The recovery of metal oxides from stainless steel dust using C（graphite）, SiFe, and Al as reductants was investigated under various conditions. The apparent distribution ratio of Cr（L Cr ′^m/s ） in the recovered ...The recovery of metal oxides from stainless steel dust using C（graphite）, SiFe, and Al as reductants was investigated under various conditions. The apparent distribution ratio of Cr（L Cr ′^m/s ） in the recovered metal and residual slag phases was defined as the major performance metric. The results show that the recovery ratio of metals increases as the ratio of CaO ：SiO2 by mass in the residual slag increases to 1.17. The residual content of metals in the slag decreases as the Al2O3 content of the slag is increased from approximately 8wt% to 10wt%. The recovery ratio of Cr increases with increasing L Cr ′^ m/s , and a linear relationship between L Cr ′^m/s and the activity coefficient ratio of CrO in the slag and the recovered metal phase is observed. The combination of C and SiFe or Al as the reducing agents reveals that Si is the more effective coreductant.展开更多
The dull-finish ferritic stainless steel （FSS） sheet B445R for architectural roofing has been developed by Baosteel. This steel product exhibits excellent corrosion resistance superior to that of SUS 316L with a low...The dull-finish ferritic stainless steel （FSS） sheet B445R for architectural roofing has been developed by Baosteel. This steel product exhibits excellent corrosion resistance superior to that of SUS 316L with a lower cost. It can be easily formed into roofing panels by ordinary processes. Moreover,the thermal strain of it is less than SUS 316L because of its lower thermal expansion coefficient, and its reflectivity is lower due to the dull-finish treatment. All of these features make it capable of being used as architectural roofing materials in coastal regions.展开更多
The corrosion of stainless steel was experimentally investigated and analyzed to improve the service-life of the crucible and fixture clamps. Through the experiment, stainless steel was found to satisfy the crucible a...The corrosion of stainless steel was experimentally investigated and analyzed to improve the service-life of the crucible and fixture clamps. Through the experiment, stainless steel was found to satisfy the crucible and fixture clamps materials. As the chromium element mass percentage of the stainless steel increased, the corrosion decreased rapidly at first and then slowly increased. With the corrosion time prolonging, the corrosion growth rate is generally a downward trend. With Chromium 20%, the corrosive were the least. With Nickel element mass percentage increased, the corrosion increased rapidly at first and then decreased rapidly, flatten at the last. It was special that the corrosion had little relationship with the Chromium and Nickel mass percentage when the Nickel percentage is more than 35%. The most remarkable corrosion is corresponding with the Nickel element 12%, the least corrosion with Nickel element 80%. So Nickel element 35% is the most optional.展开更多
The intergranular corrosion （IGC） behavior of high nitrogen austenitic stainless steel （HNSS） sensitization treated at 650-950℃ was investigated by the double loop electrochemical potentiodynamic reactivation （D...The intergranular corrosion （IGC） behavior of high nitrogen austenitic stainless steel （HNSS） sensitization treated at 650-950℃ was investigated by the double loop electrochemical potentiodynamic reactivation （DL-EPR） method. The effects of the electrolytes, scan rate, sensitizing temperature on the susceptibility to IGC of HNSS were examined. The results show that the addi-tion of NaCl is an effective way to improve the formation of the cracking of a passive film in chromium-depleted zones during the reactivation scan. Decreasing the scan rate exhibits an obvious effect on the breakdown of the passive film. A solution with 2 mol/L H2SO4＋1 mol/L NaCl＋0.01 mol/L KSCN is suitable to check the susceptibility to IGC of HNSS at a sensitizing temperature of 650-950℃ at a suitable scan rate of 1.667 mV/s. Chromium depletion of HNSS is attributed to the precipitation of Cr2N which results in the susceptibility to IGC. The synergistic effect of Mo and N is suggested to play an important role in stabilizing the passive film to prevent the attack of IGC.展开更多
Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microsco...Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microscopy （SEM） equipped with energy-dispersive spectroscopy （EDS）, as well as the thermodynamic software FactSage 6.2, were used for sample characterization. The results show that the addition of FeO can decrease the viscosity of molten slag and the precipitation temperatures of melilite and merwinite. The solidus temperature significantly decreases from 1400 to 1250℃ with the increase of FeO content from 0wt% to 6wt%. The addition of FeO could enhance the content of Cr in spinel phases and reduce the content of Cr in soluble minerals, such as merwinite, melilite, and dicalcium silicate. Hence, the addition of FeO is conducive to decreasing Cr leaching.展开更多
