A coating of composition Si-40Mo (wt pct) was prepared by fused slurry coating method on the two-dimensional carbon/carbon (2D-C/C) composite to improve oxidation resistance. In the procedure of the fabrication, pure ...A coating of composition Si-40Mo (wt pct) was prepared by fused slurry coating method on the two-dimensional carbon/carbon (2D-C/C) composite to improve oxidation resistance. In the procedure of the fabrication, pure St slurry inner layer in the pre-coating was necessary to apply because of infiltration of liquid Si into the substrate during the sintering. The coating consists of Si continuous phase and MoSi2 particles. In addition, the infiltration of Si into the substrate and the SiC reaction layer between the coating and the C/C composite were observed. Oxidation behavior of coated and uncoated C/C composites was studied in cyclic mode. The oxidation resistance and the thermal shock resistance of the Si-Mo fused slurry coating were quite excellent at 1370℃.展开更多
Microstructure of plasma spray boron carbide coating was studied by SEM and TEM. its physical, mechanical and electrical properties were measured. The results showed that high microhardness. modulus and low porosity o...Microstructure of plasma spray boron carbide coating was studied by SEM and TEM. its physical, mechanical and electrical properties were measured. The results showed that high microhardness. modulus and low porosity of B4C coating were manufactured by plasma spray. It was lamellar packing and dense. The B4C coating examined here contained two principal structures and two impurity phase besides major phase. The relatively small value of Young’s modulus, comparing with that of the bulk materials, is explained by porosity. The Fe impurity phase could account for the relatively high electrical conductivity of boron carbide coating by comparing with the general boron carbide materials.展开更多
文摘A coating of composition Si-40Mo (wt pct) was prepared by fused slurry coating method on the two-dimensional carbon/carbon (2D-C/C) composite to improve oxidation resistance. In the procedure of the fabrication, pure St slurry inner layer in the pre-coating was necessary to apply because of infiltration of liquid Si into the substrate during the sintering. The coating consists of Si continuous phase and MoSi2 particles. In addition, the infiltration of Si into the substrate and the SiC reaction layer between the coating and the C/C composite were observed. Oxidation behavior of coated and uncoated C/C composites was studied in cyclic mode. The oxidation resistance and the thermal shock resistance of the Si-Mo fused slurry coating were quite excellent at 1370℃.
文摘Microstructure of plasma spray boron carbide coating was studied by SEM and TEM. its physical, mechanical and electrical properties were measured. The results showed that high microhardness. modulus and low porosity of B4C coating were manufactured by plasma spray. It was lamellar packing and dense. The B4C coating examined here contained two principal structures and two impurity phase besides major phase. The relatively small value of Young’s modulus, comparing with that of the bulk materials, is explained by porosity. The Fe impurity phase could account for the relatively high electrical conductivity of boron carbide coating by comparing with the general boron carbide materials.