Chemically resistant anodic oxide layers were formed on pure aluminum substrates in oxalic acid-sulphuric acid bath.Acid dissolution tests of the obtained anodic layers were achieved in accordance with the ASTM B 680-...Chemically resistant anodic oxide layers were formed on pure aluminum substrates in oxalic acid-sulphuric acid bath.Acid dissolution tests of the obtained anodic layers were achieved in accordance with the ASTM B 680-80 specifications：35mL/L 85% H3PO4＋20g/L CrO3 at 38℃.Influence of oxalic acid concentration,bath temperature and anodic current density on dissolution rate and coating ratio was examined,when the sulphuric acid concentration was maintained at 160g/L.It was found that chemically resistant and compact oxide layers were produced under low operational temperature （5℃） and high current densities （3A/dm^2）.A beneficial effect was observed concerning the addition of oxalic acid （18g/L）.The morphology and the composition of the anodic oxide layer were examined by scanning electron microscopy （SEM）,atomic force microscopy （AFM） and glow-discharge optical emission spectroscopy （GDOES）.展开更多
This study aimed to optimize the rapid test factors of dry basis weight of reconstituted tobacco, in order to afford a reference test method for companies which produce reconstituted tobacco to better control the basi...This study aimed to optimize the rapid test factors of dry basis weight of reconstituted tobacco, in order to afford a reference test method for companies which produce reconstituted tobacco to better control the basis weight and coating ratio on line. The dry basis weight of reconstituted tobacco was tested by fast method and normal oven method individually. And the effects on the test values of different test factors such as temperature, time and the number of baking sheets were studied. Then the test values of these two methods were compared, so the proper factors of rapid test method were determined. As the baking temperature rose from 130 ℃ to 150 ℃, and the baking time rose from 1 min to 2 min, the difference between fast test method and normal oven method grew, and when the number of baking pieces rose from 3 pieces to 5 pieces, the difference between the two methods went down. The optimum test condition was baking temperature of 130 ℃, baking time of 1 min, and baking sample sheet number of 5. Under this condition, the value of fast test method was the closest to the test value of normal oven method, and meanwhile, the test factor was more proper for testing on line. The study will provide a reference for online controlling of dry basis weight and coating ratio of reconstituted tobacco.展开更多
The Absorption and permeability of air-jet textured glass fiber yarn and its fabric and bonded tenacity of the fabric have been studied in relation to the main parameters, air supplied pressure and overfeed ratio.It h...The Absorption and permeability of air-jet textured glass fiber yarn and its fabric and bonded tenacity of the fabric have been studied in relation to the main parameters, air supplied pressure and overfeed ratio.It has been observed that increasing the level of main parameters improves the coated ratio of the textured yarn and its fabric as well as the bonded tenacity of the fabric made of textured yarn. Comparison of absorption or permeability between textured and supplied yarns, and comparison of absorption or permeability and bonded tenacity between the two kinds of fabrics have been elucidated.展开更多
文摘Chemically resistant anodic oxide layers were formed on pure aluminum substrates in oxalic acid-sulphuric acid bath.Acid dissolution tests of the obtained anodic layers were achieved in accordance with the ASTM B 680-80 specifications：35mL/L 85% H3PO4＋20g/L CrO3 at 38℃.Influence of oxalic acid concentration,bath temperature and anodic current density on dissolution rate and coating ratio was examined,when the sulphuric acid concentration was maintained at 160g/L.It was found that chemically resistant and compact oxide layers were produced under low operational temperature （5℃） and high current densities （3A/dm^2）.A beneficial effect was observed concerning the addition of oxalic acid （18g/L）.The morphology and the composition of the anodic oxide layer were examined by scanning electron microscopy （SEM）,atomic force microscopy （AFM） and glow-discharge optical emission spectroscopy （GDOES）.
基金Supported by Science and Technology Planning Project of China Tobacco Schweitzer(Yunnan)Reconstituted Tobacco Co.,Ltd.(KY-17-ZL-01)China Tobacco Yunnan Industrial Co.,Ltd.(2016YL02)
文摘This study aimed to optimize the rapid test factors of dry basis weight of reconstituted tobacco, in order to afford a reference test method for companies which produce reconstituted tobacco to better control the basis weight and coating ratio on line. The dry basis weight of reconstituted tobacco was tested by fast method and normal oven method individually. And the effects on the test values of different test factors such as temperature, time and the number of baking sheets were studied. Then the test values of these two methods were compared, so the proper factors of rapid test method were determined. As the baking temperature rose from 130 ℃ to 150 ℃, and the baking time rose from 1 min to 2 min, the difference between fast test method and normal oven method grew, and when the number of baking pieces rose from 3 pieces to 5 pieces, the difference between the two methods went down. The optimum test condition was baking temperature of 130 ℃, baking time of 1 min, and baking sample sheet number of 5. Under this condition, the value of fast test method was the closest to the test value of normal oven method, and meanwhile, the test factor was more proper for testing on line. The study will provide a reference for online controlling of dry basis weight and coating ratio of reconstituted tobacco.
文摘The Absorption and permeability of air-jet textured glass fiber yarn and its fabric and bonded tenacity of the fabric have been studied in relation to the main parameters, air supplied pressure and overfeed ratio.It has been observed that increasing the level of main parameters improves the coated ratio of the textured yarn and its fabric as well as the bonded tenacity of the fabric made of textured yarn. Comparison of absorption or permeability between textured and supplied yarns, and comparison of absorption or permeability and bonded tenacity between the two kinds of fabrics have been elucidated.