied leather had better quality characteristics with the addition of the nano-sized silica.展开更多
Composite layers containing~0.8%vol Al_(2)O_(3) nanoparticles were produced on AZ91 magnesium alloy by friction stir processing(FSP).The treated layers were characterized using optical and scanning electron microscope...Composite layers containing~0.8%vol Al_(2)O_(3) nanoparticles were produced on AZ91 magnesium alloy by friction stir processing(FSP).The treated layers were characterized using optical and scanning electron microscopes,as well as microhardness and wear testing units.It was noticed that,by reducing the rotational speed and increasing the travel speed,the grain size of the treated layer reduces and its hardness increases.In addition,the presence of nano Al_(2)O_(3) reduces the grain sizes of the layers further and increases their hardness.Furthermore,FSP of AZ91 with Al_(2)O_(3) particles improved the wear resistance significantly and changed the wear mechanism from oxidation and adhesive mode in the as-received AZ91 to oxidation and abrasive in the FSPed specimens.Finally,the rotational speed of 800 rpm and the travel speed of 40 mm/min were the optimum parameters for achieving a suitable composite layer with the highest hardness and wear resistance among the treated layers.展开更多
We report the synthesis of TiO2/ZnSn(OH)6 as a novel nano-composite material via a simultaneous crystallization-etching route with cubic nano-ZnSn(OH)6 and TiF4 as the precursors. The structure, composition and mo...We report the synthesis of TiO2/ZnSn(OH)6 as a novel nano-composite material via a simultaneous crystallization-etching route with cubic nano-ZnSn(OH)6 and TiF4 as the precursors. The structure, composition and morphology of the composite were characterized by XRD, EDS, FETEM and FESEM, which showed the prepared TiO2/ZnSn(OH)6 had a unique morphology of hollow cubic nano-ZnSn(OH)6 attached with rutile TiO2 nanoparticles. The results of photocatalytic activity measurement indicated the photocatalytic activity of the prepared composite was better than that of nano-ZnSn(OH)6. This study may be helpful for the design and fabrication of functional comoosite materials.展开更多
Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV...Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV-visible spectra. Structural and magnetic characteristics were investigated through FT-IR and VSM. The transparency of the Fe2O3/SiO2 nano-composite films decreased with the content of the Fe2O3. Water and organic solvent in the films were evaporated with heat treatment, so the transparency of the films was enhanced under high temperature. It is also found that the saturation magnetization (Ms) of the films increases with the temperature. As the content of the Fe2O3 increases, when the content of the Fe2O3 is around 30wt%, the Ms of the films has a maximum value.展开更多
Nano-composite particles can be synthesized by a hydrogen arc plasma method, which possesses the advantages of high productivity, controllable size distribution and low electric energy consumption comparing with conve...Nano-composite particles can be synthesized by a hydrogen arc plasma method, which possesses the advantages of high productivity, controllable size distribution and low electric energy consumption comparing with conventional gas condensation method. With this method, not only the nanoparticles of metals and alloys, but also the nano-composite particles with shell structure can be synthesized. The microstructures, compositions and the formation mechanism of the nano composite particles were studied展开更多
Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, mor...Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, morphology and structure of the powder samples were investigated by using X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The XRD characterization indicates formation of a cubic crystalline phase in the pure BST. A well defined perovskite phase with nano-crystallite sizes equal to about 34 nm was achieved from XRD for B10ST3F sample, while TEM study confirmed the obtained XRD results giving the following crystallite size value about 33.75 nm for the same sample. The dielectric A.C. conductivity was evaluated as a function of temperature and frequency ranging from 42 Hz up to 1 MHz.展开更多
Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on the carbon steel surface by pulse co-deposition of nickel, tungsten, phosphorus, nano-CeO2 and nano-SiO2 particles. The influence of nano-SiO2 particles concen...Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on the carbon steel surface by pulse co-deposition of nickel, tungsten, phosphorus, nano-CeO2 and nano-SiO2 particles. The influence of nano-SiO2 particles concentrations in electrolyte on microstructures and properties of the nano-composite coatings were researched, and the characteristics were assessed by chemical compositions, element distribution, deposition rate, microhardness and microstructures. The results indicate that when nano-SiO2 particles concentrations in electrolyte are controlled at 20 g·L-1, the deposition rate with 27.07 μm·h-1 and the microhardness with 666 Hv of the nano-composite coatings are highest, element line scanning and area scanning analyses show that the average contents of elements W, P, Si and Ce in the nano-composite coatings are close, displaying that the distribution of every element within the nano-composite coatings is even. An increase in nano-SiO2 particles concentrations in electrolyte (when lower than 20 g·L-1) leads to refinement in grain structure of nano-composite coatings, but when it improved to 30 g·L-1, the crystallite sizes increase again and in the meantime there are a lot of small boss with nodulation shape appearing on the surface of nano-composite coatings.展开更多
The hydrated-titanium-oxide/montmorillonite composite samples were prepared using a hydrolysation- intercalation composite method by controlling the amount of TiOSO4·2H2O. The TiO2/montmorillonite composite sampl...The hydrated-titanium-oxide/montmorillonite composite samples were prepared using a hydrolysation- intercalation composite method by controlling the amount of TiOSO4·2H2O. The TiO2/montmorillonite composite samples were got after calculated at 700℃ and 1100 ℃. The results show that: when the value of Ti/montmorillonite is 12.5 mmol/g, the c axis of hydrated-titanium-oxide/ montmorillonite composite sample began to disorder, moreover, the crystal size of anatase is just 13.4nm in the TiO2/montmorillonite composite sample calculated at 700 ℃, and after calculated at 1100 ℃, the crystal size of anatase is 55.8 nm, and the relative content of anatase reaches the highest (55.7%). Compared with pure TiO2 nano-particle sample, TiO2/montmorillonite composite sample has a higher phase transition temperature from anatase phase to rutile phase and smaller crystal size of TiO2. Montmorillonite structure layer has a significant blocking effect on TiO2 phase transformation and grain growth, and the blocking effect reaches saturation when the value of Ti/montmorillonite is 12.5 mmol/g.展开更多
The hot deformation behaviour of extruded magnesium-zinc oxide nano composite has been studied using hot compression test.The test was conducted in the temperature range of 250-400℃ and in the strain rate range of 0....The hot deformation behaviour of extruded magnesium-zinc oxide nano composite has been studied using hot compression test.The test was conducted in the temperature range of 250-400℃ and in the strain rate range of 0.01 to 1.5 s^(−1).The processing map was obtained using the power dissipation efficiency with the functions of temperature and strain rate.The workability and instability domains were observed in the processing map for a nano composite.The optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)images were used to confirm the formation of dynamic recrystallization(DRX),dynamic recovery(DRY)and instability regions.The workability region of the composite was identified at a working temperature of 400℃ and the strain rate of 0.01 s^(−1) from the processing map.The instability regions were observed at higher strain rates(>0.1 s^(−1))and temperatures(250-400℃).展开更多
Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma s...Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma sputtering. Au particles as perfect spheres with diameters between 10 nm and 30 nm are uniformly dispersed in the SiO2 matrix. Optical absorption peaks due to the surface plasmon resonance of Au particles are observed. The absorption property is enhanced with the increase of Au content, showing a maximum value in the films with 37 vol% Au. The absorption curves of the Au/SiO2 thin films with 3 vol% to 37 vol% Au accord well with the theoretical optical absorption spectra obtained from Mie resonance theory. Increasing Au content over 37 vol% results in the partial connection of Au particles, whereby the intensity of the absorption peak is weakened and ultimately replaced by the optical absorption of the bulk. The band gap decreases with Au content increasing from 3 vol% to 37 vol % but increases as Au content further increases.展开更多
A sintered Ti13Cus7 target was sputtered by reactive direct current (DC) magnetron sputtering with a gas mixture of argon/nitrogen for different sputtering powers. Titanium-coppernitrogen thin films were deposited o...A sintered Ti13Cus7 target was sputtered by reactive direct current (DC) magnetron sputtering with a gas mixture of argon/nitrogen for different sputtering powers. Titanium-coppernitrogen thin films were deposited on Si (111), glass slide and potassium bromide (KBr) substrates. Phase analysis and structural properties of titanium-copper-nitrogen thin films were studied by X-ray diffraction (XRD). The chemical bonding was characterized by Fourier transform infrared (FTIR) spectroscopy. The results from XRD show that the observed phases are nano-crystallite cubic anti rhenium oxide (anti ReO3) structures of titanium doped Cu3N (Ti:Cu3N) and nanocrystallite face