In order to improve the high temperature oxidation resistance of TiAl alloy, Y modified silicide coatings were prepared by pack cementation process at 1030, 1080 and 1130 °C, respectively, for 5 h. The microstruc...In order to improve the high temperature oxidation resistance of TiAl alloy, Y modified silicide coatings were prepared by pack cementation process at 1030, 1080 and 1130 °C, respectively, for 5 h. The microstructures, phase constitutions and oxidation behavior of these coatings were studied. The results show that the coating prepared by co-depositing Si?Y at 1080 °C for 5 h has a multiple layer structure: a superficial zone consisting of Al-rich (Ti,Nb)5Si4 and (Ti,Nb)5Si3, an out layer consisting of (Ti,Nb)Si2, a middle layer consisting of (Ti,Nb)5Si4 and (Ti,Nb)5Si3, and aγ-TiAl inner layer. Co-deposition temperature imposes strong influences on the coating structure. The coating prepared by Si?Y co-depositing at 1080 °C for 5 h shows relatively good oxidation resistance at 1000 °C in air, and the oxidation rate constant of the coating is about two orders of magnitude lower than that of the bare TiAl alloy.展开更多
This article investigates the low-temperature formation of aluminide coatings on a Ni-base superalloy by pack cementation process. The pack cemented coatings characteristic of high density and homogeneity possess a tw...This article investigates the low-temperature formation of aluminide coatings on a Ni-base superalloy by pack cementation process. The pack cemented coatings characteristic of high density and homogeneity possess a two-layer structure. The top layer mainly consists of Al3Ni2 and Al3Ni,while the bottom layer of Al3Ni2. Great efforts are made to elucidate the effects of different experimental parameters on the microstructure and the constituent distribution of the coatings. The results show that all the parameters exclusive of the pack activator （NH4Cl） content produce effect on the coating thickness,but do not on the microstructure and the constituent distribution. The pack activator （NH4Cl） content affects neither the coating thickness nor structure and constituent distribution. The parabolic relationship between the coating thickness and the deposition time suggests that the process is diffusion-controlled. Furthermore,the article demonstrates a linear relationship between the coating thickness and the re-ciprocal deposition temperature.展开更多
基金Project(2014JZ012)supported by the Natural Science Program for Basic Research in Key Areas of Shaanxi Province,China
文摘In order to improve the high temperature oxidation resistance of TiAl alloy, Y modified silicide coatings were prepared by pack cementation process at 1030, 1080 and 1130 °C, respectively, for 5 h. The microstructures, phase constitutions and oxidation behavior of these coatings were studied. The results show that the coating prepared by co-depositing Si?Y at 1080 °C for 5 h has a multiple layer structure: a superficial zone consisting of Al-rich (Ti,Nb)5Si4 and (Ti,Nb)5Si3, an out layer consisting of (Ti,Nb)Si2, a middle layer consisting of (Ti,Nb)5Si4 and (Ti,Nb)5Si3, and aγ-TiAl inner layer. Co-deposition temperature imposes strong influences on the coating structure. The coating prepared by Si?Y co-depositing at 1080 °C for 5 h shows relatively good oxidation resistance at 1000 °C in air, and the oxidation rate constant of the coating is about two orders of magnitude lower than that of the bare TiAl alloy.
文摘This article investigates the low-temperature formation of aluminide coatings on a Ni-base superalloy by pack cementation process. The pack cemented coatings characteristic of high density and homogeneity possess a two-layer structure. The top layer mainly consists of Al3Ni2 and Al3Ni,while the bottom layer of Al3Ni2. Great efforts are made to elucidate the effects of different experimental parameters on the microstructure and the constituent distribution of the coatings. The results show that all the parameters exclusive of the pack activator （NH4Cl） content produce effect on the coating thickness,but do not on the microstructure and the constituent distribution. The pack activator （NH4Cl） content affects neither the coating thickness nor structure and constituent distribution. The parabolic relationship between the coating thickness and the deposition time suggests that the process is diffusion-controlled. Furthermore,the article demonstrates a linear relationship between the coating thickness and the re-ciprocal deposition temperature.