The purpose of this study was to evaluate the influence of acid etching on the bond strength of a universal adhesive system (Single Bond Universal, 3M) to caries-affected dentin. Forty permanent third molars were sele...The purpose of this study was to evaluate the influence of acid etching on the bond strength of a universal adhesive system (Single Bond Universal, 3M) to caries-affected dentin. Forty permanent third molars were selected and carious lesions were induced by the microbiological method with?S. mutans?ATCC25175. Teeth were allocated randomly across four experimental designs (n?=?10): PA-I: phosphoric acid etching and application of the adhesive system, followed by immediate microtensile bond strength testing;PA-CC: phosphoric acid etching and application of the adhesive system, followed by microtensile bond strength testing after a 14-day cariogenic challenge;NPA-I: application of the adhesive system without acid etching, followed by immediate bond strength testing and NPA-CC: application of the adhesive system without acid etching followed by bond strength testing after 14-day cariogenic challenge. For microtensile bond strength testing,?a restoration with Charisma composite resin was made and each specimen was sectioned with a cross-sectional area of 1 mm2. Only adhesive and mixed fractures were considered for bond strength calculation. Results were evaluated by the Kruskal-Wallis and Friedman tests. The highest bond strengths were observed in the phosphoric acid etching groups (p??0.05). Cariogenic challenge did not affect bond strength (p?>?0.05). The predominant fracture type was adhesive. We conclude that phosphoric acid increased the bond strength of the Single Bond Universal system to caries-affected dentin, and that cariogenic challenge did not interfere with this bond strength.展开更多
目的:比较4种不同的粘接系统对正常牙本质和龋损影响牙本质的粘接强度。方法:24颗近中面中龋的人离体磨牙,在龋损检知液监控下用慢速球钻去龋,在远中面健康牙本质上制备相同深度的窝洞。随机分为4组,分别用4种粘接系统(Prime&Bo...目的:比较4种不同的粘接系统对正常牙本质和龋损影响牙本质的粘接强度。方法:24颗近中面中龋的人离体磨牙,在龋损检知液监控下用慢速球钻去龋,在远中面健康牙本质上制备相同深度的窝洞。随机分为4组,分别用4种粘接系统(Prime&Bond NT,Adper Single Bond 2,Adper Prompt和XenoⅢ)按照使用说明进行粘接,用树脂(FiltekP60)修复后保存于37℃的水中。沿牙长轴方向将树脂和牙齿从颊舌方向片切,厚度约为1.0mm,并修整成粘接面(正常牙本质或龋损影响牙本质)面积约1mm2的试件,进行微拉伸实验,并用扫描电镜观察粘接面形态。结果:4种粘接系统在正常牙本质上获得的粘接强度均强于在龋损影响牙本质上获得的强度(P<0.05);2种全酸蚀粘接系统在2种牙本质上获得的粘接强度均强于2种自酸蚀粘接系统获得的强度(P<0.05)。扫描电镜观察,混合层在龋损影响牙本质上表现得厚但更疏松;与正常牙本质相比,龋损影响牙本质上形成的树脂突少。结论:2种全酸蚀粘接系统无论在正常牙本质还是龋损影响牙本质上均能获得比2种自酸蚀粘接系统更强的粘接力。展开更多