centered cubic (fcc) structures of copper. Scanning electron microscopy and energy dispersive X-ray spectroscopy (SEM/EDX) were used to determine the film morphology and atomic titanium/copper ratio, respectively. The films possess continuous and agglomerated structure with an atomic titanium/copper ratio (-0.07) below that of the original target (- 0.15). The transmittance spectra of the composite films were measured in the range of 360 nm to 1100 nm. Film thickness, refractive index and extinction coefficient were extracted from the measured transmittance using a reverse engineering method. In the visible range, the higher absorption coefficient of the films prepared at lower sputtering power indicates more nitrification in comparison to those prepared at higher sputtering power. This is consistent with the formation of larger Ti:Cu3N crystallites at lower sputtering power. The deposition rate vs. sputtering power shows an abrupt transition from metallic mode to poisoned mode. A complicated behavior of the films' resistivity upon sputtering power is shown.展开更多
Nano-composite films of Au particles in Teflon were obtained by thermal vacuum deposition. The obtained films were characterized by the different shapes and dimensions of the inclusion particles. Absorption spectra of...Nano-composite films of Au particles in Teflon were obtained by thermal vacuum deposition. The obtained films were characterized by the different shapes and dimensions of the inclusion particles. Absorption spectra of the films were measured in-situ. A model for the calculation of the optical properties of the nano-composite thin films with an inho-mogeneous distribution of the inclusions along the thickness of the film is proposed. Absorption properties of inclusions were analyzed by considering the local field interaction. The calculated absorption profiles are compared with the experimentally obtained absorption profiles. This comparison gives a possibility to draw conclusions about the concentration, shapes and shape distributions of the inclusion particles. For example, the films obtained by duration deposition are characterized by inclusions having the shape of prolate ellipsoids oriented normally to surface of the film.展开更多
A metalloid Ti13Cu87 target was sputtered by reactive DC magnetron sputtering at various substrate temperatures in an Ar-N2 mixture ambient. The sputtered species were condensed on Si (111), glass slide and Potsssium ...A metalloid Ti13Cu87 target was sputtered by reactive DC magnetron sputtering at various substrate temperatures in an Ar-N2 mixture ambient. The sputtered species were condensed on Si (111), glass slide and Potsssium bromide (KBr) substrates. The as-deposited films were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, Scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), optical spectrophotometry and four point probe technique. The as-deposited films present composite structure of nano-crystallite cubic anti-ReO3 structure of Ti inserted Cu3N (Ti:Cu3N) and nano-crystallite face centre cubic (fcc) structure of Cu. The titanium atoms and sequential nitrogen excess form a solid solution within the Cu3N crystal structure and accommodate in crystal lattice and vacant interstitial site, respectively. Depending on substrate temperature, unreacted N atoms interdiffuse between crystallites and their (and grain) boundaries. The films have agglomerated structure with atomic Ti:Cu ratio less than that of the original targets. A theoretical model has been developed, based on sputtering yield, to predict the atomic Ti:Cu ratio for the as-deposited films. Film thickness, refractive index and extinction coefficient are extracted from the measured transmittance spectra. The films’ resistivity is strongly depending on its microstructural features and substrate temperature.展开更多
In this study, free and forced vibration analysis of nano-composite rotating pressurized microbeam reinforced by carbon nanotubes (CNTs) under magnetic field based on modify couple stress theory (MCST) with temper...In this study, free and forced vibration analysis of nano-composite rotating pressurized microbeam reinforced by carbon nanotubes (CNTs) under magnetic field based on modify couple stress theory (MCST) with temperature-variable material propertiesis presented. Also, the boundary conditions at two ends of nano-composite rotating pressurized microbeam reinforced by CNTs are considered as simply supported. The governing equations are obtained based on the Hamilton's principle and then computed these equations by using Navier's solution. The magnetic field is inserted in the thickness direction of the nano-composite microbeam. The effects of various parameters such as angular velocity, temperature changes, and pressure between of the inside and outside, the magnetic field, material length scale parameter, and volume fraction of nanocomposite microbeam on the natural frequency and response systemare studied. The results show that with increasing volume fraction of nano-composite microbeam, thickness, material length scale parameter, and magnetic fields, the natural frequency increases. The results of this research can be used for optimization of micro-structures and manufacturing sensors, displacement fluid, and drug delivery.展开更多
