In this work, Co 2D antidot arrays with well-ordered hexagonal holes ranging in size from 1.3 to 6.2 μm were fabricated by colloidal crystal template method. The geometry configuration and magnetic properties of the ...In this work, Co 2D antidot arrays with well-ordered hexagonal holes ranging in size from 1.3 to 6.2 μm were fabricated by colloidal crystal template method. The geometry configuration and magnetic properties of the samples were investigated. An enormous increase in coercivity and squareness, as compared with the corresponding continuous film, was observed. Magnetic properties of Co 2D antidot arrays showed a close dependence on pore diameter. According to geometric calculation, the effect of the pore diameter on magnetic properties was also discussed. The Co 2D antidot arrays obtained by this method are promising candidates for high-density information storage.展开更多
A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite wa...A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite was obtained after the polystyrene template was removed by calcination. The micro/macro-pore structure of the prepared β-zeolite was highly ordered. In comparison with other assembly methods, the co-deposition method could obtain a highly ordered macro-porous material with relatively large zeolite filling particles, and therefore the co-deposition of particles with different size is a promising method for the fabrication of macro-porous materials.展开更多
A stable 3DOM CeO2 with well-defined inverse opal microstructure and crystalline walls structure has been successfully synthesized by application of three-dimensional order PMMA beads as templates. Structural feature ...A stable 3DOM CeO2 with well-defined inverse opal microstructure and crystalline walls structure has been successfully synthesized by application of three-dimensional order PMMA beads as templates. Structural feature of products was characterized by using SEM, DTA-TG XRD.展开更多
基金financially supported by the Innovation Foundation of Aviation Industry Corporation of China (No. JK65150307)
文摘In this work, Co 2D antidot arrays with well-ordered hexagonal holes ranging in size from 1.3 to 6.2 μm were fabricated by colloidal crystal template method. The geometry configuration and magnetic properties of the samples were investigated. An enormous increase in coercivity and squareness, as compared with the corresponding continuous film, was observed. Magnetic properties of Co 2D antidot arrays showed a close dependence on pore diameter. According to geometric calculation, the effect of the pore diameter on magnetic properties was also discussed. The Co 2D antidot arrays obtained by this method are promising candidates for high-density information storage.
基金the National Basic Research Program of China （No. 2004CB217808） the National Natural Science Foundation of China （No. 20376046）.
文摘A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite was obtained after the polystyrene template was removed by calcination. The micro/macro-pore structure of the prepared β-zeolite was highly ordered. In comparison with other assembly methods, the co-deposition method could obtain a highly ordered macro-porous material with relatively large zeolite filling particles, and therefore the co-deposition of particles with different size is a promising method for the fabrication of macro-porous materials.
基金The financial supports from The National Natural Science Foundation of China(20163002)Natural Science Foundation of Yunnan Province(2003E0005Z)are gratefully acknowledged.
文摘A stable 3DOM CeO2 with well-defined inverse opal microstructure and crystalline walls structure has been successfully synthesized by application of three-dimensional order PMMA beads as templates. Structural feature of products was characterized by using SEM, DTA-TG XRD.