Phase Structure and Cycle Stabilities of Mg_2Ni/Mm_(0.3)Ml_(0.7)Ni_(3.55)Co_(0.75)Mn_(0.4)Al_(0.3) Composite Hydrogen Storage Alloys Prepared by Two-step re-melting

Mm0.3Ml0.7Ni3.55Co0.75Mn0.4-Al0.3 alloy has high chemical activity and favorable plateaus pressure. Mg2Ni is in favor of high hydrogen storage capacity and low weight, but it is difficult to be activated. In order to improve the capacity and cycle performances of hydrogen-storage alloy electrodes, Mm0.3Ml0.7Ni3.55Co0.75Mn0.4-Al0.3-x%Mg2Ni(x=0, 5, 10, 30) composite hydrogen storage alloys prepared by two-step re-melting were investigated in this work. The influences of Mg2Ni content on the cycle stabilities were analyzed by electrochemical methods. It was observed by XRD that the main phase of all the alloys is LaNi5 and the crystal lattice parameters of LaNi5 are changed with the increasing of x value, i.e, a-axis and unit cell volume decrease and c-axis decreases nonlinearly. The c-axis of alloy with x=5 is larger than the others. With the increasing of x value, capacity retentions of the composite hydrogen storage alloys rise from 66.21% while x=0 to 82.04% while x=10, but the capacity retention of the composite alloy with 30% Mg2Ni declines because of its decreasing axial ratio. More over, the composite alloy with 5% Mg2Ni shows the best cycle stability and higher discharge capacity, and it is an appropriate candidate for battery materials.

Electrochemical hydrogen storage characteristics of Ti_(0.10)Zr_(0.15)V_(0.35)Cr_(0.10)Ni_(0.30)-10% LaNi_3 composite and its synergetic effect

Hydrogen storage composite alloy Ti0.10Zr0.15V0.35Cr0.10Ni0.30–10% LaNi3 was prepared by two-step arc-melting to improve the electro-catalytic activity and the kinetic performance of Ti-V-based solid solution alloy. The electrochemical properties and synergetic effect of the composite alloy electrode were systematically investigated by using X-ray diffractometry, field emission scanning electron microscopy, energy-dispersive spectrometry, electrochemical impedance spectroscopy and galvanostatic charge/discharge test. It is found that the main phase of the composite alloy is composed of V-based solid solution phase with a BCC structure and C14 Laves phase with hexagonal structure, while the secondary phase is formed in the composite alloy. The comprehensive electrochemical properties of the composite alloy electrode are significantly improved. The activation cycle number, the maximum discharge capacity and the low temperature dischargeability of the composite alloy are 5 cycles, 362.5 mA-h/g and 65.84% at 233 K, respectively. It is suggested that distinct synergetic effect occurs in the activation process, composite process, cyclic process and discharge process at a low or high temperature under different current densities, in the charge–transfer resistance and exchange current density.

Microstructure and Hydrogen Absorption Pro-perties of Mg/MmNi_(5-x) (CoAlMn)_x Composite Prepared by Mechanical Alloying

The microstructure ofthe Mg/MmNi5-x (CoAlMn )x composite hydrogen storage material preparedby the method of mechanical alloyingwas characterized by X-ray diffraction, SEM and particle size distribution analysis. By measuring PCTcurves, the hydrogen absorption properties of the composite was evaluated.The results show that nanocrystallinecomposite structure can be obtainedunder adequate ball milling condition. The reactive activation and hydrogen absorption capacity are improved compared with the sole MmNi5-x(CoAlMn)x alloy. The effect ofmagnesium on the microstructure andhydrogen absorption properties of thecomposite were also evaluated.