The effects of four sand contents on the compressive, flexural and splitting-tensile strength of cement mortars were evaluated. Moreover, we experimentally investigated the pore structure of cement mortar brought abou...The effects of four sand contents on the compressive, flexural and splitting-tensile strength of cement mortars were evaluated. Moreover, we experimentally investigated the pore structure of cement mortar brought about by changing the sand content and water/cement ratio. The changes in the pore structure were quantified by measuring the porosity and pore size distribution obtained by using mercury intrusion porosimetry（MIP） technique. The test results show that the strengths of cement mortar increase with increasing sand content. It is also suggested that the traditional water/cement ratio law can be applied to cement mortar with different sand contents, provided that a slight modification is introduced. Sand content is an important parameter influencing the pore structure of cement mortar. Moreover, there is a good relationship between the pore structure and strength of cement mortar.展开更多
Oyster shell powder was used as the admixture of ordinary portland cement.The effects of different addition amounts and grinding ways on the strength and stability of cement mortar were discussed and proper addition a...Oyster shell powder was used as the admixture of ordinary portland cement.The effects of different addition amounts and grinding ways on the strength and stability of cement mortar were discussed and proper addition amount of oyster shell powder was determined.The structure and property changes of cementing samples with different oyster shell powder contents were tested by XRD and SEM means.The results revealed that compressive and rupture strengths of the sample with 10% oyster shell powder was close to those of the original one without addition.Stability experiment showed that the sample prepared by pat method had smooth surface without crack and significant expansion or shrinkage after pre-curing and boiling,which indicated that cementing material dosed with oyster shell powder had fine stability.XRD and SEM observation showed that oyster shell independently exists in the cementing material.展开更多
基金Founded by the National Natural Science Foundation of China(Nos.51279054 and 51279052)
文摘The effects of four sand contents on the compressive, flexural and splitting-tensile strength of cement mortars were evaluated. Moreover, we experimentally investigated the pore structure of cement mortar brought about by changing the sand content and water/cement ratio. The changes in the pore structure were quantified by measuring the porosity and pore size distribution obtained by using mercury intrusion porosimetry（MIP） technique. The test results show that the strengths of cement mortar increase with increasing sand content. It is also suggested that the traditional water/cement ratio law can be applied to cement mortar with different sand contents, provided that a slight modification is introduced. Sand content is an important parameter influencing the pore structure of cement mortar. Moreover, there is a good relationship between the pore structure and strength of cement mortar.
基金Supported by the National Natural Science Foundation of China (No. 51102047)Fujian Provincial of Science and Technology (2011Y0037)Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry SRF for ROCS,SEM
文摘Oyster shell powder was used as the admixture of ordinary portland cement.The effects of different addition amounts and grinding ways on the strength and stability of cement mortar were discussed and proper addition amount of oyster shell powder was determined.The structure and property changes of cementing samples with different oyster shell powder contents were tested by XRD and SEM means.The results revealed that compressive and rupture strengths of the sample with 10% oyster shell powder was close to those of the original one without addition.Stability experiment showed that the sample prepared by pat method had smooth surface without crack and significant expansion or shrinkage after pre-curing and boiling,which indicated that cementing material dosed with oyster shell powder had fine stability.XRD and SEM observation showed that oyster shell independently exists in the cementing material.