Two kinds of poly(vinyl alcohol) (PVA)-silica composites were prepared with different methods. One composite was prepared by directly mixing PVA with 80 nm silica nano-particles which were made from tetraethoxysil...Two kinds of poly(vinyl alcohol) (PVA)-silica composites were prepared with different methods. One composite was prepared by directly mixing PVA with 80 nm silica nano-particles which were made from tetraethoxysilane (TEOS). The another was obtained by the mixing PVA and hydrolyzed TEOS in the presence of acid-catalyst. The properties of the two PVA/silica hybrids were characterized by means of scanning electron microscopy (SEM), UV-Visible spectroscopy, solubility tests, limiting oxygen index (LOI) test, tensile test and dynamical mechanical analysis (DMA), respectively. The results indicate that PVA-TEOS composites (PT for short) display more transparency than PVA-silica nano-particles hybrids (PS for short). At the same time, The PT composites presented more excellent performance than PS in water resistance, fire resistance and mechanical properties. Moreover, the Tg of PT increased with increasing TEOS content, while that of PS decreased.展开更多
Multifunctional nano composite coatings of Zn-TiO_2-WO_3 were deposited electrolytically on mild steel(MS) from Zn bath, having Zn^(2+) ions and uniform dispersion of TiO_2 and WO_3 nano particulates. The electrical, ...Multifunctional nano composite coatings of Zn-TiO_2-WO_3 were deposited electrolytically on mild steel(MS) from Zn bath, having Zn^(2+) ions and uniform dispersion of TiO_2 and WO_3 nano particulates. The electrical, optical and corrosion resistance characteristics of the electrocodeposited coatings were assessed by Keithley 2400 Series Source meter with Multimeters, Newport Solar Simulator and a PGSTAT30 Autolab potentiostat respectively. The morphological characteristics of the composite coatings were characterized by scanning electron microscope(SEM) equipped with energy dispersive spectrometer(EDS). The result revealed that the electrocodeposits showed good stability and Zn-TiO_2-WO_3 nanocomposite deposits displayed enhanced microstructural qualities, good electrical conductivity and exhibited enriched corrosion resistance.展开更多
基金The authors gratefully acknowledge the support of DST(GOI)through Smart Foundry 2020 program.
文摘In this study,the effects of WC nano-particles amount and surface roughness on corrosion behavior of magnesium metal matrix nanocomposites in 3.5%NaCl solution are examined with the help of electrochemical test.Varying wt%of WC nano-particles(0.5,1,1.5 and 2)are used to fabricate metal matrix nano-composites through ultrasonic vibration assisted stir casting method.Basic characterizations of fabricated composites are performed by using scanning electron microscopy(SEM)and energy dispersive x-ray analysis(EDAX).SEM images show that nano-particles are well distributed throughout the magnesium matrix while EDAX results confirm the presence of WC particles in nano-composites.Micro-hardness result shows increasing trend with increasing weight percentage of WC.Mg nano-composite containing 0.5 wt%WC nano-particles is found to be the most corrosion resistive one followed by base alloy,Mg-2 wt%WC,Mg-1.5 wt%WC and Mg-1 wt%WC.Additionally,corrosion behavior of Mg-2WC with different surface quality is examined and it is observed that sample with lowest surface roughness shows better corrosion resistance.In the end,corrosion mechanisms are assessed with the help of SEM and EDAX study of corroded surfaces.
基金supported by the Natural Science Foundation of China(21173147 and 21376143)973 Program of China(2014CB239700)
文摘As an ionic conductive functional layer of intermediate temperature solid oxide fuel cells(ITSOFC), samarium-doped ceria(SDC)–Li Na SO4nano-composites were synthesized by a sol–gel method and their properties were investigated. It was found that the content of Li Na SO4 strongly affected the crystal phase, defect concentration, and conductivity of the composites. When the content of Li Na SO4 was 20 wt%, the highest conductivity of the composite was found to be, respectively, 0.22, 0.26, and 0.35 S cm-1at temperatures of 550, 600, and 700 °C, which are much higher than those of SDC. The peak power density of the single cell using this composite as an interlayer was improved to, respectively, 0.23, 0.39, and 0.88 W cm-2at 500, 600, and 700 °C comparing with that of the SDC-based cell. Further, the SDC–Li Na SO4(20 wt%)-based cell also displayed better thermal stability according to the performance measurements at 560 °C for 50 h. These results reveal that SDC–Li Na SO4 composite may be a potential good candidate as interlayer for ITSOFC due to its high ionic conductivity and thermal stability.
