Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microsco...Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microscopy （SEM） equipped with energy-dispersive spectroscopy （EDS）, as well as the thermodynamic software FactSage 6.2, were used for sample characterization. The results show that the addition of FeO can decrease the viscosity of molten slag and the precipitation temperatures of melilite and merwinite. The solidus temperature significantly decreases from 1400 to 1250℃ with the increase of FeO content from 0wt% to 6wt%. The addition of FeO could enhance the content of Cr in spinel phases and reduce the content of Cr in soluble minerals, such as merwinite, melilite, and dicalcium silicate. Hence, the addition of FeO is conducive to decreasing Cr leaching.展开更多
Regular spherical chromium doped spinel lithium manganese oxides （LiCr0.04Mn1.96O4） with an average particle size of about 20μm were prepared by the slurry spray drying process. The materials were compared with non...Regular spherical chromium doped spinel lithium manganese oxides （LiCr0.04Mn1.96O4） with an average particle size of about 20μm were prepared by the slurry spray drying process. The materials were compared with non-spherical LiCr0.04Mnl.96O4 materials prepared by the common drying process, and all materials were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, laser particle analyzer and Brunaner-Emmett-Teller （BET） specific surface area test. Electrochemical performances of these cathode materials were studied by cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and Li/LiCr0.04Mn1.9604 battery test. The results show that the spherical active material is single spinel structure, compact, and with narrow particle size distribution and low BET specific surface area. Compared with the non-spherical material, the spherical material prepared by the spray drying process shows a lower electrochemical impedance, a fewer electrochemical polarization and a better charge/discharge rate capability and capacity retention at elevated temperatures.展开更多
To improve the efficiency of melting modification for stainless steel(SS) slag, a shear force was introduced in this work and its effects on the spinel and silicate melt were experimentally investigated. The results i...To improve the efficiency of melting modification for stainless steel(SS) slag, a shear force was introduced in this work and its effects on the spinel and silicate melt were experimentally investigated. The results indicated that the use of shear force changed the nucleation and growth behaviors of spinel and that the effects of shear force varied with its intensity. The aggregation behavior of spinel under different shear-force conditions was studied, revealing that large spinel clusters could be formed when the stirring speed was controlled. However, no notable change in the melt structure of the silicate was detected in this study. The optimal stirring speed for the melting modification treatment was 50 r·min^(-1), which substantially promoted spinel growth and aggregation, resulting in modified SS slag with excellent chromium sequestration capability.展开更多
Terahertz(THz)time-domain spectroscopy(THz-TDS)of polycrystalline MnCr_(2)O_(4)was performed at<9 T and low temperatures.A resonance absorption in the sub-THz range with linear blueshifts was observed as the magnet...Terahertz(THz)time-domain spectroscopy(THz-TDS)of polycrystalline MnCr_(2)O_(4)was performed at<9 T and low temperatures.A resonance absorption in the sub-THz range with linear blueshifts was observed as the magnetic field was increased from 4 T to 9 T.These magnetism-driven absorptions originated from a ferromagnetic resonance,which agrees with low-field electron spin resonance measurements and ferromagnetic resonance theory.The low-temperature g-factors of MnCr_(2)O_(4)were also obtained using THz-TDS.This work provides new insights into the spin dynamics of chromite spinel compounds in the THz region.展开更多
基金the Chinese Scholarship Council for financial support
文摘Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microscopy （SEM） equipped with energy-dispersive spectroscopy （EDS）, as well as the thermodynamic software FactSage 6.2, were used for sample characterization. The results show that the addition of FeO can decrease the viscosity of molten slag and the precipitation temperatures of melilite and merwinite. The solidus temperature significantly decreases from 1400 to 1250℃ with the increase of FeO content from 0wt% to 6wt%. The addition of FeO could enhance the content of Cr in spinel phases and reduce the content of Cr in soluble minerals, such as merwinite, melilite, and dicalcium silicate. Hence, the addition of FeO is conducive to decreasing Cr leaching.
基金supported by the National High-Tech Research and Development Program of China(No.2006AA11A160)
文摘Regular spherical chromium doped spinel lithium manganese oxides （LiCr0.04Mn1.96O4） with an average particle size of about 20μm were prepared by the slurry spray drying process. The materials were compared with non-spherical LiCr0.04Mnl.96O4 materials prepared by the common drying process, and all materials were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, laser particle analyzer and Brunaner-Emmett-Teller （BET） specific surface area test. Electrochemical performances of these cathode materials were studied by cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and Li/LiCr0.04Mn1.9604 battery test. The results show that the spherical active material is single spinel structure, compact, and with narrow particle size distribution and low BET specific surface area. Compared with the non-spherical material, the spherical material prepared by the spray drying process shows a lower electrochemical impedance, a fewer electrochemical polarization and a better charge/discharge rate capability and capacity retention at elevated temperatures.
基金financially supported by the National Natural Science Foundation of China(No.51704068)the National Key Technologies R&D Program of China(No.2017YFC0805100)the Fundamental Research Funds for the Central Universities(No.N172504020)
文摘To improve the efficiency of melting modification for stainless steel(SS) slag, a shear force was introduced in this work and its effects on the spinel and silicate melt were experimentally investigated. The results indicated that the use of shear force changed the nucleation and growth behaviors of spinel and that the effects of shear force varied with its intensity. The aggregation behavior of spinel under different shear-force conditions was studied, revealing that large spinel clusters could be formed when the stirring speed was controlled. However, no notable change in the melt structure of the silicate was detected in this study. The optimal stirring speed for the melting modification treatment was 50 r·min^(-1), which substantially promoted spinel growth and aggregation, resulting in modified SS slag with excellent chromium sequestration capability.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.12174398 and 51727806)the Natural Science Research Project of the Education Department of Anhui Province,China(Grant No.KJ2021A0679)+1 种基金the Natural Science Foundation of Fuyang Normal University(Grant No.rcxm202107)the Cooperative Research Project of Fuyang Normal University and Fuyang Municipal Government(Grant No.SXHZ202012)。
文摘Terahertz(THz)time-domain spectroscopy(THz-TDS)of polycrystalline MnCr_(2)O_(4)was performed at<9 T and low temperatures.A resonance absorption in the sub-THz range with linear blueshifts was observed as the magnetic field was increased from 4 T to 9 T.These magnetism-driven absorptions originated from a ferromagnetic resonance,which agrees with low-field electron spin resonance measurements and ferromagnetic resonance theory.The low-temperature g-factors of MnCr_(2)O_(4)were also obtained using THz-TDS.This work provides new insights into the spin dynamics of chromite spinel compounds in the THz region.