A novel low-temperature alkaline smelting process is proposed to convert and separate amphoteric metals in crushed metal enrichment originated from waste printed circuit boards. The central composite design was used t...A novel low-temperature alkaline smelting process is proposed to convert and separate amphoteric metals in crushed metal enrichment originated from waste printed circuit boards. The central composite design was used to optimize the operating parameters,in which mass ratio of Na OH-to-CME, smelting temperature and smelting time were chosen as the variables, and the conversions of amphoteric metals tin, lead, aluminum and zinc were response parameters. Second-order polynomial models of high significance and3 D response surface plots were constructed to show the relationship between the responses and the variables. Optimum area of80%-85% Pb conversion and over 95% Sn conversion was obtained by the overlaid contours at mass ratio of Na OH-to-CME of4.5-5.0, smelting temperature of 653-723 K, smelting time of 90-120 min. The models were validated experimentally in the optimum area, and the results demonstrate that these models are reliable and accurate in predicting the smelting process.展开更多
基金Projects(51074190,51234009)supported by the National Natural Science Foundation of ChinaProject(2014DFA90520)supported by International Cooperation Program of Ministry of Science of ChinaProject(20110162110049)supported by the Doctoral Scientific Fund Project of the Ministry of Education of China
文摘A novel low-temperature alkaline smelting process is proposed to convert and separate amphoteric metals in crushed metal enrichment originated from waste printed circuit boards. The central composite design was used to optimize the operating parameters,in which mass ratio of Na OH-to-CME, smelting temperature and smelting time were chosen as the variables, and the conversions of amphoteric metals tin, lead, aluminum and zinc were response parameters. Second-order polynomial models of high significance and3 D response surface plots were constructed to show the relationship between the responses and the variables. Optimum area of80%-85% Pb conversion and over 95% Sn conversion was obtained by the overlaid contours at mass ratio of Na OH-to-CME of4.5-5.0, smelting temperature of 653-723 K, smelting time of 90-120 min. The models were validated experimentally in the optimum area, and the results demonstrate that these models are reliable and accurate in predicting the smelting process.