In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ...In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ80 Mg alloy were investigated.Citric acid(CA)was used to activate the alloy surface during the pretreatment process.The alloy was first pretreated with CA and then subjected to a hydrothermal process using ultrapure water to produce Mg-Al-LDH/Mg(OH)_(2)steam coating.The effect of different time of acid pretreatment on the activation of the intermetallic compounds was investigated.The microstructure and elemental composition of the obtained coatings were analyzed using FE-SEM,EDS,XRD and FT-IR.The corrosion resistance of the coated samples was evaluated using different techniques,i.e.,potentiodynamic polarization(PDP),electrochemical impedance spectrum(EIS)and hydrogen evolution test.The results indicated that the CA pretreatment significantly influenced the activity of the alloy surface by exposing the intermetallic compounds.The surface area fraction of Mg_(17)Al_(12)and Al_(8)Mn_(5)phases on the surface of the alloy was significantly higher after the CA pretreatment,and thus promoted the growth of the subsequent Mg-Al-LDH coatings.The CA pretreatment for 30 s resulted in a denser and thicker LDH coating.Increase in the CA pretreatment time significantly led to the improvement in corrosion resistance of the coated AZ80 alloy.The corrosion current density of the coated alloy was lower by three orders of magnitude as compared to the uncoated alloy.展开更多
Catalytic oxidation is regarded as one of the most promising strategies for volatile organic compounds(VOCs)purification.Mixed metal oxides(MMOs),after topological transformation using layered double hydroxides(LDHs)a...Catalytic oxidation is regarded as one of the most promising strategies for volatile organic compounds(VOCs)purification.Mixed metal oxides(MMOs),after topological transformation using layered double hydroxides(LDHs)as precursors,are extensively used as catalysts for VOCs oxidation due to their uniformity advantage.This review summarizes the developments in the LDH-derived VOCs heterogeneous catalytic oxidation over the last 10 years.Particularly,it addresses the VOCs abatement performance over MMO,noble metal/MMO,core-shell structured MMO,and integral MMO film catalysts originating from LDHs.Moreover,it highlights the water vapor effect and oxidation mechanism.This review indicates that LDH-based catalysts are a category of important VOCs oxidation materials.展开更多
Sulphur-containing aromatic nitro compounds were rapidly reduced to the corresponding amines in high yields by employing hydrazine hydrate as a hydrogen donor in the presence of iron oxide hydroxide catalyst. It was w...Sulphur-containing aromatic nitro compounds were rapidly reduced to the corresponding amines in high yields by employing hydrazine hydrate as a hydrogen donor in the presence of iron oxide hydroxide catalyst. It was worth noting that the catalyst exhibited extremely high activity. The reduction could be completed within 20-50 min and the yields were up to 97-99 %.展开更多
Mg-Al layered double hydroxide intercalated with CO_(3)^(2-)(CO_(3)·Mg-Al LDH) is effective for treating HCl exhaust gas.HCl reacts with CO_(3)^(2-) in CO_(3)·Mg-Al LDH, resulting in the formation of Cl·...Mg-Al layered double hydroxide intercalated with CO_(3)^(2-)(CO_(3)·Mg-Al LDH) is effective for treating HCl exhaust gas.HCl reacts with CO_(3)^(2-) in CO_(3)·Mg-Al LDH, resulting in the formation of Cl·Mg-Al LDH.We propose that CO_(2) can be used for the desorption of Cl^(-)from Cl·Mg-Al LDH to regenerate CO_(3)·Mg-Al LDH.Herein,we studied the desorption of a from CI-Mg-Al LDH by adding water to Cl·Mg-Al LDH and blowing CO_(2) into it.We also analyzed the effects of temperature and water addition speed on the desorption of CI^(-)from Cl·Mg-Al LDH.Our results show that the added water adhered to CI·Mg-Al LDH and that CO_(2) in the gaseous phase was dissolved in this adhered water,thus generating CO_(3)^(2-).Therefore,anion exchange occurred between CO_(3)^(2-) and Cl^(-)in the Cl·Mg-Al LDH,thus desorbing Cl^(-).展开更多