目的:比较臭氧(O3)联合再矿化与单纯O3、单纯再矿化处理对离体乳牙脱矿牙本质显微硬度及表层微结构的影响。方法:根据纳入和排除标准筛选出经无创伤修复治疗法去腐后包埋纵剖的40例离体乳牙样本,随机分为4组,分别进行40 s O3处理(A组);1...目的:比较臭氧(O3)联合再矿化与单纯O3、单纯再矿化处理对离体乳牙脱矿牙本质显微硬度及表层微结构的影响。方法:根据纳入和排除标准筛选出经无创伤修复治疗法去腐后包埋纵剖的40例离体乳牙样本,随机分为4组,分别进行40 s O3处理(A组);1 min再矿化液涂布(B组)及40 s O3联合1 min再矿化处理(C组)及对照组(D组)。用维氏显微硬度值(Vikers Microhardness Number,VHN)和扫描电镜(Scanningelectron microscope,SEM)评价效果。结果:本实验采取析因设计,经方差分析显示,A、B两组VHN与对照组相比差异有统计学意义(P<0.05),C组VHN虽有升高,但其交互作用无统计学意义(P>0.05);扫描电镜显示:A组和C组较B组及D组(对照组)清洁度高。结论:40 s O3联合1 min再矿化处理可显著提高乳牙脱矿牙本质的VHN,但VHN的升高主要是因O3对牙本质有较强的脱水作用,改变了牙本质弹性模量而引起的。O3的负压状态有利于清除牙本质碎屑,暴露牙本质小管。展开更多
目的:评价人工唾液浸泡对牙本质黏结强度的影响。方法:30个中龋人离体磨牙,在龋检液监控下慢速手机去龋后,以洞底为准磨平周围健康牙本质。然后随机分成3组,分别应用Prime & Bond NT、Adper Prompt、Contax黏结剂处理,其上制作复合...目的:评价人工唾液浸泡对牙本质黏结强度的影响。方法:30个中龋人离体磨牙,在龋检液监控下慢速手机去龋后,以洞底为准磨平周围健康牙本质。然后随机分成3组,分别应用Prime & Bond NT、Adper Prompt、Contax黏结剂处理,其上制作复合树脂冠。制备1mm×1mm的条形试件,每个牙取黏结界面为正常牙本质(ND)和龋损内层牙本质(CAD)的试件各6个。再随机分成3组,其中1组立即进行微拉伸黏结强度测试(作为对照组),另2组分别在人工唾液中浸泡3个月、6个月,然后进行微拉伸黏结强度测试。结果:唾液浸泡前3种黏结系统对龋损内层牙本质和正常牙本质的黏结强度均无显著差异(P>0.05),唾液浸泡3个月,3种黏结系统对正常牙本质的黏结强度与对照组相比无显著下降,与对照组相比差异不显著(P>0.05);而对龋损内层牙本质的黏结强度均明显下降,显著小于对照组和正常牙本质(P<0.05)。唾液浸泡6个月,3种黏结系统对龋损内层牙本质的黏结强度均低于3个月组(P<0.05),对正常牙本质的黏结强度CT仍与对照组无显著差异(P>0.05),而NT和AP则明显低于3个月组(P<0.05)。结论:随着唾液浸泡时间延长,牙本质黏结强度逐渐下降,2种牙本质之间,龋损内层牙本质黏结稳定性较差。展开更多
目的：评估简化乙醇湿粘结技术对龋影响牙本质粘结强度的影响。方法：选取人慢性龋离体第三磨牙36颗去龋备洞后保留龋影响牙本质。随机分为6组,分别使用自制疏水性粘结剂,Prime＆Bond NT（PB）,Adper Single bond plus（SB）进行粘结,...目的：评估简化乙醇湿粘结技术对龋影响牙本质粘结强度的影响。方法：选取人慢性龋离体第三磨牙36颗去龋备洞后保留龋影响牙本质。随机分为6组,分别使用自制疏水性粘结剂,Prime＆Bond NT（PB）,Adper Single bond plus（SB）进行粘结,堆砌树脂厚度约4~5mm。实验组采用简化乙醇湿粘结法,对照组采用传统水湿粘结法。制作1mm×1mm×8mm的条形微拉伸强度试件,每组选取8个。采用万能材料试验机测试微拉伸强度并记录,观察断裂界面。结果：在自制疏水性粘结剂组中,实验组粘结强度较对照组有显著提高（P〈0.05）。结论：简化乙醇湿粘结技术可以提高CAD界面的粘结强度,尤其是在与疏水性粘结剂联合运用时,有显著提高。展开更多
