Thin films of Zn1-xCuxSe （x= 0.00, 0.05, 0.10, 0.15, 0.20） were grown on glass substrates by closed space sublimation technique. The deposited films were annealed at 200 ~C and 400 ~C in air for 1 h. The annealed sa...Thin films of Zn1-xCuxSe （x= 0.00, 0.05, 0.10, 0.15, 0.20） were grown on glass substrates by closed space sublimation technique. The deposited films were annealed at 200 ~C and 400 ~C in air for 1 h. The annealed samples have been investigated through Rutherford backscattering spectroscopy （RBS）, X-ray diffraction （XRD）, spectroscopic ellipsometer, spectrophotometer and Raman spectroscopy. Through RBS, the composition of the films was calculated and compared with the initial concentration. Structural characteriza- tion including crystal structure, crystal orientation, lattice parameter, grain size, strain and dislocation density were carried out using XRD data. From XRD spectra it was revealed that the as-deposited and annealed films were polycrystalline in nature with zinc-blende structure. However, the crystallinity and the grain size were improved with the increase of annealing temperature. According to Raman spectroscopy, it was observed that as deposited and annealed samples have the same characteristic vibrational modes of ZnSe at low and high frequency optical phonon modes while another mode was observed for 400 ℃ annealed samples at 745 cm-1. Spectroscopic ellipsometer has been used to found annealing effect on the optical properties of ZnSe. The band gap energy has been determined using transmission spectra. It was found that the band gap energy of the film increased with the increase of annealing temperature.展开更多
Sn-doped CdTe polycrystalline films were successfully deposited on ITO glass substrates by close space sublimation. The effects of Sn-doping on the microstructure, surface morphology, and optical properties of polycry...Sn-doped CdTe polycrystalline films were successfully deposited on ITO glass substrates by close space sublimation. The effects of Sn-doping on the microstructure, surface morphology, and optical properties of polycrys- talline films were studied using X-ray diffraction, scanning electron microscopy, and ultraviolet-visible spectrophotometry, respectively. The results show that the lower molar ratio of Sn and CdTe conduces to a strongly preferential orientation of （111） in films and a larger grain size, which indicates that the crystallinity of films can be improved by appropriate Sn-doping. As the molar ratio of Sn and CdTe increases, the preferential orientation of （111） in films becomes weaker, the grain size becomes smaller, and the crystal boundary becomes indistinct, which indicates that the crystallization growth of films is incomplete. However, as the Sn content increases, optical absorption becomes stronger in the visible region. In summary, a strongly preferential orientation of （111） in films and a larger grain size can be obtained by appropriate Sn-doping （molar ratio of Sn ： CdTe = 0.06 ： 1）, while the film retains a relatively high optical absorption in the visible region. However, Sn-doping has no obvious influence on the energy gap of CdTe films.展开更多
文摘Thin films of Zn1-xCuxSe （x= 0.00, 0.05, 0.10, 0.15, 0.20） were grown on glass substrates by closed space sublimation technique. The deposited films were annealed at 200 ~C and 400 ~C in air for 1 h. The annealed samples have been investigated through Rutherford backscattering spectroscopy （RBS）, X-ray diffraction （XRD）, spectroscopic ellipsometer, spectrophotometer and Raman spectroscopy. Through RBS, the composition of the films was calculated and compared with the initial concentration. Structural characteriza- tion including crystal structure, crystal orientation, lattice parameter, grain size, strain and dislocation density were carried out using XRD data. From XRD spectra it was revealed that the as-deposited and annealed films were polycrystalline in nature with zinc-blende structure. However, the crystallinity and the grain size were improved with the increase of annealing temperature. According to Raman spectroscopy, it was observed that as deposited and annealed samples have the same characteristic vibrational modes of ZnSe at low and high frequency optical phonon modes while another mode was observed for 400 ℃ annealed samples at 745 cm-1. Spectroscopic ellipsometer has been used to found annealing effect on the optical properties of ZnSe. The band gap energy has been determined using transmission spectra. It was found that the band gap energy of the film increased with the increase of annealing temperature.
基金Project supported by the Important Project of College Scientific Research Projects of Xinjiang Uygur Autonomous Region(No.XJEDU2008I05)the Young Teacher Scientific Research Initial Fund of Xinjiang University (No.QN070106)
文摘Sn-doped CdTe polycrystalline films were successfully deposited on ITO glass substrates by close space sublimation. The effects of Sn-doping on the microstructure, surface morphology, and optical properties of polycrys- talline films were studied using X-ray diffraction, scanning electron microscopy, and ultraviolet-visible spectrophotometry, respectively. The results show that the lower molar ratio of Sn and CdTe conduces to a strongly preferential orientation of （111） in films and a larger grain size, which indicates that the crystallinity of films can be improved by appropriate Sn-doping. As the molar ratio of Sn and CdTe increases, the preferential orientation of （111） in films becomes weaker, the grain size becomes smaller, and the crystal boundary becomes indistinct, which indicates that the crystallization growth of films is incomplete. However, as the Sn content increases, optical absorption becomes stronger in the visible region. In summary, a strongly preferential orientation of （111） in films and a larger grain size can be obtained by appropriate Sn-doping （molar ratio of Sn ： CdTe = 0.06 ： 1）, while the film retains a relatively high optical absorption in the visible region. However, Sn-doping has no obvious influence on the energy gap of CdTe films.