A series of Zn-xAl(x=0-35 wt.%)alloy filler metals were designed to join AZ31 Mg alloy to 6061 Al alloy by laser-TIG hybrid welding.The effect of Al content on the wettability of filler metals,microstructure evolution...A series of Zn-xAl(x=0-35 wt.%)alloy filler metals were designed to join AZ31 Mg alloy to 6061 Al alloy by laser-TIG hybrid welding.The effect of Al content on the wettability of filler metals,microstructure evolution and strength of joint was investigated.The results indicated that the strength of joints was improved with the increase of Al content in filler metals.When Zn-15Al filler was used,the ultimate fracture load reached the maximum of 1475.3 N/cm,which was increased by 28%than that with pure Zn filler.The reason is that the Al element acts as a"reaction depressant"in filler metal,which contributes to inhibiting the dissolution of Mg base metal and the Mg-Zn reaction.The addition of appropriate quantity of Al element promoted the precipitation of Al-rich solid solution instead of Zn solid solution.The MgZn_(2) IMCs have lower lattice mismatch with Al solid solution than Zn solid solution,thus the strength of joints is improved.However,the excessive addition of Al caused the formation of brittle Mg32(Al,Zn)49 ternary compounds,leading to the deterioration of joint performance.展开更多
The preparation of ZnAlLa-hydrotalcite-like compounds [ZnAlLa-HTLcs] wasstudied. ZnAlLa-HTLcs were synthesized by a method of variable pH with the raw materials ofZn(NO_3)_2, Al(NO_3)_3, La(NO_3)_3, and NaOH. The eS&#...The preparation of ZnAlLa-hydrotalcite-like compounds [ZnAlLa-HTLcs] wasstudied. ZnAlLa-HTLcs were synthesized by a method of variable pH with the raw materials ofZn(NO_3)_2, Al(NO_3)_3, La(NO_3)_3, and NaOH. The eS'ccts of some factors (i.e. pH values, the moleratio of Al^(3+) to La^(3+), temperature and the period of hydrothermal treatment) on thepreparation of HTLcs were discussed systematically. XRD, TG-DTA, FT-IR spectroscopy, and ICP wereperformed to characterize ZnAlLa-HTLcs samples, and the thermal stability of HTLcs was alsodiscussed. It was shown that unique ZnAlLa-HTLcs with high crystallinity can be prepared, under theconditions of pH = 5.5-6.5, n(Zn^(2+))/n(Al^(3+) + La^(3+))=2 and the atomic ratio of La^(3+) toAl^(3+) ranging from 0.07 to 2, hydrothermal treatment at 120 ℃ for 5 h. When the calcination ofthe HTLcs is performed at temperatures above 200 ℃, ZnO phase is detected with Al_2O_3 and La_2O_3spreading on its top. The complex metal oxides derived from ZnAlLa-HTLcs at 500 ℃ have highercatalytic activity and selectivity than those from ZnAl-HTLcs for the esterification of acetic acidwith n-butanol under the same reaction conditions.展开更多
A series of Zn_(x)Ni_(y)CrO_(m±δ)catalysts were synthesized via a typical co-precipitation method,in which Zn-Cr layered double hydroxides(LDHs)were found and Ni-Zn intermetallic compound(IMC)was formed after re...A series of Zn_(x)Ni_(y)CrO_(m±δ)catalysts were synthesized via a typical co-precipitation method,in which Zn-Cr layered double hydroxides(LDHs)were found and Ni-Zn intermetallic compound(IMC)was formed after reduction in hydrogen.During auto-thermal reforming(ATR)of acetic acid(HAc),the Ni-Zn IMC was transformed into Ni/(amorphous-ZnO)-ZnCr_(2)O_(4) species with uniformed distribution and appropriate interaction within these Ni-Zn-Cr-O species;besides,the adsorbed oxygen promoted the activation and transfer of oxygen species;therefore,deactivation by oxidation,sintering and coking was inhibited.And the optimized Zn_(2.37)Ni_(0.63)CrO_(4.5±δ)catalyst presented high activity and stability in a 45-h ATR test with HAc conversion near 100%and hydrogen yield at 2.7 mol-H_(2)/mol-HAc,showing potential for hydrogen production via ATR of HAc.展开更多
基金This work was supported by the National Natural Science Foundation of China(Grant Nos.51601108 and 52071191)the Natural Science Foundation of Shandong Province(ZR2020ME011).
