Sulphuric Acid Bake-Leach Process for the Treatment of Mixed Copper-Cobalt Oxide Ores

A sulphuric acid bake–leach method for the treatment of mixed copper-cobalt oxide minerals was investigated as an alternative to the reductive leaching method. Sulphuric acid bake-leach process of the mixed copper-cobalt oxide ore was carried out by mixing the sample with sulphuric acid followed by baking of the mixture in a muffle furnace. Baking tests were conducted at different conditions such as temperature, time, and varying amounts of acid. The reacted samples were then subjected to water leaching at room temperature to determine the leachability of copper and cobalt from the baked material. The dissolutions of copper and cobalt were dependent on acid concentration with cobalt showing more sensitivity to the amount of acid. Both copper and cobalt were extracted from the baked material within short leaching times and without the addition of reducing agents. The outcome of this work has shown that the sulphuric acid bake-leach process is a possible alternative to the reductive leaching method for copper-cobalt oxide ores.

刚果(金)某氧化铜钴矿选矿试验研究

针对刚果(金)某难处理氧化铜钴矿开展小型浮选工艺试验,探究了单因素条件对于浮选指标的影响,进行了粗扫选开路和闭路试验。单因素条件试验确定了以NaHS作为浮选硫化剂,以丁基黄药+戊基黄药(1∶1)的组合药剂作为捕收剂。在最优药剂制度下,经粗扫选开路浮选试验,获得了泡沫精矿Cu、Co回收率分别为92.74%、89.32%的浮选指标;经闭路浮选试验,获得精矿Cu、Co回收率分别为90.22%、83.21%的浮选指标,实现了难处理氧化铜钴矿中铜钴资源的有效回收。

不同螯合剂对花生富集污染土壤中Co的影响

采用模拟Co污染土壤的方法,分别投加2.5 mmol/kg、5.0mmol/kg、7.5 mmol/kg的EDDS、NTA、CA和OA,研究了其对花生生长与吸收土壤重金属Co,以及对土壤中Co的活化能力的影响。结果表明:螯合剂处理使花生的生物量降低,在高浓度螯合剂处理时,降幅最大;EDDS的添加比NTA、CA和OA更显著地增加了土壤Co的有效态质量比,同时明显提高了花生的富集系数和转运能力;在螯合剂处理下,花生的转运系数最高达到0.916,具备了修复土壤重金属污染的能力;根系和地上部富集Co能力最强时分别达到58.64 mg/kg和46.33 mg/kg,是对照组的1.29和3.63倍;各处理花生根系中的Co质量比要高于茎叶中的质量比,花生植株Co质量比与土壤有效态Co质量比呈显著(p<0.05)或极显著相关(p<0.01);综合来看,螯合剂的投加能有效活化土壤溶液中的Co,促进植物吸收、转运重金属。

液相法制备钴蓝颜料的性能及动力学研究

研究了液相法制备钴蓝所用沉淀剂 ,探讨了主要工艺参数诸如CoO与Al2 O3 的摩尔比 ,阴离子SO2 - 4 的引入及浓度、煅烧温度等与钴蓝光学性能、粒径、形貌以及晶型转化的关系 .实验结果表明液相法制备钴蓝不仅较常规固相法煅烧温度低 2 0 0℃左右 ,颜料色泽鲜艳 ,而且颜料不用粉碎就很松散 ,粒径均匀 ,性能优异 ,具有尖晶石结构 .通过热重分析研究了由钴蓝前驱体到钴蓝热分解过程的反应动力学 ,提出了反应动力学模型 .

活性球化剂对草酸钴形貌的影响

研究了添加活性球化剂对草酸钴形貌的影响 ,利用X衍射仪对工业草酸钴和球形草酸钴的结构进行分析 ,同时用扫描电镜观察它们的形貌 ,实验表明 ,添加活性球化剂在不改变草酸钴晶体结构的前提下 ,使其外观形貌发生了明显的变化 ,从而改善了其物理性能。

软化学法制备尖晶石结构的钴蓝颜料的研究

研究了以尿素为沉淀剂 ,采用软化学法合成具有尖晶石结构的钴蓝颜料的制备方法 ,尿素在不同条件下的水解行为及水解率的表征 ;探讨了煅烧温度与颜料的光学性能、晶型转化、以及粒径大小的关系 ;并将本法与干法所制颜料进行了对比。结果表明 ,本方法较干法煅烧温度低 10 0～ 2 0 0℃ ,晶型好 ,粒度均匀 ,晶界清晰 。

