Experimental Study on the Chloride Ion Concentration of Cement Pastes Prepared with Limestone Powder

To investigate the impact of limestone powder on the chloride ion concentration coefficient of cement pastes,various techniques such as scanning electron microscopy(SEM),X-ray diffraction(XRD),thermogravimetric analysis(TGA),and mercury-porosimetry(MIP)were employed in this paper.The findings demonstrate that the creation of Friedel's salt is inversely associated with the addition of limestone powder,that is,Friedel's salt production is lessened by adding more limestone powder,however,the coefficient of chloride ion concentration initially decreased and then increased again,as does the porosity,and most likely the pore size as well.The specific surface area of limestone powder has increased,and the content of Friedel’s salt increased first and then decreased.However,the shifting trend of Friedel's salt and chloride ion concentration coefficient is in direct opposition,and the pore structure was therefore significantly enhanced.The results of this study offer robust theoretical backing for the inclusion of limestone powder in concrete and provide a positive assessment of its potential applications.

Influence of chloride ion concentration on immersion corrosion behaviour of plasma sprayed alumina coatings on AZ31B magnesium alloy

Corrosion attack of aluminium and magnesium based alloys is a major issue worldwide.The corrosion degradation of an uncoated and atmospheric plasma sprayed alumina(APS)coatings on AZ31B magnesium alloy was investigated using immersion corrosion test in NaCl solutions of different chloride ion concentrations viz.,0.01 M,0.2 M,0.6 M and 1 M.The corroded surface was characterized by an optical microscope and X-ray diffraction.The results showed that the corrosion deterioration of uncoated and coated samples were significantly influenced by chloride ion concentration.The uncoated magnesium and alumina coatings were found to offer a superior corrosion resistance in lower chloride ion concentration NaCl solutions(0.01 M and 0.2 M NaCl).On the other hand the coatings and Mg alloy substrate were found to be highly susceptible to localized damage,and could not provide an effective corrosion protection in solutions containing higher chloride concentrations(0.6 M and 1 M).It was found that the corrosion resistance of the ceramic coatings and base metal gets deteriorated with the increase in the chloride concentrations.

The Combined Impact of Magnetic Field and Chloride Ion Concentration on Corrosion Behavior of Al-Mg Alloys

The impact of magnetic field on the corrosion behavior of Al-Mg-xR_(E)/Fe alloys in NaCl solutions with concentrations of 1.5wt%,3.5wt%,and 5.5wt%were studied by microstructure observation,immersion test,and electrochemical test.The combined impacts of magnetic field and chloride ion concentration on the corrosion behavior of Al-Mg alloys with various electrode potential phases were discussed.The results indicate that Al-3.0Mg-xR_(E)/Fe alloys corrode faster and have a higher pitting corrosion potential in the NaCl solution with a higher concentration.In addition,a magnetic field can lower the pitting sensitivity and corrosion rate of Al-3.0Mg and Al-3.0Mg-0.2R_(E)/Fe alloys in NaCl solution with different concentrations.However,at a higher concentration of NaCl solution,the magnetic field has a weaker inhibiting effect on corrosion rate and pitting sensitivity.In NaCl solutions with concentrations of 1.5wt%and 3.5wt%,the corrosion rate and pitting sensitivity of Al-3.0Mg-1.0R_(E)/Fe alloys can be reduced by a magnetic field.However,in NaCl solution with the concentration of 5.5wt%,the corrosion rate of the alloys is increased by a magnetic field.

Corrosion behavior of micro-arc oxidation coating on AZ91D magnesium alloy in NaCl solutions with different concentrations

Ceramic oxide coatings were prepared on AZ91D magnesium alloys in alkaline silicate solution using micro-arc oxidation（MAO） technique.The corrosion behavior of MAO coating on AZ91D magnesium alloys in NaCl solutions with different concentrations（0.1%,0.5%,1.0%,3.5% and 5.0% in mass fraction） was evaluated by electrochemical measurements and immersion tests.The results showed that the corrosion rate of the MAO coated AZ91D increased with increasing chloride ion concentration.The main form of corrosion failure was localized corrosion for the MAO coated AZ91D immersed in higher concentration NaCl solutions（1.0%,3.5% and 5.0%）,while it was general corrosion in dilute NaCl solutions（0.1% and 0.5%）.Two different stages of the failure process of the MAO coated AZ91D could be identified：1） occurrence of the metastable pits and 2） growth of the pits.Different equivalent circuits were also proposed based on the results of electrochemical impedance spectroscopy（EIS） for the MAO coated AZ91D immersed in different concentrations of NaCl solutions for 120 h.