Comparative experimental investigation of chemical grouting into a fracture with flowing and static water

We present a series of experimental tests on chemical grouting into a fracture with flowing and static water,using a transparent fracture grouting experimental device.Variations of seepage pressure and grout propagation were compared in our investigation.The results show that flowing water results in drops of seepage pressure,development of penetration radii in the upstream side and drops of propagation area during the same period,compared with grouting in static water.The propagation area in static water is always round before grouts reach the joint boundaries.However,the propagation shape changes from round to an elliptic shape for grouting into a fracture with flowing water.A theoretical model for the grout penetration radius in a fracture considering flowing velocity was developed and validated by our experimental results.These results are helpful in improving understanding of fracture grouting mechanism and in guiding engineering practices.

Strength of copolymer grouting material based on orthogonal experiment

Using the orthogonal experimental design method involving three factors and three levels, the flexural strength and the compressive strength of copolymer grouting material were studied with different compositions of water-cement ratio （mass fraction of water to cement）, epoxy resin content, and waterborne epoxy curing agent content. By orthogonal range and variance analysis, the orders of three factors to influence the strength, the significance levels of different factors, and the optimized compound ratio scheme of copolymer grouting material mixture at different curing ages were determined. An empirical relationship among the strength of copolymer grouting material, the water-cement ratio, the epoxy resin content, and the waterborne epoxy curing agent content was established by multivariate regression analysis. The results indicate that water-cement ratio is the most principal and significant influencing factor on the strength. Epoxy resin content and waterbome epoxy curing agent content also have a significant influence on the strength. But epoxy resin content has a greater influence on the 7-day and 28-day flexural strength, and waterborne epoxy curing agent content has a greater influence on the 3-day flexural strength and the compressive strength. The copolymer grouting material with water-cement ratio of 0.4, epoxy resin content of 8% （mass fraction） and waterbome epoxy curing agent content of 2% （mass fraction） is the best one for repairing of cement concrete pavement. The flexural strength and the compressive strength have good correlation, and the ratio of compressive strength to flexural strength is between 1.0 and 3.3.

Gel time of calcium acrylate grouting material

Calcium acrylate is a polymerized grout, and can polymerize in an aqueous solution. The polymerization reaction utilizes ammonium persulfate as a catalyst and sodium thiosulfate as the activator. Based on the theory of reaction kinetics, this study on the relation between gel time and concentration of activator and catalyst showed that gel time of calcium acrylate is inversely proportional to activator and catalyst concentration. A formula of gel time is proposed, and an example is provided to verify the proposed formula.

Chemical grout diffusion in porous rock based on response of geoelectric feld

Porous rock chemical grouting simulation test was conducted using established large scale physical model.Chemical grout diffusing rule in porous media with different permeability was studied by monitoring the spontaneous potential and exciting current response during grouting.The results show that chemical grout spread evenly in all directions and diffusion areas are approximately concentric circles in the cross section of homogeneous transverse isotropic pore medium,the grout spread flling range can be quantitatively decrypted by the diffusion radius.The average diffusion speed and radius increase approximately as the square root with the permeability coeffcient in different permeability media under the same conditions.Calculation results using Maag cylindrical diffusion equation show that the calculated value of diffusion radius is in good agreement with the test value under different grouting pressures and permeability conditions.