文摘In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ80 Mg alloy were investigated.Citric acid(CA)was used to activate the alloy surface during the pretreatment process.The alloy was first pretreated with CA and then subjected to a hydrothermal process using ultrapure water to produce Mg-Al-LDH/Mg(OH)_(2)steam coating.The effect of different time of acid pretreatment on the activation of the intermetallic compounds was investigated.The microstructure and elemental composition of the obtained coatings were analyzed using FE-SEM,EDS,XRD and FT-IR.The corrosion resistance of the coated samples was evaluated using different techniques,i.e.,potentiodynamic polarization(PDP),electrochemical impedance spectrum(EIS)and hydrogen evolution test.The results indicated that the CA pretreatment significantly influenced the activity of the alloy surface by exposing the intermetallic compounds.The surface area fraction of Mg_(17)Al_(12)and Al_(8)Mn_(5)phases on the surface of the alloy was significantly higher after the CA pretreatment,and thus promoted the growth of the subsequent Mg-Al-LDH coatings.The CA pretreatment for 30 s resulted in a denser and thicker LDH coating.Increase in the CA pretreatment time significantly led to the improvement in corrosion resistance of the coated AZ80 alloy.The corrosion current density of the coated alloy was lower by three orders of magnitude as compared to the uncoated alloy.
基金supported by the National Key R&D Program of China(2017YFC0211503,2016YFC0207100)the Strategic Priority Research Program(A)of the Chinese Academy of Sciences(XDA23030300)+2 种基金the National Natural Science Foundation of China(21401200,51672273)the Open Research Fund of State Key Laboratory of Multi-phase Complex Systems(MPCS-2017-D-06)the Young Talent Project of the Center for Excellence in Regional Atmospheric Environment,CAS(CERAE201805)~~
文摘Catalytic oxidation is regarded as one of the most promising strategies for volatile organic compounds(VOCs)purification.Mixed metal oxides(MMOs),after topological transformation using layered double hydroxides(LDHs)as precursors,are extensively used as catalysts for VOCs oxidation due to their uniformity advantage.This review summarizes the developments in the LDH-derived VOCs heterogeneous catalytic oxidation over the last 10 years.Particularly,it addresses the VOCs abatement performance over MMO,noble metal/MMO,core-shell structured MMO,and integral MMO film catalysts originating from LDHs.Moreover,it highlights the water vapor effect and oxidation mechanism.This review indicates that LDH-based catalysts are a category of important VOCs oxidation materials.
文摘Sulphur-containing aromatic nitro compounds were rapidly reduced to the corresponding amines in high yields by employing hydrazine hydrate as a hydrogen donor in the presence of iron oxide hydroxide catalyst. It was worth noting that the catalyst exhibited extremely high activity. The reduction could be completed within 20-50 min and the yields were up to 97-99 %.
文摘Mg-Al layered double hydroxide intercalated with CO_(3)^(2-)(CO_(3)·Mg-Al LDH) is effective for treating HCl exhaust gas.HCl reacts with CO_(3)^(2-) in CO_(3)·Mg-Al LDH, resulting in the formation of Cl·Mg-Al LDH.We propose that CO_(2) can be used for the desorption of Cl^(-)from Cl·Mg-Al LDH to regenerate CO_(3)·Mg-Al LDH.Herein,we studied the desorption of a from CI-Mg-Al LDH by adding water to Cl·Mg-Al LDH and blowing CO_(2) into it.We also analyzed the effects of temperature and water addition speed on the desorption of CI^(-)from Cl·Mg-Al LDH.Our results show that the added water adhered to CI·Mg-Al LDH and that CO_(2) in the gaseous phase was dissolved in this adhered water,thus generating CO_(3)^(2-).Therefore,anion exchange occurred between CO_(3)^(2-) and Cl^(-)in the Cl·Mg-Al LDH,thus desorbing Cl^(-).