目的：探讨表没食子儿茶素没食子酸酯（EGCG）改良后自酸蚀粘接剂可乐丽Clearfil SE Bond对龋影响牙本质即刻粘接性能影响。方法选取中龋离体牙20颗,在龋指示剂下去除龋感染牙本质,保留龋影响牙本质。将EGCG配制成100、200、300μg/ml C...目的：探讨表没食子儿茶素没食子酸酯（EGCG）改良后自酸蚀粘接剂可乐丽Clearfil SE Bond对龋影响牙本质即刻粘接性能影响。方法选取中龋离体牙20颗,在龋指示剂下去除龋感染牙本质,保留龋影响牙本质。将EGCG配制成100、200、300μg/ml Clearfil SE Bond粘接剂溶液及水溶液,以不添加EGCG粘接剂及水溶液作为对照组。微拉伸试件分组按照Clearfil SE Bond说明书指导进行粘接,上方堆塑5-6 mm Z350树脂。使用慢速线性切割机沿牙齿长轴进行切割,形成约1 mm ×1 mm试件,进行微拉伸实验。显微硬度试件分组浸泡于EGCG水溶液中24 h后测试显微硬度。使用SPSS 22.0统计学软件,在One-Way ANOVA模式下进行统计学分析。结果 EGCG处理后龋影响牙本质的粘接强度及显微硬度均明显提高,差异有统计学意义（F粘接强度=24.554,P粘接强度﹤0.05；F 显微硬度=20.418,P显微硬度﹤0.05）。结论 EGCG可增强龋影响牙本质的即刻粘接强度及显微硬度。展开更多
文摘The purpose of this study was to evaluate the influence of acid etching on the bond strength of a universal adhesive system (Single Bond Universal, 3M) to caries-affected dentin. Forty permanent third molars were selected and carious lesions were induced by the microbiological method with?S. mutans?ATCC25175. Teeth were allocated randomly across four experimental designs (n?=?10): PA-I: phosphoric acid etching and application of the adhesive system, followed by immediate microtensile bond strength testing;PA-CC: phosphoric acid etching and application of the adhesive system, followed by microtensile bond strength testing after a 14-day cariogenic challenge;NPA-I: application of the adhesive system without acid etching, followed by immediate bond strength testing and NPA-CC: application of the adhesive system without acid etching followed by bond strength testing after 14-day cariogenic challenge. For microtensile bond strength testing,?a restoration with Charisma composite resin was made and each specimen was sectioned with a cross-sectional area of 1 mm2. Only adhesive and mixed fractures were considered for bond strength calculation. Results were evaluated by the Kruskal-Wallis and Friedman tests. The highest bond strengths were observed in the phosphoric acid etching groups (p??0.05). Cariogenic challenge did not affect bond strength (p?>?0.05). The predominant fracture type was adhesive. We conclude that phosphoric acid increased the bond strength of the Single Bond Universal system to caries-affected dentin, and that cariogenic challenge did not interfere with this bond strength.