文摘This study investigates the removal of Congo Red dye from aqueous solution using functionalized generation 3.0 and 5.0 polyamidoamine dendrimer-silica gel composite (G-3PS, G-5PS). Fourier Transform-Infra Red spectroscopy, Brunauer Emmett and Teller, Thermo Gravimetric Analysis, pH at point of zero charge, and scanning electron microscopy measurements have been applied to characterize the synthetic nanohybrid composite, these techniques revealed the successful functionalization of both dendrimer molecules and subsequent immobilization onto silica gel. The implications of varying adsorption parameters such as contact time, initial concentration of adsorbate, temperature and pH on both composites were studied. Experimental data obtained from batch adsorption processes were fitted into two equilibrium isotherms (Langmuir and Freundlich) and 3 kinetic models (Pseudo-First-Order, Pseudo-Second-Order, Intra Particle Diffusion). Adsorption mechanism was mainly governed by film diffusion due to electrostatic interactions between the functionalized dendrimer surface and Congo Red molecules. Thermodynamic parameters illustrate that the adsorption is endothermic and spontaneous. Findings suggest the Nanocomposites (G-3PS and G-5PS) are good adsorbents for the removal of Congo Red dye from aqueous solutions.
基金Applied Basic Research Plans Program of Yunnan Province(2007E187M)Scientific Research Fund (2006-02)Analysis and Measurement Research Fund (2007-22) of Kunming University of Science and Technology
文摘Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on common carbon steel surface by pulse electrodeposition of nickel, tungsten, phosphorus, rare earth (nano-CeO2) and silicon carbide (nano-SiO2) particles. The effects of nano-CeO2 concentrations in electrolyte on microstructures and properties of nano-composite coatings were studied. The samples were characterized with chemical compositions, elements distributions, microhardness and microstructures. The results indicated that when nano-CeO2 concentration was controlled at 10 g/L, the nano-composite coatings possessed higher microhardness and compact microstmctures with clear outline of spherical matrix metal crystallites, fine crystallite sizes and uniform distribution of elements W, P, Ce and Si within the Ni-W-P matrix metal. Increasing the nano-CeO2 particles concentrations from 4 to 10 g/L led to refinement in grain structure and improvement of microstructures, while when increased to 14 g/L, the crystallite sizes began to increase again and there were a lot of small boss with nodulation shape appearing on the nano-composite coatings surface.
文摘The radical polymerization of maleic anhydride(MA),styrene(ST)with the vinyl groups introduced onto the surface of the nano-sized silica via solution polymerization method was developed.The methacryloxypropyl nano-sized silica(MPNS)was used as macromonomer and polymerized with maleic anhydride and styrene by initiating with BPO in toluene.The structure and properties of MPNS/SMA nano-composite were characterized by FT-IR spectra and TEM.Meanwhile,it was applied as tanning agent compared with the traditional styrene-maleic anhydride copolymer in leather.It was found that the applied leather had better quality characteristics with the addition of the nano-sized silica.
文摘Composite layers containing~0.8%vol Al_(2)O_(3) nanoparticles were produced on AZ91 magnesium alloy by friction stir processing(FSP).The treated layers were characterized using optical and scanning electron microscopes,as well as microhardness and wear testing units.It was noticed that,by reducing the rotational speed and increasing the travel speed,the grain size of the treated layer reduces and its hardness increases.In addition,the presence of nano Al_(2)O_(3) reduces the grain sizes of the layers further and increases their hardness.Furthermore,FSP of AZ91 with Al_(2)O_(3) particles improved the wear resistance significantly and changed the wear mechanism from oxidation and adhesive mode in the as-received AZ91 to oxidation and abrasive in the FSPed specimens.Finally,the rotational speed of 800 rpm and the travel speed of 40 mm/min were the optimum parameters for achieving a suitable composite layer with the highest hardness and wear resistance among the treated layers.