Spinel phase is considered to be the optimal phase for stabilization of chromium in stainless steel slag.In order to restrain chromium leaching from slag for the effective environmental protection,Al2O3 was utilized f...Spinel phase is considered to be the optimal phase for stabilization of chromium in stainless steel slag.In order to restrain chromium leaching from slag for the effective environmental protection,Al2O3 was utilized for the modification treatment,and the effects on the enrichment and stabilization of chromium were investigated. The mineral phases and the existence state of chromium in slag with various Al2O3 contents at different basicities（ w（CaO）/w（SiO2） were analyzed by scanning electron microscopy-energy dispersive spectroscopy（ SEM-EDS） and X-ray diffraction（ XRD）. The results showed that chromium mainly existed in the glass and spinel phases at basicity of 1. 0 and 1. 5. As the slag basicity increased to 2. 0,chromium was also found in periclase phase. Al2O3 in the stainless steel slag reacted with MgO and Cr2O3,which could generate the Al-rich Mg（CrxAl（1- x））2O4 solid solution. Moreover,the addition of Al2O3 was favorable to reduce the solubility of chromium oxide in liquid phase and suppress the precipitation of periclase phase. The experimental results demonstrated that Al2O3 modification has a positive influence on the enrichment and the stabilization of chromium in the stainless steel slag.展开更多
The leaching of chromium from stainless steel dust （SSD） is deleterious to the environment. To address this issue, the reduction of SSD briquettes can be employed to effectively extract chromium. The recovery rates ...The leaching of chromium from stainless steel dust （SSD） is deleterious to the environment. To address this issue, the reduction of SSD briquettes can be employed to effectively extract chromium. The recovery rates of iron, chromium, and nickel via ironbath reduction of SSD briquettes were determined using X-ray fluorescence spectroscopy, X-ray diffraction, and scanning electron microscopy measurements. First, the effects of basicity and contents of silicon, iron, CaF2, and carbon on the recovery rates of the three metals were analyzed using the slag amount prediction model, which was originally established from the A1203 balance of corundum crucible erosion behavior. Second, the effect of feeding mode, i.e., whether steel scrap and SSD briquettes were simultaneously added, on the recovery rates was discussed in detail. Third, the iron-bath reduction of SSD briquettes was thermodynamically analyzed. The results indicated that the recovery rates of the three metals are greater than 95% those of using a basicity of 1.5 and 6.0% CaF2, 15% carbon, and 7% ferrosilicon. The recovery rate of chromium increases twofold with the addition of ferrosilicon. The feeding mode of adding briquettes and steel scrap simultaneously is better for recovery of metals and separation of the metal and slag than the feeding mode of adding steel scrap firstly and then briquettes.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51474021)the Fundamental Research Funds for the Central Universities of China (No. FRF-SD-12-009A)
文摘The recovery of metal oxides from stainless steel dust using C（graphite）, SiFe, and Al as reductants was investigated under various conditions. The apparent distribution ratio of Cr（L Cr ′^m/s ） in the recovered metal and residual slag phases was defined as the major performance metric. The results show that the recovery ratio of metals increases as the ratio of CaO ：SiO2 by mass in the residual slag increases to 1.17. The residual content of metals in the slag decreases as the Al2O3 content of the slag is increased from approximately 8wt% to 10wt%. The recovery ratio of Cr increases with increasing L Cr ′^ m/s , and a linear relationship between L Cr ′^m/s and the activity coefficient ratio of CrO in the slag and the recovered metal phase is observed. The combination of C and SiFe or Al as the reducing agents reveals that Si is the more effective coreductant.
文摘The dull-finish ferritic stainless steel （FSS） sheet B445R for architectural roofing has been developed by Baosteel. This steel product exhibits excellent corrosion resistance superior to that of SUS 316L with a lower cost. It can be easily formed into roofing panels by ordinary processes. Moreover,the thermal strain of it is less than SUS 316L because of its lower thermal expansion coefficient, and its reflectivity is lower due to the dull-finish treatment. All of these features make it capable of being used as architectural roofing materials in coastal regions.
基金Funded by the National Natural Science Foundation of China (No.50675165)the National Key Technology R&D Program (No.2006BAF02A29)
文摘The corrosion of stainless steel was experimentally investigated and analyzed to improve the service-life of the crucible and fixture clamps. Through the experiment, stainless steel was found to satisfy the crucible and fixture clamps materials. As the chromium element mass percentage of the stainless steel increased, the corrosion decreased rapidly at first and then slowly increased. With the corrosion time prolonging, the corrosion growth rate is generally a downward trend. With Chromium 20%, the corrosive were the least. With Nickel element mass percentage increased, the corrosion increased rapidly at first and then decreased rapidly, flatten at the last. It was special that the corrosion had little relationship with the Chromium and Nickel mass percentage when the Nickel percentage is more than 35%. The most remarkable corrosion is corresponding with the Nickel element 12%, the least corrosion with Nickel element 80%. So Nickel element 35% is the most optional.