文摘目的:比较4种不同的粘接系统对正常牙本质和龋损影响牙本质的粘接强度。方法:24颗近中面中龋的人离体磨牙,在龋损检知液监控下用慢速球钻去龋,在远中面健康牙本质上制备相同深度的窝洞。随机分为4组,分别用4种粘接系统(Prime&Bond NT,Adper Single Bond 2,Adper Prompt和XenoⅢ)按照使用说明进行粘接,用树脂(FiltekP60)修复后保存于37℃的水中。沿牙长轴方向将树脂和牙齿从颊舌方向片切,厚度约为1.0mm,并修整成粘接面(正常牙本质或龋损影响牙本质)面积约1mm2的试件,进行微拉伸实验,并用扫描电镜观察粘接面形态。结果:4种粘接系统在正常牙本质上获得的粘接强度均强于在龋损影响牙本质上获得的强度(P<0.05);2种全酸蚀粘接系统在2种牙本质上获得的粘接强度均强于2种自酸蚀粘接系统获得的强度(P<0.05)。扫描电镜观察,混合层在龋损影响牙本质上表现得厚但更疏松;与正常牙本质相比,龋损影响牙本质上形成的树脂突少。结论:2种全酸蚀粘接系统无论在正常牙本质还是龋损影响牙本质上均能获得比2种自酸蚀粘接系统更强的粘接力。
文摘目的:比较臭氧(O3)联合再矿化与单纯O3、单纯再矿化处理对离体乳牙脱矿牙本质显微硬度及表层微结构的影响。方法:根据纳入和排除标准筛选出经无创伤修复治疗法去腐后包埋纵剖的40例离体乳牙样本,随机分为4组,分别进行40 s O3处理(A组);1 min再矿化液涂布(B组)及40 s O3联合1 min再矿化处理(C组)及对照组(D组)。用维氏显微硬度值(Vikers Microhardness Number,VHN)和扫描电镜(Scanningelectron microscope,SEM)评价效果。结果:本实验采取析因设计,经方差分析显示,A、B两组VHN与对照组相比差异有统计学意义(P<0.05),C组VHN虽有升高,但其交互作用无统计学意义(P>0.05);扫描电镜显示:A组和C组较B组及D组(对照组)清洁度高。结论:40 s O3联合1 min再矿化处理可显著提高乳牙脱矿牙本质的VHN,但VHN的升高主要是因O3对牙本质有较强的脱水作用,改变了牙本质弹性模量而引起的。O3的负压状态有利于清除牙本质碎屑,暴露牙本质小管。
文摘目的:评价人工唾液浸泡对牙本质黏结强度的影响。方法:30个中龋人离体磨牙,在龋检液监控下慢速手机去龋后,以洞底为准磨平周围健康牙本质。然后随机分成3组,分别应用Prime & Bond NT、Adper Prompt、Contax黏结剂处理,其上制作复合树脂冠。制备1mm×1mm的条形试件,每个牙取黏结界面为正常牙本质(ND)和龋损内层牙本质(CAD)的试件各6个。再随机分成3组,其中1组立即进行微拉伸黏结强度测试(作为对照组),另2组分别在人工唾液中浸泡3个月、6个月,然后进行微拉伸黏结强度测试。结果:唾液浸泡前3种黏结系统对龋损内层牙本质和正常牙本质的黏结强度均无显著差异(P>0.05),唾液浸泡3个月,3种黏结系统对正常牙本质的黏结强度与对照组相比无显著下降,与对照组相比差异不显著(P>0.05);而对龋损内层牙本质的黏结强度均明显下降,显著小于对照组和正常牙本质(P<0.05)。唾液浸泡6个月,3种黏结系统对龋损内层牙本质的黏结强度均低于3个月组(P<0.05),对正常牙本质的黏结强度CT仍与对照组无显著差异(P>0.05),而NT和AP则明显低于3个月组(P<0.05)。结论:随着唾液浸泡时间延长,牙本质黏结强度逐渐下降,2种牙本质之间,龋损内层牙本质黏结稳定性较差。
文摘目的：评估简化乙醇湿粘结技术对龋影响牙本质粘结强度的影响。方法：选取人慢性龋离体第三磨牙36颗去龋备洞后保留龋影响牙本质。随机分为6组,分别使用自制疏水性粘结剂,Prime＆Bond NT（PB）,Adper Single bond plus（SB）进行粘结,堆砌树脂厚度约4~5mm。实验组采用简化乙醇湿粘结法,对照组采用传统水湿粘结法。制作1mm×1mm×8mm的条形微拉伸强度试件,每组选取8个。采用万能材料试验机测试微拉伸强度并记录,观察断裂界面。结果：在自制疏水性粘结剂组中,实验组粘结强度较对照组有显著提高（P〈0.05）。结论：简化乙醇湿粘结技术可以提高CAD界面的粘结强度,尤其是在与疏水性粘结剂联合运用时,有显著提高。
文摘目的：探讨表没食子儿茶素没食子酸酯（EGCG）改良后自酸蚀粘接剂可乐丽Clearfil SE Bond对龋影响牙本质即刻粘接性能影响。方法选取中龋离体牙20颗,在龋指示剂下去除龋感染牙本质,保留龋影响牙本质。将EGCG配制成100、200、300μg/ml Clearfil SE Bond粘接剂溶液及水溶液,以不添加EGCG粘接剂及水溶液作为对照组。微拉伸试件分组按照Clearfil SE Bond说明书指导进行粘接,上方堆塑5-6 mm Z350树脂。使用慢速线性切割机沿牙齿长轴进行切割,形成约1 mm ×1 mm试件,进行微拉伸实验。显微硬度试件分组浸泡于EGCG水溶液中24 h后测试显微硬度。使用SPSS 22.0统计学软件,在One-Way ANOVA模式下进行统计学分析。结果 EGCG处理后龋影响牙本质的粘接强度及显微硬度均明显提高,差异有统计学意义（F粘接强度=24.554,P粘接强度﹤0.05；F 显微硬度=20.418,P显微硬度﹤0.05）。结论 EGCG可增强龋影响牙本质的即刻粘接强度及显微硬度。