基金Supported by the Natural Science Foundation of Fujian Province(No.2013J05027)Fujian Province Education-Science Project for Middle-aged and Young Teachers(No.JA13050)
文摘We report the synthesis of TiO2/ZnSn(OH)6 as a novel nano-composite material via a simultaneous crystallization-etching route with cubic nano-ZnSn(OH)6 and TiF4 as the precursors. The structure, composition and morphology of the composite were characterized by XRD, EDS, FETEM and FESEM, which showed the prepared TiO2/ZnSn(OH)6 had a unique morphology of hollow cubic nano-ZnSn(OH)6 attached with rutile TiO2 nanoparticles. The results of photocatalytic activity measurement indicated the photocatalytic activity of the prepared composite was better than that of nano-ZnSn(OH)6. This study may be helpful for the design and fabrication of functional comoosite materials.
基金Funded by the Innovative Program of Shanghai Municipal Education Commission (No.08YZ97)the National Natural Science Foundation of China (No.10704048)
文摘Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV-visible spectra. Structural and magnetic characteristics were investigated through FT-IR and VSM. The transparency of the Fe2O3/SiO2 nano-composite films decreased with the content of the Fe2O3. Water and organic solvent in the films were evaporated with heat treatment, so the transparency of the films was enhanced under high temperature. It is also found that the saturation magnetization (Ms) of the films increases with the temperature. As the content of the Fe2O3 increases, when the content of the Fe2O3 is around 30wt%, the Ms of the films has a maximum value.
文摘Nano-composite particles can be synthesized by a hydrogen arc plasma method, which possesses the advantages of high productivity, controllable size distribution and low electric energy consumption comparing with conventional gas condensation method. With this method, not only the nanoparticles of metals and alloys, but also the nano-composite particles with shell structure can be synthesized. The microstructures, compositions and the formation mechanism of the nano composite particles were studied
文摘Nano-composite, perovskite Ba(1- x - y)Sr(x)TiFe(y)O3, denoted as (BSTFe) in powder form was derived via sol-gel (SG) method followed by sintering at fixed temperature 750℃ for one hour. The chemical composition, morphology and structure of the powder samples were investigated by using X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The XRD characterization indicates formation of a cubic crystalline phase in the pure BST. A well defined perovskite phase with nano-crystallite sizes equal to about 34 nm was achieved from XRD for B10ST3F sample, while TEM study confirmed the obtained XRD results giving the following crystallite size value about 33.75 nm for the same sample. The dielectric A.C. conductivity was evaluated as a function of temperature and frequency ranging from 42 Hz up to 1 MHz.
基金Projects supported by Applied Basic Research Plans Programof Yunnan Province (2007E 187M)Scientific Research Fund(2006-02)Analysis and Measurement Research Fund (2007-22) of Kunming University of Science and Technology
文摘Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on the carbon steel surface by pulse co-deposition of nickel, tungsten, phosphorus, nano-CeO2 and nano-SiO2 particles. The influence of nano-SiO2 particles concentrations in electrolyte on microstructures and properties of the nano-composite coatings were researched, and the characteristics were assessed by chemical compositions, element distribution, deposition rate, microhardness and microstructures. The results indicate that when nano-SiO2 particles concentrations in electrolyte are controlled at 20 g·L-1, the deposition rate with 27.07 μm·h-1 and the microhardness with 666 Hv of the nano-composite coatings are highest, element line scanning and area scanning analyses show that the average contents of elements W, P, Si and Ce in the nano-composite coatings are close, displaying that the distribution of every element within the nano-composite coatings is even. An increase in nano-SiO2 particles concentrations in electrolyte (when lower than 20 g·L-1) leads to refinement in grain structure of nano-composite coatings, but when it improved to 30 g·L-1, the crystallite sizes increase again and in the meantime there are a lot of small boss with nodulation shape appearing on the surface of nano-composite coatings.
