The magnesia composite materials were prepared using fused magnesia, used magnesia chrome bricks, magnesium aluminate spinel, alumina powder and chrome oxide powder as starting materials. In order to improve the perfo...The magnesia composite materials were prepared using fused magnesia, used magnesia chrome bricks, magnesium aluminate spinel, alumina powder and chrome oxide powder as starting materials. In order to improve the performance of magnesia composite material, the influence of chrome oxide concentrate powder on the properties of magnesia composite material was re-searched. The apparent porosity, bulk density, cold crushing streugth, linear expausion and thermal shock resistance of the specimens were determined. The results show that adding chrome oxide concentrate promotes the formation of the composite phases of three kinds of spi-nel, which is beneficial to the thermal shock resistance.The magnesia chrome spbwl can not be .[brined at high temperatures theoreticalby, but can dissolve in the mag-nesia composite material. Comprehensively, the optimal addition of chrome oxide concentrate is 10. 0 mass% for the magnesia composite materials.展开更多
To meet the needs of environmental protection and promote the application of chromium-free refractories for RH refining furnaces, research on application of new non-burned periclase-magnesia alumina spinel bricks was ...To meet the needs of environmental protection and promote the application of chromium-free refractories for RH refining furnaces, research on application of new non-burned periclase-magnesia alumina spinel bricks was carried out. Through laboratory research and field application, it is concluded that the non-burned periclase-magnesia alumina spinel brick can replace magnesia-chrome material, and its service life is equivalent to that of the magnesia-chrome material with reduced cost.展开更多
The research progress and industrial application of chrome-free refractories for RH degasser were introduced in the paper.It is proved that unburned magnesia-spinel refractories used for RH throat and snorkel in Baost...The research progress and industrial application of chrome-free refractories for RH degasser were introduced in the paper.It is proved that unburned magnesia-spinel refractories used for RH throat and snorkel in Baosteel have longer service life compared with traditional direct bonded fused magnesia-chrome materials.The new developed chrome-free unburned magnesia-spinel composite can fully meet the present demand for RH operation and can be applied extensively for RH processing.At present,instead of chrome-containing materials,chrome-free refractories have been applied widely for RH in Baosteel.Super low carbon MgO-C material with high mechanical properties at mild and high temperatures can be an alternative chrome-free material for RH.展开更多
Chrame containing refractories are a kind of traditional material for the lining of alkali recovery furnaces, but the formation of hexavalent chrome compounds will give rise to detrimental effect on environment and hu...Chrame containing refractories are a kind of traditional material for the lining of alkali recovery furnaces, but the formation of hexavalent chrome compounds will give rise to detrimental effect on environment and human＇s health. With the gradual awakening of people＇s comciousness about environment protection, it is urgent to prepare environmental-friendly materials for alkali recovery jurnaces with high quality and long life. In this paper, alumina-rich MgAl2O4 spinel （ AR90 ） was used to replace chromite. The physical properties of dried （110 ℃ for 24 h） or fired （1 300 ℃ for 3 h） AR90 and chromite were studied, respectively. The alkali vapor method was used to determine the alkali resistance of the two materials. The results show that： （1） after drying at 110 ℃ for 24 h, AR90 specimens show higher apparent porosity and slightly lower bulk density than chromite specimens; after firing at 1 300 ℃ for 3 h, AR90 has significantly higher apparent porosity as well as higher bulk density; （2） after the alkali attack, the AR90 specimens sintered at 1 300 ℃ exhibit smaller strength change and much higher compressive strength than the chromite specimens; meanwhile, the permeability degree of alkali salt in chromite specimens is more serious than that in AR90 specimens, which indicates that AR90 possesses better alkali resistance.展开更多
基金supported by the Industrial Special Resource Protecting Office of Liaoning Province
文摘The magnesia composite materials were prepared using fused magnesia, used magnesia chrome bricks, magnesium aluminate spinel, alumina powder and chrome oxide powder as starting materials. In order to improve the performance of magnesia composite material, the influence of chrome oxide concentrate powder on the properties of magnesia composite material was re-searched. The apparent porosity, bulk density, cold crushing streugth, linear expausion and thermal shock resistance of the specimens were determined. The results show that adding chrome oxide concentrate promotes the formation of the composite phases of three kinds of spi-nel, which is beneficial to the thermal shock resistance.The magnesia chrome spbwl can not be .[brined at high temperatures theoreticalby, but can dissolve in the mag-nesia composite material. Comprehensively, the optimal addition of chrome oxide concentrate is 10. 0 mass% for the magnesia composite materials.
文摘To meet the needs of environmental protection and promote the application of chromium-free refractories for RH refining furnaces, research on application of new non-burned periclase-magnesia alumina spinel bricks was carried out. Through laboratory research and field application, it is concluded that the non-burned periclase-magnesia alumina spinel brick can replace magnesia-chrome material, and its service life is equivalent to that of the magnesia-chrome material with reduced cost.
文摘The research progress and industrial application of chrome-free refractories for RH degasser were introduced in the paper.It is proved that unburned magnesia-spinel refractories used for RH throat and snorkel in Baosteel have longer service life compared with traditional direct bonded fused magnesia-chrome materials.The new developed chrome-free unburned magnesia-spinel composite can fully meet the present demand for RH operation and can be applied extensively for RH processing.At present,instead of chrome-containing materials,chrome-free refractories have been applied widely for RH in Baosteel.Super low carbon MgO-C material with high mechanical properties at mild and high temperatures can be an alternative chrome-free material for RH.
文摘Chrame containing refractories are a kind of traditional material for the lining of alkali recovery furnaces, but the formation of hexavalent chrome compounds will give rise to detrimental effect on environment and human＇s health. With the gradual awakening of people＇s comciousness about environment protection, it is urgent to prepare environmental-friendly materials for alkali recovery jurnaces with high quality and long life. In this paper, alumina-rich MgAl2O4 spinel （ AR90 ） was used to replace chromite. The physical properties of dried （110 ℃ for 24 h） or fired （1 300 ℃ for 3 h） AR90 and chromite were studied, respectively. The alkali vapor method was used to determine the alkali resistance of the two materials. The results show that： （1） after drying at 110 ℃ for 24 h, AR90 specimens show higher apparent porosity and slightly lower bulk density than chromite specimens; after firing at 1 300 ℃ for 3 h, AR90 has significantly higher apparent porosity as well as higher bulk density; （2） after the alkali attack, the AR90 specimens sintered at 1 300 ℃ exhibit smaller strength change and much higher compressive strength than the chromite specimens; meanwhile, the permeability degree of alkali salt in chromite specimens is more serious than that in AR90 specimens, which indicates that AR90 possesses better alkali resistance.