A grain-oriented silicon steel strip with AlN as main inhibitor was produced by thin slab casting and rolling（TSCR）process.The microstructure,texture and precipitates of the hot-rolled strip were investigated by use...A grain-oriented silicon steel strip with AlN as main inhibitor was produced by thin slab casting and rolling（TSCR）process.The microstructure,texture and precipitates of the hot-rolled strip were investigated by use of optical microscope（OM）,X-ray diffractometer,transmission electron microscope（TEM）and energy dispersive spectroscope（EDS）.The result shows that the microstructure and texture exhibit a through-thickness gradient similar to that of the hot-rolled strip produced by conventional high-temperature slab-reheating process;the preferred orientation varies from {110}〈001〉in the surface layer to{001}〈110〉in the center layer,and the Goss texture with a maximum intensity mainly concentrates on the surface layer.In addition,some other texture components,for example rotated Goss texture,form in the 1/4thickness layer,which are not observed in the hotrolled strip produced by conventional high-temperature slab-reheating process.The precipitates in the hot-rolled strip are mainly（Mn,Cu）S and AlN compound particles with dimension of 100-200 nm,and the fine precipitates are significantly less than that in the hot-rolled strip produced by conventional high-temperature slab-reheating process.Moreover,the areal density of the fine precipitates in the center layer is more than that in the surface layer.展开更多
The status quo and future development trend of Baosteel continuous casting （CC） technology is introduced. Since its commissioning over ten years ago, Baosteel＇ s CC process has made great progress. The construction...The status quo and future development trend of Baosteel continuous casting （CC） technology is introduced. Since its commissioning over ten years ago, Baosteel＇ s CC process has made great progress. The construction of Baosteel CC research and development base is also introduced. Two aspects of the future CC technology development in Baosteel are stressed. One is to follow the advanced CC technology and solve problems in real production, making full use of pilot plants, while the other is to integrate the present CC technology and make technical breakthroughs in engineering proiects.展开更多
The development of continuous casting technology of electrical steel was analyzed. The technologies and products characteristics of conventional continuous casting, thin slab continuous casting and rolling, middle thi...The development of continuous casting technology of electrical steel was analyzed. The technologies and products characteristics of conventional continuous casting, thin slab continuous casting and rolling, middle thin slab continuous casting and rolling and twin-roll thin strip were compared. Conventional continuous casting technology was widely adopted in producing electrical steel, thin slab continuous casting and rolling and middle thin slab contin- uous casting and roiling technology industrialized electrical steel~ and study of twin-roll thin strip casting technology was focused on fundamental experiments.展开更多
Based on the characteristics of Thin slab casting and rolling (TSCR) process,using test methods such as SEM,EDS and measuring content of inclusions, the influencing factor of controlling inclusions during producing mi...Based on the characteristics of Thin slab casting and rolling (TSCR) process,using test methods such as SEM,EDS and measuring content of inclusions, the influencing factor of controlling inclusions during producing middle and high carbon steel was studied. The technologies of electric furnace smelting, LF refining and controlling inclusions of tundish were proposed. The inclusions control level of middle and high carbon steel in which the carbon content is 0.3-1.0%, The level reached and even exceeded the level of like product producing with conventional process at home and abroad.展开更多
基金funded by National Natural Science Foundation of China(51274155)Provincial Natural Science Foundation of Hubei Province of China(2014CFB819)
文摘A grain-oriented silicon steel strip with AlN as main inhibitor was produced by thin slab casting and rolling（TSCR）process.The microstructure,texture and precipitates of the hot-rolled strip were investigated by use of optical microscope（OM）,X-ray diffractometer,transmission electron microscope（TEM）and energy dispersive spectroscope（EDS）.The result shows that the microstructure and texture exhibit a through-thickness gradient similar to that of the hot-rolled strip produced by conventional high-temperature slab-reheating process;the preferred orientation varies from {110}〈001〉in the surface layer to{001}〈110〉in the center layer,and the Goss texture with a maximum intensity mainly concentrates on the surface layer.In addition,some other texture components,for example rotated Goss texture,form in the 1/4thickness layer,which are not observed in the hotrolled strip produced by conventional high-temperature slab-reheating process.The precipitates in the hot-rolled strip are mainly（Mn,Cu）S and AlN compound particles with dimension of 100-200 nm,and the fine precipitates are significantly less than that in the hot-rolled strip produced by conventional high-temperature slab-reheating process.Moreover,the areal density of the fine precipitates in the center layer is more than that in the surface layer.
文摘The status quo and future development trend of Baosteel continuous casting （CC） technology is introduced. Since its commissioning over ten years ago, Baosteel＇ s CC process has made great progress. The construction of Baosteel CC research and development base is also introduced. Two aspects of the future CC technology development in Baosteel are stressed. One is to follow the advanced CC technology and solve problems in real production, making full use of pilot plants, while the other is to integrate the present CC technology and make technical breakthroughs in engineering proiects.
文摘The development of continuous casting technology of electrical steel was analyzed. The technologies and products characteristics of conventional continuous casting, thin slab continuous casting and rolling, middle thin slab continuous casting and rolling and twin-roll thin strip were compared. Conventional continuous casting technology was widely adopted in producing electrical steel, thin slab continuous casting and rolling and middle thin slab contin- uous casting and roiling technology industrialized electrical steel~ and study of twin-roll thin strip casting technology was focused on fundamental experiments.
文摘Based on the characteristics of Thin slab casting and rolling (TSCR) process,using test methods such as SEM,EDS and measuring content of inclusions, the influencing factor of controlling inclusions during producing middle and high carbon steel was studied. The technologies of electric furnace smelting, LF refining and controlling inclusions of tundish were proposed. The inclusions control level of middle and high carbon steel in which the carbon content is 0.3-1.0%, The level reached and even exceeded the level of like product producing with conventional process at home and abroad.