文摘The hydrated-titanium-oxide/montmorillonite composite samples were prepared using a hydrolysation- intercalation composite method by controlling the amount of TiOSO4·2H2O. The TiO2/montmorillonite composite samples were got after calculated at 700℃ and 1100 ℃. The results show that: when the value of Ti/montmorillonite is 12.5 mmol/g, the c axis of hydrated-titanium-oxide/ montmorillonite composite sample began to disorder, moreover, the crystal size of anatase is just 13.4nm in the TiO2/montmorillonite composite sample calculated at 700 ℃, and after calculated at 1100 ℃, the crystal size of anatase is 55.8 nm, and the relative content of anatase reaches the highest (55.7%). Compared with pure TiO2 nano-particle sample, TiO2/montmorillonite composite sample has a higher phase transition temperature from anatase phase to rutile phase and smaller crystal size of TiO2. Montmorillonite structure layer has a significant blocking effect on TiO2 phase transformation and grain growth, and the blocking effect reaches saturation when the value of Ti/montmorillonite is 12.5 mmol/g.
文摘The hot deformation behaviour of extruded magnesium-zinc oxide nano composite has been studied using hot compression test.The test was conducted in the temperature range of 250-400℃ and in the strain rate range of 0.01 to 1.5 s^(−1).The processing map was obtained using the power dissipation efficiency with the functions of temperature and strain rate.The workability and instability domains were observed in the processing map for a nano composite.The optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)images were used to confirm the formation of dynamic recrystallization(DRX),dynamic recovery(DRY)and instability regions.The workability region of the composite was identified at a working temperature of 400℃ and the strain rate of 0.01 s^(−1) from the processing map.The instability regions were observed at higher strain rates(>0.1 s^(−1))and temperatures(250-400℃).
基金Project supported by the National Natural Science Foundation of China (Grant Nos 50842028 and 50972012)the National Basic Research Program of China (Grant No 2007CB613301)
文摘Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma sputtering. Au particles as perfect spheres with diameters between 10 nm and 30 nm are uniformly dispersed in the SiO2 matrix. Optical absorption peaks due to the surface plasmon resonance of Au particles are observed. The absorption property is enhanced with the increase of Au content, showing a maximum value in the films with 37 vol% Au. The absorption curves of the Au/SiO2 thin films with 3 vol% to 37 vol% Au accord well with the theoretical optical absorption spectra obtained from Mie resonance theory. Increasing Au content over 37 vol% results in the partial connection of Au particles, whereby the intensity of the absorption peak is weakened and ultimately replaced by the optical absorption of the bulk. The band gap decreases with Au content increasing from 3 vol% to 37 vol % but increases as Au content further increases.
基金the financial support of the Iranian nanotechnology initiative
文摘A sintered Ti13Cus7 target was sputtered by reactive direct current (DC) magnetron sputtering with a gas mixture of argon/nitrogen for different sputtering powers. Titanium-coppernitrogen thin films were deposited on Si (111), glass slide and potassium bromide (KBr) substrates. Phase analysis and structural properties of titanium-copper-nitrogen thin films were studied by X-ray diffraction (XRD). The chemical bonding was characterized by Fourier transform infrared (FTIR) spectroscopy. The results from XRD show that the observed phases are nano-crystallite cubic anti rhenium oxide (anti ReO3) structures of titanium doped Cu3N (Ti:Cu3N) and nanocrystallite face centered cubic (fcc) structures of copper. Scanning electron microscopy and energy dispersive X-ray spectroscopy (SEM/EDX) were used to determine the film morphology and atomic titanium/copper ratio, respectively. The films possess continuous and agglomerated structure with an atomic titanium/copper ratio (-0.07) below that of the original target (- 0.15). The transmittance spectra of the composite films were measured in the range of 360 nm to 1100 nm. Film thickness, refractive index and extinction coefficient were extracted from the measured transmittance using a reverse engineering method. In the visible range, the higher absorption coefficient of the films prepared at lower sputtering power indicates more nitrification in comparison to those prepared at higher sputtering power. This is consistent with the formation of larger Ti:Cu3N crystallites at lower sputtering power. The deposition rate vs. sputtering power shows an abrupt transition from metallic mode to poisoned mode. A complicated behavior of the films' resistivity upon sputtering power is shown.
文摘Nano-composite films of Au particles in Teflon were obtained by thermal vacuum deposition. The obtained films were characterized by the different shapes and dimensions of the inclusion particles. Absorption spectra of the films were measured in-situ. A model for the calculation of the optical properties of the nano-composite thin films with an inho-mogeneous distribution of the inclusions along the thickness of the film is proposed. Absorption properties of inclusions were analyzed by considering the local field interaction. The calculated absorption profiles are compared with the experimentally obtained absorption profiles. This comparison gives a possibility to draw conclusions about the concentration, shapes and shape distributions of the inclusion particles. For example, the films obtained by duration deposition are characterized by inclusions having the shape of prolate ellipsoids oriented normally to surface of the film.
