Microstructure evolution of Al-Cu-Mg alloy during rapid cold punching and recrystallization annealing

The microstructure evolution of spray formed and rapidly solidified Al-Cu-Mg alloy with fine grains during rapid cold punching and recrystallization annealing was investigated by transmission electron microscopy(TEM). The results show that the precipitates of fine-grained Al-Cu-Mg alloy during rapid cold punching and recrystallization annealing mainly consist of S phase and a small amount of coarse Al6Mn phase. With the increase of deformation passes, the density of precipitates increases, the size of precipitates decreases significantly, and the deformation and transition bands disappear gradually. In addition, the grains are refined and tend to be uniform. Defects introduced by rapid cold punching contribute to the precipitation and recrystallization, and promote nucleation and growth of S phase and recrystallization. Deformation and transition bands in the coarse grains transform into deformation-induced grain boundary during the deformation and recrystallization, which refine grains, obtain uniform nanocrystalline structure and promote homogeneous distribution of S phase.

Effect of aging treatment on evolution of S'phase in rapid cold punched Al−Cu−Mg alloy

High-resolution transmission electron microscopy(TEM),X-ray diffractometer(XRD),and hardness test were used to study the evolution of long plate-shaped S'phase in the spray-formed fine-grained Al−Cu−Mg alloy during aging after rapid cold punching deformation.Results show that the long plate-shaped S'phase in the extruded Al−Cu−Mg alloy undergoes evident distortion,brittle failure,separation and redissolution,during rapid cold punching deformation,leading to the transformation of long plate-shaped S'phase into short rod or even redissolution and disappearance,causing the matrix to become a supersaturated solid solution.After the aging treatment,the reprecipitation of the phases occurs,and these aging phases are mainly long plate-shaped and granular.The incompletely dissolved S'phase acts as nucleation core,promoting uphill diffusion of the surrounding solute atoms.The S'phase gradually grows with increasing the aging time.The completely dissolved S'phase forms the incoherent equilibrium phase with the matrix to reduce its free energy.After rapid cold punching,the aging response of the deformed Al−Cu−Mg alloy is accelerated,and the hardness of the alloy is substantially increased.