Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hyd...Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hydration products in the cement pastes modified by HEMC and HPMC in this article.The results show that the hydration products in modified cement pastes were finally identical with those in the unmodified cement paste,but the major hydration products,such as CH（calcium hydroxide）,ettringite and C-S-H,appeared later in the modified cement pastes than in the unmodified cement paste.The cellulose ethers decrease the outer products and increase inner products of C-S-H gels.Compared to unmodified cement pastes,no new products are found in the modified cement pastes in the present experiment.The HEMC and HPMC investigation shows almost the same influence on the hydration products of Portland cement.展开更多
Main performance of the cement grouting materials made up by Portland cement（PC） and sulphoaluminate cement（SAC） was investigated in this program, a kind of expanding agent（EA） which was mainly constituted by me...Main performance of the cement grouting materials made up by Portland cement（PC） and sulphoaluminate cement（SAC） was investigated in this program, a kind of expanding agent（EA） which was mainly constituted by metakaolin and alunite was utilized for the compensation of the shrinkage, the hydration products and micro structure of the grouting materials were researched by X-ray diffraction（XRD） and scanning electron microscopy（SEM）. The results showed that a high expansion rate of the grouting materials could be reached as the expanding agent mixed in 6% of PC mass; the addition of SAC in the S2（PC：SAC：EA=34：6：2.25） brought a further improvement of the expansion rate of the grouting materials, the analysis of XRD and SEM showed that due to the reaction of expanding agent and SAC in the grouting materials, more ettringite crystal was generated, which resulted in a higher early strength, the addition of SAC played an expansion and strength reinforcement role in the grouting materials.展开更多
基金Funded by Youth Fund of National Natural Science Foundation of China(No.50902107)the 973 Program(No.2009CB623201)from Ministry of Science and Technology of Chinathe Fundamental Research Funds for the Central Universities
文摘Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hydration products in the cement pastes modified by HEMC and HPMC in this article.The results show that the hydration products in modified cement pastes were finally identical with those in the unmodified cement paste,but the major hydration products,such as CH（calcium hydroxide）,ettringite and C-S-H,appeared later in the modified cement pastes than in the unmodified cement paste.The cellulose ethers decrease the outer products and increase inner products of C-S-H gels.Compared to unmodified cement pastes,no new products are found in the modified cement pastes in the present experiment.The HEMC and HPMC investigation shows almost the same influence on the hydration products of Portland cement.
基金Funded by the National Key Technology R&D Program in the12th Five Year Plan of China(No.2011BAE14B06)the National High Technology ResearchDevelopment Program of China(No.2015AA034701)
文摘Main performance of the cement grouting materials made up by Portland cement（PC） and sulphoaluminate cement（SAC） was investigated in this program, a kind of expanding agent（EA） which was mainly constituted by metakaolin and alunite was utilized for the compensation of the shrinkage, the hydration products and micro structure of the grouting materials were researched by X-ray diffraction（XRD） and scanning electron microscopy（SEM）. The results showed that a high expansion rate of the grouting materials could be reached as the expanding agent mixed in 6% of PC mass; the addition of SAC in the S2（PC：SAC：EA=34：6：2.25） brought a further improvement of the expansion rate of the grouting materials, the analysis of XRD and SEM showed that due to the reaction of expanding agent and SAC in the grouting materials, more ettringite crystal was generated, which resulted in a higher early strength, the addition of SAC played an expansion and strength reinforcement role in the grouting materials.