吸附胶体浮选法处理电解钴废水的研究

采用吸附胶体浮选法处理电解钴废水。用十二烷基磺酸钠（ＳＬＳ）作浮选剂，用ＦｅＣｌ３和Ａｌ２（ＳＯ４）３作混凝剂，浮选后废水可达到国家工业废水排放标准（３ｍｇ／Ｌ）。为实际废水的处理提供了可靠的依据。

玻璃纤维毡增强不饱和聚酯树脂复合材料中促进剂及固化剂加入量的探讨

以不饱和聚酯为基体,玻璃纤维毡为增强材料,用过氧化甲乙酮为固化剂、异辛酸钴为促进剂,常温固化得到复合材料。研究固化剂、促进剂不同加入量和配比对材料力学性能的影响。

反应条件对六氨合钴同时脱硫脱硝效果的影响

钴氨络合剂可同时脱除SO_2和NO,对燃煤电厂排放控制有积极意义。在分析钴氨配合物同时脱硫脱硝反应机理的基础上,设计了同时脱硫脱硝实验装置,在反应器中对[Co(NH_3)_6]Cl_2吸收剂同时脱硫脱硝的影响因素进行实验研究。结果表明:提高[Co(NH_3)_6]Cl_2的浓度可以提高SO_2和NO的去除率;过高温度不利于NO的吸收,实验过程中48℃时NO的去除率最高;碱性溶液可促进NO的氧化,但是碱性过强导致配合物不稳定,会降低NO的去除率,实验条件下溶液最佳pH值为9.88。

氢氧化镍钴生产工艺中碱基活化控制技术的研发及应用

红土镍矿湿法冶金产出中间产品氢氧化镍钴(MHP),氢氧化钠沉淀镍钴工艺简单,设备投资小,生产成本低,但存在产物细小、含水率高、可溶性杂质含量高、沉降及过滤性能差等问题。中国恩菲针对此问题研发了碱基活化控制技术,该技术利用沉淀后溶液中的镁对氢氧化钠进行转化,使得液态碱转变为难溶碱,并在转碱过程中实现沉淀颗粒的活性控制,从而降低氢氧根释放速度,降低碱过饱和度,为沉淀颗粒生长机制创造了先决条件。整套技术包括转碱技术、活性生长技术以及联合控制方法,已应用于瑞木镍钴项目,经过长期生产实践探索及调试,目前运行高效稳定,经济效果明显。

掺钴LiFePO_4/C的电化学性能研究

通过固相烧结法制备了掺钴的LiFePO4/C正极材料.采用充放电测试、循环伏安和交流阻抗等现代技术测试了样品的电化学性能.结果表明,750℃烧结的掺钴样在2 C倍率电流下首次循环的放电容量达到115 mAh/g.该样品50次循环的容量衰减率仅为2.61%,电化学性能稳定.

提高大冶铁矿钴品位的试验研究

为提高大冶铁矿的硫钴精矿中的钴品位,以CS活化剂调浆,在矿浆浓度(质量分数)29.63%、pH值为9(硫酸调节)、捕收剂为丁基黄药(用量70g/t)、起泡剂为2#油(用量70g/t)的条件下活化再选,钴品位可达到0.28%,回收率为98.2%.

刚果(金)某复杂氧化铜钴矿选矿工艺研究

刚果(金)某氧化铜钴矿含铜3.12%、含钴0.15%,铜、钴矿物赋存状态复杂,选矿难度大,采用"硫化矿与氧化矿分步浮选-硫化粗精矿再磨-氧化粗精矿再选抛尾"的选矿工艺,实现了铜和钴的高效回收。全流程闭路试验获得硫化精矿产品含铜71.13%、含钴0.16%,铜、钴回收率分别为46.47%、2.38%;获得的氧化精矿产品含铜31.66%、含钴1.32%,铜、钴回收率分别为38.23%、36.24%;铜、钴的总回收率分别达到84.70%和38.62%。钴主要因石英、白云石、绿泥石、针铁矿或赤铁矿及硬锰矿等矿物赋存钴而损失于尾矿中。