基金supported by the National Natural Science Foundation of China (No.50534010) and Baosteel Group Corporation
文摘The intergranular corrosion （IGC） behavior of high nitrogen austenitic stainless steel （HNSS） sensitization treated at 650-950℃ was investigated by the double loop electrochemical potentiodynamic reactivation （DL-EPR） method. The effects of the electrolytes, scan rate, sensitizing temperature on the susceptibility to IGC of HNSS were examined. The results show that the addi-tion of NaCl is an effective way to improve the formation of the cracking of a passive film in chromium-depleted zones during the reactivation scan. Decreasing the scan rate exhibits an obvious effect on the breakdown of the passive film. A solution with 2 mol/L H2SO4＋1 mol/L NaCl＋0.01 mol/L KSCN is suitable to check the susceptibility to IGC of HNSS at a sensitizing temperature of 650-950℃ at a suitable scan rate of 1.667 mV/s. Chromium depletion of HNSS is attributed to the precipitation of Cr2N which results in the susceptibility to IGC. The synergistic effect of Mo and N is suggested to play an important role in stabilizing the passive film to prevent the attack of IGC.
基金the Chinese Scholarship Council for financial support
文摘Synthetic slag samples of the CaO-SiO2-MgO-A1203-Cr203 system were obtained to clarify the effect of FeO on the formation of spinel phases and Cr distribution. X-ray diffraction （XRD） and scanning electron microscopy （SEM） equipped with energy-dispersive spectroscopy （EDS）, as well as the thermodynamic software FactSage 6.2, were used for sample characterization. The results show that the addition of FeO can decrease the viscosity of molten slag and the precipitation temperatures of melilite and merwinite. The solidus temperature significantly decreases from 1400 to 1250℃ with the increase of FeO content from 0wt% to 6wt%. The addition of FeO could enhance the content of Cr in spinel phases and reduce the content of Cr in soluble minerals, such as merwinite, melilite, and dicalcium silicate. Hence, the addition of FeO is conducive to decreasing Cr leaching.
基金financial support by the National Natural Science Foundation of China(Project No.51374059 and 51304042)
文摘Spinel phase is considered to be the optimal phase for stabilization of chromium in stainless steel slag.In order to restrain chromium leaching from slag for the effective environmental protection,Al2O3 was utilized for the modification treatment,and the effects on the enrichment and stabilization of chromium were investigated. The mineral phases and the existence state of chromium in slag with various Al2O3 contents at different basicities（ w（CaO）/w（SiO2） were analyzed by scanning electron microscopy-energy dispersive spectroscopy（ SEM-EDS） and X-ray diffraction（ XRD）. The results showed that chromium mainly existed in the glass and spinel phases at basicity of 1. 0 and 1. 5. As the slag basicity increased to 2. 0,chromium was also found in periclase phase. Al2O3 in the stainless steel slag reacted with MgO and Cr2O3,which could generate the Al-rich Mg（CrxAl（1- x））2O4 solid solution. Moreover,the addition of Al2O3 was favorable to reduce the solubility of chromium oxide in liquid phase and suppress the precipitation of periclase phase. The experimental results demonstrated that Al2O3 modification has a positive influence on the enrichment and the stabilization of chromium in the stainless steel slag.
基金This research was supported by the National Natural Science Foundation of China （Grant No. 51304053）, Jiangxi University of Science and Technology Doctoral Start-up Fund （No. 3401223181）.
文摘The leaching of chromium from stainless steel dust （SSD） is deleterious to the environment. To address this issue, the reduction of SSD briquettes can be employed to effectively extract chromium. The recovery rates of iron, chromium, and nickel via ironbath reduction of SSD briquettes were determined using X-ray fluorescence spectroscopy, X-ray diffraction, and scanning electron microscopy measurements. First, the effects of basicity and contents of silicon, iron, CaF2, and carbon on the recovery rates of the three metals were analyzed using the slag amount prediction model, which was originally established from the A1203 balance of corundum crucible erosion behavior. Second, the effect of feeding mode, i.e., whether steel scrap and SSD briquettes were simultaneously added, on the recovery rates was discussed in detail. Third, the iron-bath reduction of SSD briquettes was thermodynamically analyzed. The results indicated that the recovery rates of the three metals are greater than 95% those of using a basicity of 1.5 and 6.0% CaF2, 15% carbon, and 7% ferrosilicon. The recovery rate of chromium increases twofold with the addition of ferrosilicon. The feeding mode of adding briquettes and steel scrap simultaneously is better for recovery of metals and separation of the metal and slag than the feeding mode of adding steel scrap firstly and then briquettes.