文摘A metalloid Ti13Cu87 target was sputtered by reactive DC magnetron sputtering at various substrate temperatures in an Ar-N2 mixture ambient. The sputtered species were condensed on Si (111), glass slide and Potsssium bromide (KBr) substrates. The as-deposited films were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, Scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), optical spectrophotometry and four point probe technique. The as-deposited films present composite structure of nano-crystallite cubic anti-ReO3 structure of Ti inserted Cu3N (Ti:Cu3N) and nano-crystallite face centre cubic (fcc) structure of Cu. The titanium atoms and sequential nitrogen excess form a solid solution within the Cu3N crystal structure and accommodate in crystal lattice and vacant interstitial site, respectively. Depending on substrate temperature, unreacted N atoms interdiffuse between crystallites and their (and grain) boundaries. The films have agglomerated structure with atomic Ti:Cu ratio less than that of the original targets. A theoretical model has been developed, based on sputtering yield, to predict the atomic Ti:Cu ratio for the as-deposited films. Film thickness, refractive index and extinction coefficient are extracted from the measured transmittance spectra. The films’ resistivity is strongly depending on its microstructural features and substrate temperature.
基金the Iranian Nanotechnology Development Committee for their financial supportthe University of Kashan (463855/7)
文摘In this study, free and forced vibration analysis of nano-composite rotating pressurized microbeam reinforced by carbon nanotubes (CNTs) under magnetic field based on modify couple stress theory (MCST) with temperature-variable material propertiesis presented. Also, the boundary conditions at two ends of nano-composite rotating pressurized microbeam reinforced by CNTs are considered as simply supported. The governing equations are obtained based on the Hamilton's principle and then computed these equations by using Navier's solution. The magnetic field is inserted in the thickness direction of the nano-composite microbeam. The effects of various parameters such as angular velocity, temperature changes, and pressure between of the inside and outside, the magnetic field, material length scale parameter, and volume fraction of nanocomposite microbeam on the natural frequency and response systemare studied. The results show that with increasing volume fraction of nano-composite microbeam, thickness, material length scale parameter, and magnetic fields, the natural frequency increases. The results of this research can be used for optimization of micro-structures and manufacturing sensors, displacement fluid, and drug delivery.
基金financially supported by the National Natural Science Foundation of China(No.51173112)the Special Funds for Major Basic Research Projects of China(No.2011CB606006)
文摘Two kinds of poly(vinyl alcohol) (PVA)-silica composites were prepared with different methods. One composite was prepared by directly mixing PVA with 80 nm silica nano-particles which were made from tetraethoxysilane (TEOS). The another was obtained by the mixing PVA and hydrolyzed TEOS in the presence of acid-catalyst. The properties of the two PVA/silica hybrids were characterized by means of scanning electron microscopy (SEM), UV-Visible spectroscopy, solubility tests, limiting oxygen index (LOI) test, tensile test and dynamical mechanical analysis (DMA), respectively. The results indicate that PVA-TEOS composites (PT for short) display more transparency than PVA-silica nano-particles hybrids (PS for short). At the same time, The PT composites presented more excellent performance than PS in water resistance, fire resistance and mechanical properties. Moreover, the Tg of PT increased with increasing TEOS content, while that of PS decreased.
基金financial support by National Research Foundation
文摘Multifunctional nano composite coatings of Zn-TiO_2-WO_3 were deposited electrolytically on mild steel(MS) from Zn bath, having Zn^(2+) ions and uniform dispersion of TiO_2 and WO_3 nano particulates. The electrical, optical and corrosion resistance characteristics of the electrocodeposited coatings were assessed by Keithley 2400 Series Source meter with Multimeters, Newport Solar Simulator and a PGSTAT30 Autolab potentiostat respectively. The morphological characteristics of the composite coatings were characterized by scanning electron microscope(SEM) equipped with energy dispersive spectrometer(EDS). The result revealed that the electrocodeposits showed good stability and Zn-TiO_2-WO_3 nanocomposite deposits displayed enhanced microstructural qualities, good electrical conductivity and exhibited enriched corrosion resistance.