基金supported by the National Natural Science Foundation of China (Nos.51601108,52071191)the Natural Science Foundation of Shandong Province,China (No.ZR2020ME011).
基金supported by the National Natural Science Funds of China(No.52175290 and No.51975090).
文摘A series of Zn-xAl(x=0-35 wt.%)alloy filler metals were designed to join AZ31 Mg alloy to 6061 Al alloy by laser-TIG hybrid welding.The effect of Al content on the wettability of filler metals,microstructure evolution and strength of joint was investigated.The results indicated that the strength of joints was improved with the increase of Al content in filler metals.When Zn-15Al filler was used,the ultimate fracture load reached the maximum of 1475.3 N/cm,which was increased by 28%than that with pure Zn filler.The reason is that the Al element acts as a"reaction depressant"in filler metal,which contributes to inhibiting the dissolution of Mg base metal and the Mg-Zn reaction.The addition of appropriate quantity of Al element promoted the precipitation of Al-rich solid solution instead of Zn solid solution.The MgZn_(2) IMCs have lower lattice mismatch with Al solid solution than Zn solid solution,thus the strength of joints is improved.However,the excessive addition of Al caused the formation of brittle Mg32(Al,Zn)49 ternary compounds,leading to the deterioration of joint performance.
基金Supported by Shanxi Province Natural Science Funds.(20001015)
文摘The preparation of ZnAlLa-hydrotalcite-like compounds [ZnAlLa-HTLcs] wasstudied. ZnAlLa-HTLcs were synthesized by a method of variable pH with the raw materials ofZn(NO_3)_2, Al(NO_3)_3, La(NO_3)_3, and NaOH. The eS'ccts of some factors (i.e. pH values, the moleratio of Al^(3+) to La^(3+), temperature and the period of hydrothermal treatment) on thepreparation of HTLcs were discussed systematically. XRD, TG-DTA, FT-IR spectroscopy, and ICP wereperformed to characterize ZnAlLa-HTLcs samples, and the thermal stability of HTLcs was alsodiscussed. It was shown that unique ZnAlLa-HTLcs with high crystallinity can be prepared, under theconditions of pH = 5.5-6.5, n(Zn^(2+))/n(Al^(3+) + La^(3+))=2 and the atomic ratio of La^(3+) toAl^(3+) ranging from 0.07 to 2, hydrothermal treatment at 120 ℃ for 5 h. When the calcination ofthe HTLcs is performed at temperatures above 200 ℃, ZnO phase is detected with Al_2O_3 and La_2O_3spreading on its top. The complex metal oxides derived from ZnAlLa-HTLcs at 500 ℃ have highercatalytic activity and selectivity than those from ZnAl-HTLcs for the esterification of acetic acidwith n-butanol under the same reaction conditions.
基金supported by International Cooperation Program from Sichuan Science and Technology Program(Nos.2019YFH0181,2015HH0013)the National Natural Science Foundation of China(No.21276031)。
文摘A series of Zn_(x)Ni_(y)CrO_(m±δ)catalysts were synthesized via a typical co-precipitation method,in which Zn-Cr layered double hydroxides(LDHs)were found and Ni-Zn intermetallic compound(IMC)was formed after reduction in hydrogen.During auto-thermal reforming(ATR)of acetic acid(HAc),the Ni-Zn IMC was transformed into Ni/(amorphous-ZnO)-ZnCr_(2)O_(4) species with uniformed distribution and appropriate interaction within these Ni-Zn-Cr-O species;besides,the adsorbed oxygen promoted the activation and transfer of oxygen species;therefore,deactivation by oxidation,sintering and coking was inhibited.And the optimized Zn_(2.37)Ni_(0.63)CrO_(4.5±δ)catalyst presented high activity and stability in a 45-h ATR test with HAc conversion near 100%and hydrogen yield at 2.7 mol-H_(2)/mol-HAc,showing potential for hydrogen production via ATR of HAc.