Conductive and corrosion behaviors of silver-doped carbon-coated stainless steel as PEMFC bipolar plates

Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316 L substrate. The corrosion resistance of this film in 0.5 mol·L^（-1） H_2SO_4 solution containing 5 ppm F- at 80°C was investigated using polarization tests. The results showed that the surface treatment of the SS316 L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316 L, the Ag-doped carbon-coated SS316 L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell（PEMFC） and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 m？·cm^2 to 21.6 m？·cm^2 at a compaction pressure of 1.2 MPa.

Preparation of silver-coated glass frit and its application in silicon solar cells

A simple electroless plating process was employed to prepare silver-coated glass frits for solar cells. The surface of the glass frits was modified with polyvinyl-pyrrolidone（PVP） before the electroless plating process. Infrared（IR） spectroscopy,field emission scanning electron microscopy（FESEM）, and x-ray diffraction（XRD） were used to characterize the PVP modified glass frits and investigate the mechanism of the modification process. It was found that the PVP molecules adsorbed on the glass frit surface and reduced the silver ions to the silver nanoparticles. Through epitaxial growth, these nanoparticles were uniformly deposited onto the surface of the glass frit. Silicon solar cells with this novel silver coating exhibited a photoelectric conversion efficiency increase of 0.33%. Compared with the electroless plating processes, this method provides a simple route to prepare silver-coated glass frits without introducing impurity ions.

The Membrane-Associated Sec1/Munc18 KEULE is Required for Phragmoplast Microtubule Reorganization During Cytokinesis in Arabidopsis

Cytokinesis, the partitioning of the cytoplasm following nuclear division, requires extensive coordination between membrane trafficking and cytoskeletal dynamics. In plants, the onset of cytokinesis is characterized by the assembly of a bipolar microtubule array, the phragmoplast, and of a transient membrane compartment, the cell plate. Little is known about the coordination between membrane deposition at the cell plate and the dynamics of phragmoplast microtubules. In this study, we monitor the localization dynamics of microtubule and membrane markers throughout cytokinesis. Our spatiotemporal resolution is consistent with the general view that microtubule dynamics drive membrane movements. Nonetheless, we provide evidence for active sorting at the cell plate and show that this is, at least in part, mediated by the TRAPPII tethering complex. We also characterize phragmoplast microtubule organization and cell plate formation in a suite of cytokinesis-defective mutants. Of four mutant lines with defects in phragmoplast microtubule organization, only morl microtubule-associated mutants exhibited aberrant cell plates. Conversely, the mutants with the strongest impairment in phragmoplast microtubule reorganization are keule alleles, which have a primary defect in membrane fusion. Our findings identify the SEC1/Munc18 protein KEULE as a central regulatory node in the coordination of membrane and microtubule dynamics during plant cytokinesis.