7─（4─磺苯基偶氮）─8─羟基喹啉用作钴的新光度试剂及其用于VB_（12）的间接分光光度测定

合成了题述试剂ＳＰＡＨＱ，可用其作钴显色剂。生成的红棕色１：４（Ｃｏ：ＳＰＡＨＱ）螯合物λｍａｘ＝４８０ｎｍ，ε４８０＝８．１×１０４Ｌ·ｍｏｌ－１·ｃｍ－１，Δλ＝９０ｎｍ。０～１．２μｇ／ｍＬＣｏ２＋遵守比尔定律。１～１０ｍｇ的７种离子和０．０３５～０．９４ｍｇ的１８种离子不干扰。用于间接分光光度测定ＶＢ１２，结果与亚硝基Ｒ盐法一致。本法既灵敏、选择性也好。

多壁碳纳米管表面的钴-铁化学镀(英文)

采用化学镀法在多壁碳纳米管表面沉积钴-铁涂层。主要研究了镀液中钴盐和铁盐的摩尔比、络合剂浓度和镀液温度对镀层的影响。在钴-铁的摩尔比为9∶1,络合剂浓度为0.32mol/L,镀液温度为60℃时,可得到的较为平整的镀层,且镀层中钴-铁摩尔之和达90%以上。其他条件下,则会在镀层中出现金属颗粒或钴-铁含量过少的情况。

钴改性磁粉的表面活性剂处理

用多种表面活性剂处理了包钴磁粉，并按Ｗａｓｈｂｕｒｎ方程测定其斜率值．就中以季铵盐和聚乙烯醇混合物的处理效果最好，在丁酮、甲苯和环己酮３种溶剂中，其斜率值均增大近一倍．

麦穗状钴镍合金微晶的合成研究

以二价钴盐、镍盐为前驱体,以酒石酸钠为络合剂,以次亚磷酸钠为还原剂,采用水热还原法制得形貌新颖的麦穗状钴镍合金微晶。该微晶由厚度约为100 nm的纳米板在"主茎"两侧按一定的方向排列而成。采用扫描电镜(SEM)、电子能谱仪(EDS)、X射线衍射仪(XRD)对样品进行表征。考察了络合剂类型及用量、氢氧化钠用量对产品形貌的影响。结果表明:氢氧化钠是合成麦穗状微晶的关键,其用量直接影响产品的形貌;酒石酸钠作为络合剂对麦穗状结构的形成也起到了重要的作用。

氯化物锌-钴合金镀液中氯化锌的分析方法

制定了氯化物锌-钴合金镀液中氯化锌的分析方法。在氨性溶液中加热至沸腾的条件下,用过硫酸铵将Co^(2+)离子氧化成Co^(3+)离子并与NH_3反应生成[Co(NH_3)_6]^(3+)配离子,Fe^(3+)在pH=8~9的条件下生成Fe(OH)_3沉淀,加氟化钠掩蔽Al^(3+)杂质,以Cu-PAN作指示剂,用EDTA标准滴定溶液滴定锌。分析结果的相对平均偏差为0.13%,回收率为99.49%~99.92%,满足容量法的测定要求。

钴镍渣综合回收后结晶母液萃取回收铜研究

介绍了株洲冶炼集团股份有限公司二段净化渣选择性分离锌、浸出液结晶铜后的结晶母液采用30%CP-150+70%煤油萃取剂体系萃取铜,用3 mol/L硫酸作为反萃剂,铜的萃取率为99.68%(二级),铜的反萃率为98.01%。

氯化钾镉钴合金电镀废水的组合处理方法

在pH为10~12的条件下,先用亚铁离子和钙离子共同沉淀氯化钾镉钴合金电镀和钝化混合废水中的氨三乙酸等羧酸配位剂,六价铬被亚铁离子还原成三价铬后与镉离子、钴离子等一同生成氢氧化物沉淀。再用二甲基二硫代氨基甲酸钠沉淀废水中残留的重金属离子,使其沉淀完全。最后用次氯酸钠氧化废水中的电镀添加剂,降低其化学需氧量(COD)。该方法成本低,处理结果可满足GB 21900-2008《电镀污染物排放标准》的“表3”要求。